Abstract
This research was performed to improve the properties of the pulp made of Aspen Deltoides, using antraquinone(AQ) catalizer. Neutral sulfite semichemical (NSSC) method in three efficiency levels of 55, 60, and 65% was applied. Cooking situations was selected as: Specific Temperature (175˚ C) , Time ...
Read More
This research was performed to improve the properties of the pulp made of Aspen Deltoides, using antraquinone(AQ) catalizer. Neutral sulfite semichemical (NSSC) method in three efficiency levels of 55, 60, and 65% was applied. Cooking situations was selected as: Specific Temperature (175˚ C) , Time (Variable) , Specific Percentage of Chemicals 14% and Anthraquinone 0.1% . In all stages of cooking, weight ratio of sodium sulfide to sodium bicarbonate was set as 4.5/1. The ratio of cooking liquid to chips was 5/1. The results indicated that AQ causes an increase in efficiency and a significant decrease in Kappa. Researches also indicated that by the use of AQ, strength indexes of the paper such as strength of burst, tearing, tensile, Ring Crush Test and Corrugating Medium Test increases. Optical experiments on hand sheets following addition of AQ, indicated increase in brightness and decrease in opacity.
Pulp and paper
Hamd Unesi kord khalili; Mehran Jalilvand; Rabi Behroz
Abstract
The purpose of this study was to investigate effects of different loading levels and addition of urea formaldehyde and polyethylene on the creep behavior of composites made from wastes of OCC recycling mills. The composites manufactured by hot press method and three-point ...
Read More
The purpose of this study was to investigate effects of different loading levels and addition of urea formaldehyde and polyethylene on the creep behavior of composites made from wastes of OCC recycling mills. The composites manufactured by hot press method and three-point bending test performed before creep test. In general, the results showed positive effects of additive materials such as urea formaldehyde and polyethylene on the creep behavior of the composites. While adding UF and PE decreased primary and final creep as well as return deformation percentage of the composites. Also the obtained results indicated that remaining creep had higher sensitivity to loading levels compared to primary and final creep. Also the increase of the load levels from 20% to 30% led to an increase in creep content of the composites.
Pulp and paper
Rabi Behroz; Hamed Unsi kord khelili; Saeid Kazemi najafi
Abstract
Effect of Kraft lignin as a compatibilizer on the short-term water absorption (2 and 24 hours) and mechanical properties of wood flour-polypropylene composites was studied. The black liquor of Chooka pulp and paper mill was acidified and Kraft lignin was extracted by precipitation. The extracted ...
Read More
Effect of Kraft lignin as a compatibilizer on the short-term water absorption (2 and 24 hours) and mechanical properties of wood flour-polypropylene composites was studied. The black liquor of Chooka pulp and paper mill was acidified and Kraft lignin was extracted by precipitation. The extracted lignin at three levels of 2, 5 and 10 percent was mixed with wood flour by physical mixing method. All materials used were oven-dried. Wood flour, lignin and PP with or without MAPP were used to produce composites by flat hot press method. The results of this study indicated that generally lignin improved physical (short term water absorption) and mechanical properties (flexural modulus, flexural strength and impact strength). The bending test result showed that without MAPP, the composites with 2 and 10 percent lignin exhibited higher flexural modulus and strength, respectively. But at the presence of compatibilizer, the composites with 5 percent lignin exhibited the highest flexural modulus and strength. The composite with 2 percent of lignin exhibited higher flexural modulus and short-term water absorption rather than the composites with 2% MAPP. This result indicated positive effect of lignin in the composites. Also the composites with 10 percent lignin exhibited the highest impact strength and short-term water absorption. But there were no significant difference between the impact strength of composites with 5 and 10 percent lignin.
Pulp and paper
Mohammad ali Azad far; Rabie Behroz; Ahmad Jahan - Latibari
Abstract
The influence of oxygen delignification as an environmental friendly process, was investigated on Soda/AQ pulp from Old Corrugated Container (OCC) fibers. Oxygen delignification at four levels of alkali (2, 3, 4 and 6% based on OD weight of pulp) has been applied and the optimum alkalinity to reach optimum ...
