موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091333220180622The Investigation of Physical and Mechanical Properties of Oriented Strand Board (OSB) Production Using Corn Stalks Residuesبررسی ویژگی های فیزیکی و مکانیکی تخته تراشه جهت دار (OSB ) ساخته شده از ساقه ذرت15516511514310.22092/ijwpr.2018.115515.1438FAابوالفضل کارگرفردعضو هیئت علمی بخش تحقیقات علوم چوب و فرآوردههای آن، مؤسسه تحقیقات جنگلها و مراتع کشور، تهرانJournal Article20170919Abstract: The application of corn stalks in the production of oriented strand board (OSB) is investigated. Corn stalks strands were produced in three sizes of 50, 75 and 100 millimeters length and dried to reach 2% moisture content. Oriented strand boards were made using either urea formaldehyde, melamine formaldehyde and phenol formaldehyde resin, and two press temperatures of 175 and 185 ° C. OSB boards using poplar wood strands, 100 millimeters long were also produced as control samples. The results of strength measurements of the boards were statistically analyzed using factorial experiment and completely randomized block design. The grouping of the averages was based on Duncan Multiple Range Test. The results showed that the effect of the resin type on the flexural properties and internal bonding of the boards is statistically significant and boards produced using phenol formaldehyde resin exhibited the lowest modulus of rupture, modulus of elasticity and internal bonding strength. However, the adhesive type did not statistically influence the physical properties. The strand length also statistically influenced the board strength properties and boards made using poplar strands showed higher strength compared to corn stalks strands. The thickness swelling of the poplar OSB was almost twice the values of corn stalks OSB but the water absorption of these boards was lower than of corn stalks OSB. Press temperature adversely affected the modulus of rupture and elasticity, but higher press temperature improved the internal bonding strength. Higher press temperature increased the physical properties of the boards.این بررسی با هدف استفاده از ساقه ذرت دانه ای در تولید تخته تراشه های جهت دار (OSB) انجام شده است. لذا از تراشه های تهیه شده از ساقه ذرت در 3 اندازه طولی 50، 75 و 100 میلیمتر، 3 نوع چسب اوره، ملامین و فنل فرم آلدئید و 2 زمان پرس 175 و 185 درجه سانتیگراد به عنوان عوامل متغیر و همچنین استفاده از تراشه های چوب صنوبر به عنوان شاهد اقدام به ساخت تخته تراشه گردید. نتایج حاصل از اندازه گیری خواص مکانیکی و فیزیکی تخته تراشه های ساخته شده با استفاده از طرح آزمایش فاکتوریل در قالب طرح کامل تصادفی مورد تجزیه و تحلیل قرار گرفت. نتایج نشان داد که تخته تراشه های ساخته شده با چسب فنل فرم آلدئید دارای کمترین مقاومت خمشی، مدول الاستیسیته و چسبندگی داخلی بودند. همچنین نتایج نشان داد که طول تراشه بر روی کلیه ویژگیهای مکانیکی چند سازه های ساخته شده اثر معنی داری داشته است و چند سازه های ساخته شده با تراشه های صنوبر (شاهد) به مراتب از ویژگیهای مکانیکی بالاتری برخوردار بودند. ولی تخته های ساخته شده از تراشه های صنوبر در مقایسه با تخته تراشه های ساخته شده از تراشه های ساقه ذرت با طول های مختلف از واکشیدگی ضخامت 2 برابری برخوردار بودند و این در حالی است که تخته های ساخته شده از تراشه های ذرت دارای جذب آب 2 و 24 ساعت بالاتری نسبت به تخته های شاهد (صنوبر) بودند. همچنین نتایج نشان داد که با افزایش دمای پرس از مقدار مقاومت خمشی و مدول الاستیسیته کاسته شده است. ولی مقاومت چسبندگی داخلی تخته تراشه ها با افزایش دمای پرس در سطح معنی داری بهبود یافته است. از سوی دیگر با افزایش درجه حرارت پرس کلیه ویژگی های فیزیکی تخته های ساخته شده با افزایش روبرو گردید.موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091333220180622The effect of nano wollastonite on the fire resistance and the adhesion properties of water based acrylic coating in wood surfaceتاثیر نانو ولاستونیت بر مقاومت به آتش و چسبندگی پوشش آکریلیک پایه آب در سطح چوب16617811517710.22092/ijwpr.2018.114552.1429FAحسین رنگ آوردانشیار گروه صنایع چوب دانشگاه شهید رجاییسعید خجسته خسروگروه علوم و صنایع چوب و کاغذ، دانشکده منابع طبیعی، دانشگاه تربیت مدرس، نور، مازندرانمسعود تقی پور جاویگروه صنایع چوب، دانشکده مهندسی عمران، دانشگاه تربیت دبیر شهید رجایی،Journal Article20170704The main objective of the current study was the investigation of the effect of adding the wollastonite nanoparticles (casio3) to the water based acrylic coating onto the fire resistance capability and adhesion strength of coating. The nano wollastonites with the concentrations of 0.5, 1.50, and 2.5 wt% were dispersed into the coating. Ultrasonic device was used to stabilize the nanoparticles into the substrates. The coating process was carried out with and without application of the nanoparticles on the surfaces of spruce and sycamore samples and their properties comprising the fire resistance and the adhesion strength were investigated. The obtained results showed that adding of nano wollastonite to the acrylic coating with the waight percent of 2.5% (w/w) had the significance effect onto the resistance of the samples to fire. In particluar, these effects was observed in cas of the retard time of ignition of the spruce and sycamore samples with the improvement values of 258 and 184 % compared with the control samples, respectively. Furthermore, the investigation of adhesion properties of coatings to the sample surface indicated that the applied nano wollastonites improved these properties of coatings. In case of the adhesion properties, however, the highest value of this properties was observed in the highest content of wollastonite nanoparticles. It should be noted that the performance of nanocomposite coating containing of the 1.5 wt% of nano onto investigated properties was also acceptable.