Mohammad Ahmadi; Sahab Hejazi; Kamiar Salehi
Abstract
In this study, the effect of beating time on morphologic, physical and strength properties of soda and monoethanolamine pulps obtained from wheat straw was studied, in order to optimize the time for beating operation. Beating of the pulps was applied in different time by laboratory jokromill beater. ...
Read More
In this study, the effect of beating time on morphologic, physical and strength properties of soda and monoethanolamine pulps obtained from wheat straw was studied, in order to optimize the time for beating operation. Beating of the pulps was applied in different time by laboratory jokromill beater. The results showed that rising time of beating leads to increasing the freeness (SR) of pulps and monoethanolamine pulp reached to maximum amount of freeness (SR) in less time as compared to soda pulp. In addition, it is found that monoethanolamin pulp obtained the maximum amount of tensile index (91.3 N.m/g) after 30 min beating time and after that longer time of beating process had no significant effect on increasing the tensile index. About soda pulp it is observed that tensile index was increased significantly by rising the time of beating process and for this kind of pulp, maximum amount of tensile index (87.7N.m/g) was obtained in 50 min beating process. The highest burst index for soda pulp was 5 Kp.m2 which was obtained by 50 min beating process. About mono ethanolamine pulp burst index increased by rising time of beating Process and reached to its maximum amount (5.6 Kp.m2) and after that its amount decreased. Rising the time of beating process led to decreasing the tear index in both of kinds of pulp consist of monoethanolamin and soda pulp. The results showed that mono ethanolamine pulp had the higher yield and better beating ability in comparison with soda pulp which can be caused by better ability for carbohydrates and minerals retaining in monoethanolamin pulp.
Pulp and paper
Jaber Hossein zade; Ali Abdolkhani; Mohammad Emami nasab; Hamid Khodabandeh lo; Mohammad Ahmadi
Abstract
In this research Tension Wood (TW) and Normal Wood (NW) of Poplar were analyzed for pulp production using Kraft pulping process. After preparing samples, Biometric characteristics of the NW and TW fibers were measured and samples were converted to pulp. Pulp hand sheets mechanical and physical properties ...
Read More
In this research Tension Wood (TW) and Normal Wood (NW) of Poplar were analyzed for pulp production using Kraft pulping process. After preparing samples, Biometric characteristics of the NW and TW fibers were measured and samples were converted to pulp. Pulp hand sheets mechanical and physical properties were measured and results were showed that NW fibers compared to TW fibers had a higher Rankle coefficient and aspect ratio. However the flexibility of NW fibers was better than TW fibers. Based on Results, although TW pulp yield was 13 percent greater than NW pulp yield but kappa number in TW was 45 percent lower than NW. Mechanical and physical properties of hand sheets indicated that the tensile and burst strengths of tension wood were comparatively lower than that of normal wood. Also the papers produced by equally mixture of TW fibers and NW fibers were showed higher tensile and burst strengths. Optical and color analyses of samples were showed an improvement in brightness and whiteness for TW hand sheets compared to NW papers. General speaking results were showed that presence of TW fibers inside pulp had not a significant effect on quality of produced pulp and papers.