Read More
The influence of oxygen delignification as an environmental friendly process, was investigated on Soda/AQ pulp from Old Corrugated Container (OCC) fibers. Oxygen delignification at four levels of alkali (2, 3, 4 and 6% based on OD weight of pulp) has been applied and the optimum alkalinity to reach optimum Kappa no, yield and brightness, opacity and strength based on 60 g/m2 hand sheets were determined. The results indicated that application of oxygen delignification marginally reduced the opacity of the pulp. Tear strength increased where as tensile and burst strength decreased. Based on the comparison of the data from oxygen delignified pulp, it is concluded that oxygen can be utilized to improve the properties of soda-AQ pulp from OCC prepared for bleaching step. Carbohydrates are preserved while removing lignin. Normalized equations revealed that oxygen delignification at 3% alkali produced the best results.
Somayeh Ghasemi; Rabie Behroz
Abstract
Using high consistency pulp especially in bleaching plant is highly attractive due to considerable reduction in energy and water consumptions and low effluent volume. This research investigates the effect of consistency CMP pulp on bleaching by hydrogen peroxide. For this purpose, unbleached mixed hardwood ...
Read More
Using high consistency pulp especially in bleaching plant is highly attractive due to considerable reduction in energy and water consumptions and low effluent volume. This research investigates the effect of consistency CMP pulp on bleaching by hydrogen peroxide. For this purpose, unbleached mixed hardwood CMP pulp of Mazandaran wood and paper CO. mill was used. Bleaching was carried out with QP sequences. Pretreatment or Q stage was carried out by DTPA as a chelating agent for removing transition metals. Chelating stage had a similar condition for all pulps. bleaching with hydrogen peroxide was carried out in three levels of hydrogen peroxide 2, 3, 4% and proportion NaOH to H2O2: 0.8, 0.7, 0.6 by adding 3% sodium silicate in 70˚C and 150min at four consistency level (10, 15, 25 and 30%). After bleaching, handsheets were made with grammage 60gr/m2 from bleached pulp. The experimental results showed that high brightness and opacity and lower yellowness was obtained at 30% consistency by 2 and 3% peroxide charge. However, by using 4% hydrogen peroxide, higher brightness and lower yellowness attained at 25% consistency. Brightness is increased continuously by increasing consistency from 10 to 30% at 2, 3% peroxide. But at 4% peroxide charge, brightness is increased from 10, 15 and 25%, and then at 30% consistency is decreased significantly. Also under conditioning of 2% peroxide and 30% consistency and 2% peroxide at 25% consistency can obtain similar brightness to 3% peroxide and 25% consistency and 4% peroxide at 10% consistency. That it means of 25, 30% decrease in consumption peroxide and sodium hydroxide.
Physics and anatomy
Alireza Ghotibi far; Saeid Kazemi najafi; Rabi Behroz
Abstract
This research focused on the influence of content (5, 10 and 15 %) of glass fiber on the water absorption and thickness swelling of wood flour/E-glass fiber hybrid polypropylene composites without and with MAPP. The samples (strips with 10 mm thickness and 70 mm width) were made using a laboratory twin-screw ...
Read More
This research focused on the influence of content (5, 10 and 15 %) of glass fiber on the water absorption and thickness swelling of wood flour/E-glass fiber hybrid polypropylene composites without and with MAPP. The samples (strips with 10 mm thickness and 70 mm width) were made using a laboratory twin-screw extruder. The water absorption and thickness swelling of the composites after 2h and 24h were determined. The results showed that adding glass fiber significantly increase water absorption and thickness swelling after 2h and 24h in absence of MAPP. Whereas in presence of 2% MAPP by addition glass fiber, no significant changes were observed in water absorption and thickness swelling of the composites after 2h and 24h. MAPP considerably decreased the water absorption and thickness swelling of the studied composites