در مطالعه حاضر اثر افزودن نانو ذرات ولاستونیت (casio3) به پوشش آکریلیک پایه آب بر قابلیت مقاومت به آتش و مقاومت چسبندگی پوشش مورد مطالعه قرار گرفت. نانو ولاستونیت با غلظتهای 5/0، 5/1 و 5/2 درصد وزنی نسبت به جرم خشک پوشش آکریلیک با آن مخلوط شد. برای تثبیت نانو ذرات در بستر پوشش از دستگاه اولتراسونیک استفاده گردید. فرایند پوشش دهی نمونهها با و بدون کاربرد نانو ولاستونیت در پوشش آکریلیک روی نمونههای چنار و نوئل صورت پذیرفت و ویژگیهای آنها شامل مقاومت به آتش و مقاومت چسبندگی مورد بررسی قرار گرفتند. نتایج نشان داد که افزودن نانو ولاستونیت تا 5/2 درصد به پوشش آکریلیک، اثر بسیار قابل توجهی بر بهبود مقاومت به آتش نمونهها بخصوص تاخیراندازی زمان شعلهوری گونههای نوئل و چنار با بهبود 258 و 184 درصدی نسبت به نمونههای شاهد داشته است. از طرف دیگر بررسی چسبندگی پوشش آکریلیک به سطح نمونههای چوبی حاکی از بهبود این ویژگی پوشش با افزودن نانو ولاستونیت بود. در مورد چسبندگی پوشش نیز بالاترین میزان این ویژگی در نانو پوشش حاوی بیشترین میزان نانو ذرات ولاستونیت مشاهده گردید. البته لازم به ذکر است که عملکرد نانو پوششهای حاوی 5/1 درصد نانو روی ویژگیهای مورد بررسی نیز در حد قابل قبولی بود.موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091333220180622Identification and Prioritization of factors affecting competitiveness of Classic Furniture by using ANP (Case study: Tehran Province)اولویت بندی عوامل موثر بر رقابت پذیری مبلمان کلاسیک با فرایند تحلیل شبکهای (مطالعه موردی استان تهران)17919511545310.22092/ijwpr.2018.110766.1420FAمحمد غفرانیدانشیار دانشگاه شهید رجائیزهرا محمد مرادیکارشناسی ارشد علوم و تکنولوژی صنایع چوب، دانشکده مهندسی عمران، دانشگاه تربیت دبیر شهید رجاییJournal Article20170526Nowadays, Due to the unstable world economy, to survive and create competitiveness in domestic and overseas market, sustainable production and increases in quality and quantity of products is needed, In case of no attention, the possibility of competitiveness in regional and international markets will not occur. Therefore, in this study, with cooperation of experts and industry manufacturers’ expertise determination and ranking of factors affecting classic furniture was determined by using analytical network process and DEAMATEL techniques. 5 main and 17 sub-indexes parameters examined in this study and by using analytical network process the importance of prioritizing criteria was determined and cause and effect relationships between indicators was evaluated by DEAMATEL techniques. The results showed that, the main indicator of production and sales management, quality assurance, design style and creativity have the highest normal weight and the sub-indices of the modernity of machines and technology, reasonable price and Brand longevity respectively, are the three top priorities to impact on the competitiveness of classic furniture.در دنیای ناپایدار اقتصادی امروز، تولید پایدار و افزایش سطح کمی و کیفی محصولات، جهت حفظ بقاء و رقابت پذیری در بازار داخلی و خارجی الزامیست. بگونهای که در صورت عدم توجه، امکان رقابتپذیری در بازارهای منطقهایی و بین المللی وجود نخواهد داشت. بدین جهت در این پژوهش، با بهرهمندی از نظرات متخصصین و تولیدکنندگان خبره این صنعت مبلمان به شناسایی و اولویت بندی عوامل موثر بر رقابتپذیری مبلمان کلاسیک پرداخته شد. شاخصهای مورد بررسی در این پژوهش شامل 5 شاخص اصلی و 17 زیرشاخص بودند که با بکارگیری فرایند تحلیل شبکهای اولویتبندی و درجه اهمیت شاخصها و زیر شاخصها تعیین و با کمک روش دیمتل روابط علی و معلولی شاخصها بررسی شد. نتایج حاصل از بررسیهای صورت گرفته نشان داد شاخصهای اصلی مدیریت تولید و فروش، تضمین کیفیت و سبک طراحی وخلاقیت به ترتیب دارای بالاترین وزن نرمال بودند و زیر شاخص بروز بودن ماشین آلات و فناوری، قیمت مناسب و ماندگاری برند به ترتیب اولویت اول تا سوم تاثیرگذاری بر رقابتپذیری مبلمان کلاسیک را بدست آوردند.موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091333220180622The usage effect of nano-alumina on the mechanical and surface properties of HDF made of oxidized fibersتاثیرکاربرد نانوآلومینا بر خواص مکانیکی و سطحی HDF حاصل از الیاف اکسید شده19620411585910.22092/ijwpr.2018.114650.1432FAصائب شبان پورکارشناسی ارشدنورالدین نظرنژاددانشگاه علوم کشاورزی و منابع طبیعی ساری- دانشیار گروه چوب و کاغذ0000-0003-0632-4535مریم قربانیهیات علمی- دانشگاه علوم کشاورزی و منابع طبیعی ساریJournal Article20170720Current research was conducted to investigate the effect of nano Alumina modification on the mechanical and Surface properties of High-Density Fiberboard (HDF) made from oxidized fibers. Surface activation of fiber was done with 40% nitric acid. After fibers gluing with urea-formaldehyde (7% and 9% based