Pulp and paper
ali barzan; hossein resalati; ali ghasemian; ahmadreza saraeyan; ghasem asadpour
Abstract
In this study, the effect of pigment composition on the properties of paper prepared from CMP pulp was studied. There for 3 different pigment combinations (100% calcium carbonate (GCC), 70% calcium carbonate and 30% kaolin clay (70GCC30Clay) and 70% calcium carbonate and 25% gritty and 5% titanium dioxide ...
Read More
In this study, the effect of pigment composition on the properties of paper prepared from CMP pulp was studied. There for 3 different pigment combinations (100% calcium carbonate (GCC), 70% calcium carbonate and 30% kaolin clay (70GCC30Clay) and 70% calcium carbonate and 25% gritty and 5% titanium dioxide (70GCC25Clay5TiO2)) were made with anionic starch, latex and dispersersant and Used for coating. Physical properties included (surface roughness of the paper, Ash content and Apparent density) And the optical properties included (brightness, absorption and diffusion coefficient) and paper resistance characteristics including tensile strength, bursting resistance, tear strength based on standard TAPPI standardized measurements and Using factorial design, analysis of variance was performed and the mean of paper properties was compared with Duncan's test. The purpose of this research is to achieve the best combination for coating the paper with the improvement of physical and optical properties and maintaining resistance properties. By adding clay and dioxide titanium to calcium carbonate, the roughness of the paper surface decreased The highest roughness of the surface of the paper in the diet was observed for the control paper and the lowest was seen in the treatment of 70GCC30Clay surface. Also, the highest degree of brightness is related to 70GCC25Clay5TiO2 treatment. The highest index of tensile strength and burst strength index was related to gypsum treated paper (GCC) and also the highest tear strength index for treated paper at level 2 (70GCC30Clay).
Pulp and paper
Ali Barzan; Hossein Resalati; Ghasem Asadpour atoei
Abstract
After water purification and softening, a lot of calcium carbonate with other impurities produce and these byproducts gather and bury as mineral sludge.In this research, The quality of calcium carbonate from water softening process in mazandran wood and paper industry (MWPI) mill and effects of loading ...
Read More
After water purification and softening, a lot of calcium carbonate with other impurities produce and these byproducts gather and bury as mineral sludge.In this research, The quality of calcium carbonate from water softening process in mazandran wood and paper industry (MWPI) mill and effects of loading of this byproduct on fine paper production was investigated and the results were compared with other industrial fillers like grounded calcium carbonate(GCC) and precipitated calcium carbonate(PCC) and also china clay (kaolin).From the paper structural viewpoint , the fine paper that filled with water softening calcium carbonate (derived after water softening process) have more bulk(bulkier) and more porous and rougher surface compare to fine papers that filled with the common industrial fillers.From the paper strength properties viewpoint , the fine paper that filled with water softening calcium carbonate have less decrease in tensile and burst strength but have not suitable tear strength properties. From the paper optical properties viewpoint, the fine paper that filled with water softening calcium carbonate, because of particles size and impurities of this filler have the least light scattering coefficient and consequently have less brightness and opacity.Adding of 10 and 20 percent precipitated calcium carbonate to by water softening calcium carbonate cause paper porosity and strength decreasing but the optical properties of hand sheets was increased.