In this research, the effect of oil heat-treated on the outdoor performance of coatings namely, transparent resin stain, alkydi paint, semi- transparent cellulosic stian, acrylic paint coated on eastern cotton wood was investigated. For this purpose, sound specimens with the dimensions of 50×50×2 ...
Read More
In this research, the effect of oil heat-treated on the outdoor performance of coatings namely, transparent resin stain, alkydi paint, semi- transparent cellulosic stian, acrylic paint coated on eastern cotton wood was investigated. For this purpose, sound specimens with the dimensions of 50×50×2 mm (Longitudinal × tangential × radial) were prepared from sapwood. Test samples were treated with canola oil at temperatures of 180, 200 and 220 ° C for 4 hours. The coatings were the wet film thickness of 150µm were applied on the specimens using an applicator. The coating adhesion was measured according to ASTM D 4541 standard, and the color characteristics of the coating were measured according to ASTM D 2244 before and after a natural weathering for 180 days. The statistical analysis of the color change data showed that the effect of the oil heat-treatment on the color change depended on coating type. The statistical analysis of the adhesion strength data showed that the adhesion strength depended on the combination of weathering, oil heat-treatment and coating type.
Management and Economics wood
Lila Asadi khoramabadi; Abolghasem Khazaeian; Mohammad reza Masteri Farahani; Alireza Shakeri
Abstract
Heat treatment is one of the processes used to modify the properties of wood. The investigation of thermal treatment of wood has led to the improvement of heat treatment with vegetable oils. Heat treatment improves the dimensional stability and biological durability, but reduces the mechanical properties ...
Read More
Heat treatment is one of the processes used to modify the properties of wood. The investigation of thermal treatment of wood has led to the improvement of heat treatment with vegetable oils. Heat treatment improves the dimensional stability and biological durability, but reduces the mechanical properties of wood. In this research, to improve the mechanical properties with other properties of wood, soybean oil modified with maleic anhydride was used for thermal treatment. Wood speciments were subjected to heat treatment soybean oil modified with maleic anhydride at two temperature (180 and 200° C ) and three time (2, 4 and 6 hours). Untreated beech was used as comparison for each treatment conditions. In this study, the effects of heat treatment on physical properties )water absorption and volumetric changes) and mechanical properties such as Bending strength) ISO 3133-1975(, Compression strength Parallel to grain) ISO 3787-1976 (and Impact bending) DIN 52189( were examined. The test results of heat-treated with modified soybean oil and control samples showed that physical and mechanical properties increases with heat treatment.
Composite wood products
Amineh Behzadi Shahrebabak; Mehrab Madhoushi; Mohammad reza MastriFarahani
Abstract
In this study, the effect of nanoclay and coupling agent on decay resistance and physical properties (including water absorption and thickness swelling) of nanoclay- Polyethylene- MDF sanding- powder composite were investigated. For this aim, MDF sanding dust and polyethylene were used as lignocellulose ...
Read More
In this study, the effect of nanoclay and coupling agent on decay resistance and physical properties (including water absorption and thickness swelling) of nanoclay- Polyethylene- MDF sanding- powder composite were investigated. For this aim, MDF sanding dust and polyethylene were used as lignocellulose and thermoplastic material respectively. Also, Maleic anhydride grafted polyethylene (MAPE) was used in different weight percentages; 3% and 6% as a compatibilizer and nanoclay .Cloisite®15A was used in different weight percentages 2%, 4% and 6%.At first, raw materials were producted to fabricate granules by using twin-screw extruder. Then 36 panels (12 treatments by 3 repetitions) were made by hot pressing with 1 g/cm3 nominal density at dimensions by 30 cm × 28 cm × 1 cm. Then, water absorption and thickness swelling and decay resistant (loss weight) were investigated. Specimens were exposed to Trametes versicolor for 3 months, according to ASTM-D1413 standard. The results shown, water absorption and thickness swelling reduce with increasing MAPE significantly. While, at the time when nanoclay was added 2% (phr), water absorption and thickness swelling reduced significantly and then increased. Also, decay resistance was improved with increasing coupling agent and nanoclay.