on the dry weight of fibers), the boards were made by hot pressing. For veneering, two types of paper with grammage of 70 and 80 g/m2 impregnated with melamine-formaldehyde and nano-alumina 0, 1.5 and 3% were applied. According to the results, the highest bending strength, modulus of elasticity and hardness were measured in nitric acid-modified fibers/ 9% glue/ grammage of 80 g/m2/3% nano-alumina samples that was significant increase compared to the control boards a significant increase. The samples weight loss due to abrasion was decreased with increasing the veneers grammage and nano-alumina, which confirmed the positive effect of nano-alumina. Veneer grammage did not show significant effect on the resistance to cigarette burn, but the highest concentration of nano-alumina resulted to improve this surface resistance via increase of thermal conductivity.در تحقیق حاضر اثر اصلاح نانوآلومینا بر خواص مکانیکی و سطحی HDF حاصل از الیاف اکسیدشده بررسی شد. فعال-سازی سطوح الیاف با استفاده از اسید نیتریک 40% انجام گردید. پس از چسبزنی الیاف با چسب اورهفرمآلدئید ( 7% و 9% بر اساس وزن خشک الیاف)، تختهها بهوسیله پرس گرم ساخته شدند. برای روکش کردن از دو نوع کاغذ با گراماژهای 70 و 80 گرم برمترمربع آغشته به چسب ملامینفرمآلدئید حاوی سه سطح صفر، 5/1 و 3 درصد نانوآلومینا استفاده شد. براساس نتایج، بیشترین مقاومت خمشی، مدولالاستیسیته و سختی در نمونههای ساخته شده از الیاف اصلاح شده با اسید نیتریک، مقدار مصرف چسب 9%، وزن پایه روکش 80 گرم برمترمربع محتوی 3 درصد نانو آلومینا اندازهگیری شد که در مقایسه با تختههای شاهد افزایش معنیداری نشان داد. با افزایش مقدار نانوآلومینا، کاهش وزن حاصل از سایش نمونهها کمتر بود که مبین عملکرد مثبت نانوآلومینا بودهاست. گراماژ کاغذ اثر معنیداری بر مقاومت به آتش سیگار نشان نداد، ولیکن بالاترین مقدار مصرف نانوآلومینا با افزایش هدایت حرارتی سبب بهبود مقاومت سطحی گردید.موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091333220180622Evaluating the Properties of Bleached Chemi-Mechanical Pulp (CMP) with One and Two-stage of Sodium Hypochlorite and Hydrogen Peroxideبررسی ویژگیهای خمیر کاغذ شیمیایی-مکانیکی (CMP) رنگبری شده با توالی یک و دو مرحلهای هیپوکلریت سدیم و پراکسید هیدروژن20521711617410.22092/ijwpr.2018.120401.1458FAقاسم اسدپور اتوئیدانشگاه علوم کشاورزی و منابع طبیعی ساری0000-0002-3326-5481فاطمه رجبیدانشآموخته کارشناسی ارشد صنایع چوب و کاغذ، دانشگاه علوم کشاورزی و منابع طبیعی ساریسید مجید ذبیح زادهگروه مهندسی چوب و کاغذ، دانشکده منابع طبیعی، دانشگاه علوم کشاورزی و منابع طبیعی ساری، ساریJournal Article20180123The objective of this study was the evaluation of optical, mechanical properties of chemi-mechanical pulp which were bleached by one and two stage bleaching sequence of hydrogen peroxide and sodium hypochlorite. Also the environmental effects of effluents from bleached paper liquor were studied. For this purpose, unbleached CMP pulp mixed of hardwoods was prepared from Mazandaran Wood and Paper mill. Then, these pulps were bleached using P (hydrogen peroxide), H (Sodium Hypochlorite), PH (Hydrogen Peroxide and Sodium Hypochlorite) and HP (Sodium Hypochlorite and hydrogen peroxide) stages. 60 gr/m2 hand sheets were prepared and the optical, mechanical properties of hand sheets and also their effluent bleaching liquor characteristics were measured and analyzed based on TAPPI and APHA Standards. The results showed that when peroxide was applied at the last stage of bleaching, then the properties such as tear, tensile and brightness have increased and yellowness has decreased. Generally, the role of single sequence of bleaching by P and two sequence of bleaching with HP were more effective than single sequence of H or unbleached pulp. Based on results, the highest and lowest COD load is related to bleaching liquor of H and PH respectively. Moreover, bleaching liquor of hydrogen peroxide had the highest BOD load and the lowest amount of BOD is related to PH sequence of bleaching.هدف این پژوهش بررسی خواص نوری و مقاومتی خمیر کاغذ شیمیایی-مکانیکی (CMP) رنگبری شده با توالی یک و دو مرحلهای از پراکسید هیدروژن و هیپوکلریت سدیم بوده است. همچنین بار اکسیژنخواهی شیمیایی و بیولوژیکی پساب حاصل از رنگبری خمیر کاغذ CMP، مورد مطالعه قرار گرفته است. بدین منظور خمیر کاغذ CMP رنگبری نشده مخلوط پهنبرگان از کارخانه چوب و کاغذ مازندران تهیه گردید. سپس این خمیرها با توالیهای یک و دو مرحلهای P (پراکسید هیدروژن)، H (هیپوکلریت سدیم)، PH (پراکسید هیدروژن و هیپوکلریت سدیم) و HP (هیپوکلریت سدیم و پراکسید هیدروژن) رنگبری گردیدند. از خمیر کاغذهای رنگبری شده، کاغذ دستساز آزمایشگاهی با وزن پایه 60 گرم بر مترمربع تهیه و خواص نوری و مقاومتی آنها طبق آزمونهای استاندارد TAPPI، میزان بار اکسیژنخواهی شیمیایی( (COD و بار اکسیژن خواهی بیولوژیکی (BOD) پساب رنگبری نیز با استفاده از استاندارد APHA (1998) اندازهگیری و مقایسه شدند. نتایج نشان داده است زمانیکه پراکسید درمرحلهی آخر رنگبری بکار رود، ویژگیهایی از قبیل مقاومت در برابر پارگی، کشش و روشنی افزایش و زردی کاهش مییابد. به طورکلی، نقش توالیهای رنگبری پراکسید هیدروژن (P) و رنگبـری دو مرحلـهای هیپوکلریت سدیم و پراکسید هیدروژن (HP) در رنـگبـری خمیرکاغـذ CMP و بهبـود روشـنی و مقاومتهای کاغذ حاصل، مؤثرتر از توالی یک مرحلهای هیپوکلریت سدیم (H)و خمیر رنگبری نشده کارخانه بوده است. همچنین، بیشترین و کمترین میزان بار آلودگی پساب (COD) به ترتیب مربوط به خمیر کاغذهای رنگبری شده با توالی هیپوکلریت سدیم (H) و PH (پراکسید هیدروژن و هیپوکلریت سدیم) بودند. بیشترین بار BOD را نیز لیکور رنگبری با پراکسید هیدروژن (P) دارا بوده و کمترین مقدار را نیز، توالی رنگبری پراکسید هیدروژن و هیپوکلریت سدیم (PH) داشته است.موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091333220180622Comparison of Tensile Properties and Mechanical-Dynamic Analysis of Poly-Lactic Acid / Poly-Ethylene Compounded with Natural Fibersمقایسه ویژگی های کششی و تحلیل مکانیکی-دینامیکی چندسازه پلی لاکتیک اسید/پلی اتیلن تقویت شده با الیاف طبیعی21823011617510.22092/ijwpr.2018.120584.1462FAحمید آیباغی اصفهانیگروه معماری، واحد زاهدان، دانشگاه آزاد اسلامی، زاهدان، ایرانمهدی کلاگرپژوهشگر مرکز تحقیقات و نوآوری سازمان اتکاحسین سپهری رادعضو هیات علمی، گروه معماری، دانشگاه آزاد اسلامی واحد زاهدان، زاهدانJournal Article20180211In this study, the tensile and dynamic-mechanical properties of composites made by poly-lactic acid polymer (PLA) and high density polyethylene (HDPE) as matrix and sawdust to reinforcement 30 % weight were investigated. Maleic anhydride bonded with polyethylene (MAPE) was used to increase coupling agent by 3%. The use of sawdust increased the stiffness of composites while the use of this material reduced the tensile strength of composites. The highest tensile properties (elastic modulus and tensile strength) were related to poly lactic acid /polyethylene / sawdust / coupling agent composites. The addition of natural fibers to both matrices (PLA and MAPE) increased the composite storage modulus compared to pure polymers, while the modulus of storage in pure polyethylene and its composite was higher. Simultaneous use of two polymers with an equal ratio (33.5% by weight) and composite sawdust have shown the stiffness between the composites made with single polymers. The use of natural fibers reduced the mobility of the molecular chain and transported the temperature of the composite to higher temperatures, which eventually moved the corresponding corners to the right and lower. However, in some cases, the transmission of pixels has not followed the normal process. The addition of the coupling agent (MAPE) makes bonding more common between two phases in all composites and ultimately increases stiffness.در این تحقیق ویژگیهای کششی و دینامیکی- مکانیکی چندسازه ساخته شده با پلیمر پلی لاکتیک اسید (PLA) و پلی اتیلن دانسیته سنگین (HDPE) به عنوان ماتریس و خاک اره به عنوان تقویت کننده به میزان 30 درصد وزنی مورد بررسی قرار گرفته است. از انیدرید مالئیک پیوند خورده با پلی اتیلن (MAPE) به میزان 3 درصد وزنی به عنوان اتصال دهنده استفاده شده است. استفاده از خاک اره باعث افزایش در سفتی چندسازههای ساخته شده شده است در حالیکه استفاده از این ماده باعث کاهش در مقاومت کششی چندسازهها شده است. بالاترین میزان ویژگیهای کششی (مدول الاستسیته و مقاومت کششی) مربوط به چندسازه پلی لاکتیک اسید/پلی اتیلن/ خاک اره/ اتصال دهنده بوده است. افزودن الیاف طبیعی به هر دو ماتریس (PLA و PE) مدول ذخیره چندسازه را نسبت به پلیمرهای خالص افزایش داده در حالیکه میزان مدول ذخیره در پلی اتیلن خالص و چندسازه آن بالاتر بوده است. استفاده همزمان از دو پلیمر با نسبت مساوی (5/33 درصد وزنی) و خاک اره جهت ساخت چندسازه میزان سفتی بین چندسازه ساخته شده با تک تک پلیمرها را نشان داده است. بکارگیری الیاف طبیعی باعث کاهش تحرک زنجیره مولکولی و انتقال دمای چندسازه به دماهای بالاتر شده که در نهایت پیکهای مربوطه به سمت راست و پایینتر جا به جا شدهاند. هر چند که در برخی موارد انتقال پیکها از روند نرمالی تبعیت نکرده است. افزودن اتصال دهنده MAPE باعث چسبندگی سطح مشترک بیشتر بین دو فاز در تمامی چندسازهها شده و در نهایت سفتی را افزایش داده است.موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091333220180622Identification of Cellulosic Fiberfines Properties in Kraft, Chemical Mechanical, and Recycled Pulpsشناسایی ویژگی های نرمه الیاف سلولزی خمیر کاغذهای کرافت، شیمیایی-مکانیکی و بازیافتی23124311617710.22092/ijwpr.2018.110974.1422FAجعفر عزیزیدانش آموخته کارشناسی ارشد، گروه مهندسی پالایش زیستی، دانشکده مهندسی فناوریهای نوین، دانشگاه شهید بهشتی،امید رمضانیاستادیار گروه فناوری سلولز و کاغذ، دانشگاه شهید بهشتی، زیرآب، سوادکوهاسماعیل رسولی گرمارودیدانشگاه شهید بهشتی، زیراب مازندرانحمید رضا رودیاستادیار گروه خمیر و کاغذ دانشکده مهندسی انرژی و فناوریهای نوین دانشگاه شهید بهشتیJournal Article20170607Cellulosic fines are essential parts of paper making system which impart remarkable effects on the production process parameters and the quality of final product. In this study, properties of fiberfines prepared from three kinds of pulps including Kraft, chemical mechanical (CMP), and recycled (OCC) were investigated. Required amounts of fines were prepared using Valley Beater apparatus. Then the fines were classified into three categories using dynamic drainage Jar (DDJ): fines passing a 100 mesh remained on 200 mesh (P100/R200), fines passing a 200 mesh remained on a 325 mesh (P200/R325), and fines passing a 325 mesh (P325). Fines properties including dimensional size, special hydrodynamic volume, colloidal charge, alkalinity, turbidity, viscosity, and specific area were examined. The results revealed that PH of fiber suspensions tended alkaline concurrently to the decreasing in dimensional size of fines. Additionally, the colloidal charge of the three types of fines, especially the charge associated with the fines passed through 200 mesh screen and remained on 325 mesh one, showed a different behaviour compared to those in the same classes with the adverse trend to the viscosity variation. Special hydrodynamic volume is consistent with the dimensional size and dimensional ratio with the lowest amount of it observed in the recycled pulp fines. Turbidity has a direct relationship with particles size, homogenous distribution and the specific area of the finesThe results of turbidity related to the fines passed through 200 mesh size showed different behaviour compared to other categories.ریزه الیاف سلولزی و نرمهها اجزئی مهمی از الیاف کاغذسازی محسوب میشوند که میتوانند تأثیرات قابل توجه بر فرآیند تولید و کیفیت فرآورده نهایی داشته باشند. در این تحقیق، ویژگیهای نرمه الیاف سه نوع خمیرکاغذ شامل کرافت، شیمیایی ـ مکانیکی (CMP) و خمیرکاغذ بازیافتی (OCC) مورد بررسی قرار گرفت. مقادیر موردنیاز نرمه با استفاده از دستگاه کوبنده والی (Valley beater) تهیه شدند. سپس نرمهها با استفاده از دستگاه زهکش دینامیکی (DDJ) در سه دسته نرمههای عبوری از مش 100 و باقیمانده روی مش 200 (P100/R200)، نرمههای عبوری از مش 200 و باقیمانده روی مش 325 (P200/R325) و نرمههای عبوری از مش 325 (P325) کلاسهبندی شدند. ویژگیهای نرمه شامل: اندازه ابعادی، حجم ویژه هیدرودینامیکی، بار کلوئیدی، قلیائیت، کدورت، ویسکوزیته و سطح ویژه بررسی شدند. نتایج نشان داد که pH نرمههای سلولزی خمیرکاغذ با کوچکتر شدن ابعاد، بیشتر به سمت قلیایی شدن میل میکند و بار کلوئیدی سه نوع نرمه، به ویژه در نرمههای عبوری از مش 200 و باقیمانده روی مش 325 رفتار متفاوت با سایر کلاسههای خود نشان دادند بهطوری که روند تغییرات آن معکوس ویسکوزیته میباشد. حجم ویژه هیدرودینامیکی با اندازه ابعادی و همچنین نسبت ابعادی تطابق دارد و کمترین مقدار آن مربوط به نرمههای خمیرکاغذ بازیافتی میباشد. میزان کدورت نیز با اندازه ذرات و میزان پخش همگن و همچنین با سطح ویژه نرمهها ارتباط مستقیم دارد. نتایج این ویژگی در نرمههای عبوری از مش 200 خمیر کاغذ بازیافتی رفتاری متفاوت نسبت به سایر گروهها را نشان داد.موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091333220180622Application of Bagasse as Adsorbent of Acid Orange 7 from Aqueous Solutionاستفاده از باگاس بهعنوان جاذب رنگ اسید اورانژ7 از محلول آبی24425511617610.22092/ijwpr.2018.116170.1444FAعلیرضا ضیاپورگروه علوم و مهندسی چوب و کاغذ، دانشکده منابع طبیعی، دانشگاه گرگان، گرگان، ایرانعباس زارعگروه علوم و مهندسی چوب و کاغذ، دانشگاه تربیت دبیر شهید رجایی، تهران، ایرانمحمد بخشیگروه علوم و مهندسی صنایع چوب و کاغذ، دانشگاه آزاد اسلامی واحد کرج، کرج، ایرانJournal Article20171112Chemical and biological treatment of dye- containing wastewaters is difficult due to the low adsorption level and chemical stability of dyes. Activated carbon is usually used for adsorption of these materials, but because of high prices and restore problems, researchers trying to find available low-cost materials with high adsorption. In this study, bagasse was used for adsorption of Acid Grange7 dye and its capability was examined. Variables were concentration, temperature, pH and contact time, and the degree of adsorption was examined in different situations. Then, adsorption isotherm according to Langmuir and Freundlich models was investigated. The results showed that the adsorption efficiency depends more on pH of solution and less on temperature of the solution. Maximum adsorption of Acid Orange7 dye by bagasse occurred in the first 15 minutes of contact. The study of adsorption isotherm showed that both models are suitable for description of adsorption of Acid Orange7 dye by bagasse. Maximum adsorption of Acid Orange7 dye by bagasse was calculated as 18.56 mg/g. Results of this study showed that bagasse could be used as a low-cost bio adsorbent for the adsorption of Acid Orange7 from aqueous solution.پتانسیل استفاده از باگاس برای حذف رنگ واکنشی اسید اورانژ 7 از محیط آبی با استفاده از محلول رنگ مصنوعی بررسی شد. نتایج نشان داد که با کاهش pH و دما، کارایی جذب این رنگ افزایش مییابد و از طرف دیگر با افزایش غلظت رنگ در محیط، ظرفیت جذب بیشتر میشود. سرعت جذب رنگ توسط این ماده نسبتاً سریع است و در تمامی آزمونها، غلظت تعادل در 20 دقیقة اول تیمار حاصل شد. مطالعات ایزوترم جذب با غلظت های مختلف نشان داد که فرایند جذب این رنگ بر روی باگاس هم از مدل لانگمویر و هم از مدل فروندلیچ تبعیت میکند ولی مدل لانگمویر با ظریب همبستگی بیش از 99/0 بهتر از مدل فروندلیچ با ضریب همبستگی 98/0 است. با استفاده از مدل لانگمویر، حداکثر ظرفیت جذب این رنگ 56/18 میلیگرم بر گرم محاسبه شد که در مقایسه با سایر مواد لیگنوسلولزی مطالعه شده، مقدار قابل قبول و مناسبی است.موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091333220180622Potential of GL as cationic polymer to control stickies of OCC pulpپتانسیل GL به عنوان پلیمر کاتیونی در کنترل مواد چسبناک خمیرکاغذ OCC25626911637210.22092/ijwpr.2018.116639.1450FAعلی احمدی لاجیمیگروه علوم و صنایع چوب و کاغذ - دانشگاه تهرانمحمد آزادفلاحدانشگاه تهرانمهدی رحمانی نیاعضو هیئت علمی دانشگاه تربیت مدرس0000-0001-6943-0146یحیی همزهاستاد- دانشکده منابع طبیعی کرج- دانشگاه تهرانJournal Article20171216Stickies is among the major challenges in paper recycling mills. This substance deposits on paper machine components and cause to break paper web as well as loss of end product quality. So, it is necessary to control the stickies and lessen its detrimental effects. It is known that cationic polymers as fixing agents can control the stickies efficiently. Therefore, the control of stickies of OCC pulp using a commercial cationic polymer called GL at 0.4, 0.8 and 1.2 percent based on oven dry weight of pulp at pH 4 and pH 5 were investigated. Macro- and microstickies, dissolved and colloid substances (DCS), turbidity, and drainage time were measured to evaluate GL efficiency and compared with control sample. The results indicated that GL dosing at 0.4 and 0.8 percent in pH 4 and 7 due to flocculation and fixing the stickies onto the fiber caused to decrease in macro stickies, microstickies and DCS while improved the drainage time. Although, no efficient performance was observed in controlling stickies at higher content of GL i.e. 1.2 percent. Generally, it is concluded that with consuming at desired pH and dosage content, GL can be used as efficient agent to control stickies in processing of OCC pulp.مواد چسبناک ازچالشهای مهم در کارخانههای بازیافت کاغذ هستند. این مواد مضر با رسوب بر روی اجزای ماشین کاغذ موجب پارگی کاغذ و همچنین کاهش کیفیت محصول نهایی میشوند. از این رو کنترل این مواد و کاهش اثرات مخرب آن ضروری است. استفاده از پلیمرهای کاتیونی به عنوان عامل تثبیت کننده از روشهای موثر کنترل این مواد شناخته می-شوند. لذا در این پژوهش کنترل مواد چسبناک خمیرکاغذ OCCبا استفاده از یک پلیمرکاتیونی تجاری به نام GL در سه سطح 4/0، 8/0 و 2/1 درصد و بر اساس وزن خشک خمیرکاغذ در دو دامنه pH 4 و 7 بررسی شده است. برای ارزیابی کارایی این ترکیب مواد چسبناک ماکرو، مواد چسبناک میکرو، مواد محلول و کلوییدی، میزان کدورت و زمان آبگیری اندازهگیری و با مقادیر نمونههای شاهد مقایسه شدند. نتایج نشان دادند که پلیمرکاتیونی GL در سطح 4/0 و 8/0درصد در هر دوpH 4 و 7 به دلیل دلمهشدن و تثبیت مواد چسبناک بر روی الیاف، سبب کاهش میزان مواد چسبناک ماکرو، میکرو و محلول و کلوییدی و میزان کدورت شد درحالیکه زمان آبگیری بهبود یافت. هرچند، پلیمر کاتیونی GL در مقدار 2/1 درصد عملکرد موثری در کنترل مواد چسبناک از خود نشان نداد. به طورکلی میتوان نتیجه گرفت در صورت مصرف پلیمر کاتیونی GL در دوز و pH مناسب می توان از آن به طور موثری در کنترل مواد چسبناک حاصل از فراوری خمیرکاغذ OCC استفاده کرد.موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091333220180622Use of unconventional water (rain) in urea-formaldehyde adhesive (Arian sina company case study)استفاده از آبهای نامتعارف (باران) در تولید تخته فیبر با دانسیته متوسط با استفاده از چسب اورهفرمالدهید (مطالعه موردی شرکت آرینسینا)27027911637010.22092/ijwpr.2018.116961.1452FAوحید معظمیمسئول تحقیق و توسعه و مدیر داخلی آرین سینافاطمه افسونیمدیر عاملJournal Article20180102With growth and development of the modern societies and achieve towards industrialization of the countries, Use of the water, one of the major concerns is considered. Optimal usage of water resources, has special position and considerable, that its result is importance of the reuse of rain's water as a reliable source for supply the consumption water. The purpose of this research was, use of rain's water, in composition with urea formaldehyde adhesive, In order to adjust the final concentration of the adhesive. To prevent damage against rain water equipment, the Lagan system was transferred through the canals constructed at Arian sina factory. Then it was treated with the package at the factory. The results of the FT_IR spectrum, obtained from composition adhesive samples with rain's water and ordinary water, showed that the rain's water increased the number of hydrogen bonds in the adhesive. But based on the t test, the difference between Mechanical strength and physical properties of use of rain's water than to the ordinary water was not significant. Qua that the glue combined with rain's water does not have any negative effect on adhesive properties. Therefore, after research, Arian Sina has been saving water consumption by using 14000 liters of water per day, due to the country's limited resources and lack of resources.با رشد و توسعه جوامع پیشرفته و نیل به سمت صنعتی شدن کشورها، استفاده از آب یکی از دغدغههای بزرگ محسوب میشود. مصرف مطلوب و بهینه از منابع آبی، از جایگاه ویژه و قابل توجهی برخوردار است که نتیجه آن اهمیت استفاده از آب باران بهعنوان منبعی قابل اطمینان جهت تأمین آب مصرفی میباشد. از اینرو هدف از این پژوهش استفاده از آب باران در ترکیب چسب اورهفرمالدئید بهمنظور تنظیم غلظت نهایی چسب بوده است. بدین منظور برای جلوگیری از آسیب رسیدن به تجهیزات آب باران از طریق کانالهای احداث شده در کاخانه آرینسینا به سیستم تصفیه خانه انتقال داده شد. سپس به وسیله تجهیزات موجود در کارخانه مذکور تصفیه گردید. نتایج حاصل از طیفهای FT_IR بدست آمده از نمونههای چسب ترکیب شده با آب باران و آب معمولی نشان داد که آب باران باعث افزایش تعداد پیوندهای هیدروژنی در چسب میشود. اما بر اساس آزمون t، اختلاف بین ویژگیهای چسب و مقاومتهای مکانیکی و خواص فیزیکی استفاده از آب باران نسبت به آب معمولی معنیدار نبوده است. به-طوریکه چسب ترکیب شده با آب باران هیچگونه اثر منفی بر روی ویژگیهای چسب نمیگذارد. از اینرو پس از انجام تحقیقات، کارخانه آرینسینا با توجه به محدودیتها و کمبود منابع اولیه کشور با استفاده از آب باران روزانه 14000 لیتر در مصرف آب صرفهجویی داشته است.موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091333220180622Adsorption of rhodamine B with activated carbon prepared from beech woodجذب رنگ رودامین B توسط کربن فعال تهیه شده از چوب راش28028911637110.22092/ijwpr.2018.116836.1451FAمحمود روح بخش بیدئیگروه علوم و صنایع چوب و کاغذ، دانشکده منابع طبیعی، دانشگاه تهرانمحمد آزادفلاحدانشگاه تهرانرسول یاراحمدیدانشیار گروه بهداشت حرفه ای، عضو مرکز تحقیقات بهداشت کار، دانشکده بهداشت، دانشگاه علوم پزشکی ایرانJournal Article20171224Dyes release into waste water due to its toxicity for some organisms results in major environmental pollution problems. The activated carbon (AC) is an efficient adsorbent to remove this kind of pollutants from aqueous phase. Hence, in this research activated carbon was prepared from sound and rotted beech wood by chemical activation method and its adsorption capacity for removal of Rhodamine B was assessed. The carbonization and activation steps were performed at single stage with impregnating the substrate by zinc chloride as activating agent and with the ratio of 75, 100 and 125 percent to raw material mass at 400 and 500 ºC. The results showed that with increasing the impregnating agent content, the iodine number of ACs from both woods enhanced. The yield of AC from sound wood decreased with increasing impregnating agent while it was not predictable for AC resulted from rotted wood. Scanning electron microscopic (SEM) studies revealed much morphological changes in the surface of rotted wood-AC in comparison with sound wood -AC after treatment with activating agent. Also, raising the activating temperature from 400 to 500 ºC caused to enhance the iodine number. All prepared ACs performed much efficient in removal of Rhodamine B from aqueous solution. The maximum adsorption of the dye was obtained for ACs prepared under impregnating ratio of 125 and activating temperature of 500 ºC.رهاسازی رنگها در پساب به دلیل سمیت برای بسیاری از موجودات زنده، باعث ایجاد مشکلات اساسی مرتبط با آلودگی محیطزیست میشوند. کربنفعال جاذب کارآمدی برای حذف این نوع آلایندهها از فاز آبی است. بنابراین در این تحقیق، کربن فعال به روش فعالسازی شیمیایی از چوب سالم و پوسیده راش تهیه و ظرفیت جذب آن در حذف رنگ رودامین B بررسی شد. مرحله کربونیزاسیون و فعالسازی به صورت تک مرحلهای و با آغشتهسازی توسط ماده فعالساز کلرید روی در سه سطح 75،100 و 125 درصد نسبت به جرم پیشترکیب و در دمای 400 و500 درجه سانتیگراد انجام شد. نتایج نشان داد که عدد یدی بیشتر کربن فعالهای تهیهشده از دو نوع چوب با افزایش میزان ماده آغشته سازی افزایش پیدا میکند. بازده محصول به دست آمده از چوب سالم با افزایش ماده آغشتهسازی دچار افت شد، در حالیکه بازده کربن فعال چوب پوسیده غیرقابل پیش-بینی بود. مطالعات نمونهها توسط میکروسکوپ الکترونی روبشی(SEM)، تغییرات ریختشناسایی گستردهتری را در سطح کربن فعال مشتق از چوب پوسیده در مقایسه با چوب سالم در اثر تیمار با ماده فعالساز نشان دادند. همچنین افزایش دمای فعالسازی از ۴۰۰ درجه سانتیگراد به ۵۰۰ درجه سانتیگراد باعث افزایش عدد یدی شد. کربن فعالهای تولید شده در حذف رنگ رودامین B از محیط آبی بسیار کارامد عمل کردند. بیشترین مقدار جذب رنگ در تیمارهایی با نسبت آغشتهسازی 125 درصد و دمای فعالسازی 500 درجه سانتیگراد به دست آمد.موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091333220180622Improvement of the properties of Poplar chemi-mechanical newsprint through controlling process parametersبهبود ویژگیهای کاغذ روزنامه شیمیایی-مکانیکی (CMP) صنوبر از طریق کنترل پارامترهای فرآیندی29029911637310.22092/ijwpr.2018.116361.1449FAحسین رسالتیاستاد گروه صنایع خمیروکاغذ، دانشگاه علوم کشاورزی و منابع طبیعی ساری. دانشکده مهندسی چوب و کاغذ- گروه صنایع خمیروکاغذمصطفی نیکخواه دافچاهیدانشجوی دکتری دانشگاه علوم کشاورزی و منابع طبیعی ساریJournal Article20171118One of the drawbacks of utilizing non-forest fast growing species of Poplar as raw materials to produce newsprint in Mazandran Pulp and Paper Mill is fairly low bulk and opacity of produced paper at the yield of 85% (current CMP yield of the Mill). In this research work, the effect of process parameters (cooking yield and freeness) on the optical and mechanical properties of chemi-mechanical pulp was investigated. The chemi-mechanical pulps of poplar was prepared at four various levels of cooking yield, through changing the cooking time, and their properties at different level of freeness were evaluated in comparison with the control sample of Mazandran Pulp and Paper Mill (75% hornbeam and 25% beech). Strength properties of the paper pulps stemmed from the cooking yields of 85.25% to 90.4% were higher and more favorable than the control sample. By contrast, the strength properties of the produced paper pulp from the cooking yield of 94.6% were inferior to prepared paper pulp from the control sample. According to the results, there is the possibility of significant improvement of the strength properties, opacity and bulk of the chemi-mechanical pulps of poplar trough controlling the process parameters like cooking yield and freeness to utilize it as raw material of newsprint production in Mazandran Pulp and Paper Mill.یکی از مشکلات استفاده از گونه سریعالرشد و غیرجنگلی صنوبر به عنوان ماده اولیه تولید کاغذ روزنامه در سطح بازده 85% (سطح رایج بازده CMP در کارخانه چوب و کاغذ مازندران) بالک و ماتی نسبتاً کم کاغذهای حاصل میباشد. هدف از این تحقیق، بررسی تاثیر پارامترهای فرایندی (بازده پخت و درجه روانی) بر ویژگیهای نوری و مکانیکی خمیر کاغذ شیمیایی-مکانیکی بود. خمیرهای کاغذ صنوبر با تغییر زمان پخت در 4 سطح بازده مختلف تهیه شدند و خصوصیات آنها در سطوح مختلف درجه روانی در مقایسه با نمونه شاهد رایج مورد استفاده در کارخانه چوب و کاغذ مازندران (75% ممرز و 25% راش) مورد ارزیابی قرار گرفت. خصوصیات مقاومتی و درجه روشنی خمیرهای کاغذ صنوبر حاصل از بازدههای پخت 25/85% تا 4/90% در مقایسه با ترکیب شاهد در سطحی بهتر و مطلوب قرار گرفت. اما کاغذ حاصل از بازده 6/94% دارای خصوصیات مقاومتی ضعیفتری نسبت به کاغذ شاهد بود. نتایج نشان داد که با کنترل پارامترهای فرایندی همچون بازده پخت و درجه روانی امکان بهبود قابل ملاحظه خصوصیات مقاومتی، درجه روشنی، ماتی و بالک خمیرهای کاغذ شیمیایی-مکانیکی صنوبر و رفع نقایص موجود جهت استفاده از آن برای تولید کاغذ روزنامه در کارخانه چوب و کاغذ مازندران وجود دارد.موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091333220180622Investigating the effect of butanediol diglycidyl ether on the crosslinking of nanocelluloseبررسی اثر بوتان دیول دی گلیسیدیل اتر بر ایجاد اتصالات عرضی در نانوسلولز30031011667210.22092/ijwpr.2018.121609.1473FAنازنین مطیعدانشجوی دکترای گروه علوم و صنایع چوب و کاغذ، دانشکده منابع طبیعی، دانشگاه تهران، کرج، ایرانمهدی جنوبیدانشیار، گروه علوم و صنایع چوب و کاغذ، دانشکده منابع طبیعی، دانشگاه تهران، کرج، ایرانمحمد مهدی فائزی پوراستاد، گروه علوم و صنایع چوب و کاغذ، دانشکده منابع طبیعی، دانشگاه تهران، کرج، ایراناسونتا برزاکیلواستاد، گروه علوم شیمی و فناوری مواد، کامپوزیت و بایو مواد، مؤسسه پلیمر، انجمن تحقیقات ملی ایتالیا، ناپل، ایتالیاJournal Article20180428This study was focused on the preparation of an environmentally friendly nanocellulose based hydrogel in the form of pads. Hydrogels are hydrophilic three dimensional network with crosslinks, swells in water but don’t dissolve. In this research nanofibrillated cellulose and Hydroxyethyl cellulose with different ratio (1:1, 2:1, 3:1) were used to make hydrogel. Also, citric acid which has a significant advantage over other crosslinking agents in terms of toxicity and price, has been used in different amounts of 10% and 20% by weight to crosslink. In order to find optimal hydrogel preparation conditions, FTIR analysis, FESEM, time dependent swelling measurement and evaluating the thermal and rheological properties were performed. Samples with a lower ratio of nanocellulose to hydroxyethyl cellulose were found to be inappropriate due to the loss of their apparent integrity in the swelling measurement. According to FTIR results, cross-linking were performed only in samples with the highest ratio of nanocellulose to hydroxyethyl cellulose in different amounts of citric acid. Therefore, the hydrogels' characteristics were mainly influenced by the ratio of nanocellulose to hydroxyethyl cellulose and the amount of citric acid had less effect on these properties. These two successful final samples showed acceptable properties in other evaluated properties and led to the selection of optimal reactive ratios for the preparation of hydrogels for use in various industries, including the pharmaceutical industry.در این تحقیق به بررسی ایجاد اتصالات عرضی در نانو الیاف سلولزی توسط ماده شیمیایی بوتان دیول دیگلیسیدیل اتر (BDDE) بهعنوان اتصالدهنده عرضی پرداخته شده و برخی خواص فیزیکی هیدروژل حاصل مورد ارزیابی قرار گرفت. زنجیرههای پلیمری تجدیدپذیر و قابل بازیافت مورد مطالعه شامل نانوالیاف سلولزی و هیدروکسی اتیل سلولز میباشند. برای ایجاد اتصالات عرضی، از BDDE استفاده شد. BDDE یک ماده شیمیایی زیست تخریب پذیر است و نسبت به سایر اتصال-دهندههای عرضی که گروههای عاملی با پیوند اتری دارند، به میزان قابل ملاحظهای دارای سمیت کمتر میباشد. جهت بررسی اثر BDDE بر خواص فیزیکی نانوسلولز، آزمونهای FTIR، FESEM، اندازهگیری قابلیت واکشیدگی و بررسی خواص حرارتی انجام گرفت. نمونههای با نسبت کمتر نانوسلولز به هیدروکسی اتیل سلولز به دلیل پخش شدن در آب و تشکیل اتصالات عرضی کم، در آزمون اندازه گیری قدرت واکشیدگی، نامناسب شناخته شدند. اتصال عرضی در میان نمونههای با مقدار کمتر نانوسلولز به-خوبی ایجاد نشد. با افزایش مقدار نانوسلولز هیدروژلها مقاومت کافی در تماس با آب نشان دادند و در آب پخش نشدند. در میان نمونههای با مقدار بیشتر نانوسلولز، با افزایش مقدار اتصالدهنده عرضی از 20% به 40% جذب آب بهدلیل ایجاد پیوندهای بیشتر و کاهش حضور گروههای هیدروکسیل در دسترس در نانوسلولزها کاهش یافت. با توجه به نتایج FTIR، اتصالات عرضی در هر دو نمونه با مقدار نانوسلولز بالا، در مقادیر مختلف BDDE، به خوبی انجام گرفت. با افزایش مقدار BDDE پایداری حرارتی و دمای تبدیل شیشه به دلیل ایجاد پیوندهای عرضی مناسب در بین الیاف و تشکیل ساختار قویتر و پایدارتر افزایش یافت.