Pulp and paper
Sobhan Jahanshahlou; Amir Khosravani; Mehdi Rahmaninia
Abstract
Production of test liner and fluting from old corrugated containers, is one of the most common paper recycling processes in Iran. This type of papers, have high basis weight and also contain significant fine fibrous and non-fibrous materials; hence, the drainage and in addition, the retention of fine ...
Read More
Production of test liner and fluting from old corrugated containers, is one of the most common paper recycling processes in Iran. This type of papers, have high basis weight and also contain significant fine fibrous and non-fibrous materials; hence, the drainage and in addition, the retention of fine materials, are the obstacles these paper mills may encounter. In these cases, usually application of drainage/retention aids, such as nanoparticle systems can be of much help. In this due, colloidal silica and bentonite are the two of the most commonly used nano-particles with polyelectrolytes in papermaking wet-end. Therefore, in this research, the effect of bentonite and silica sol nano-particles on the performance of cationic starch was compared in terms of drainability, retention and strength properties of paperboard from recycled old corrugated containers. The analysis of the particle size for these two nanoparticles showed that although the thickness of bentonite platelets (maximum 22 nm) was less than nanosilica dimensions (less than 50 nm), the effect of bentonite-cationic starch was not significant in terms of retention, against the nanosilica. Regarding the drainability, following dosing of both silica and bentonite, the parameter much improved (up to 186% in the case of nanosilica). On the other hand, application of cationic starch containing systems in paper handsheets resulted in improvement in tensile and tear indices, however, these properties decreased following addition of nano-particles. Also, internal bonding (Scott- type) incredibly increased (up to 354%) by application of cationic starch and nanosilica. At last, generally in the case of OCC furnish, the nanosilica-cationic starch system had a better performance in terms of drainability, retention of fine materials and fiber fines and also strength properties, rather than cationic starch-bentonite.
Amir Eshraghi; Habib alah Khademeslami; Amir Nourbakhsh; Behzad Bazyar; Mohammad Talaeipoor
Abstract
In this study, aspen chips with OCC (Old Corrugated Container) were used in particleboard production and samples were prepared at two different levels of resin contents (%9 and %10) and three levels of combination:
1- %25 OCC +%75 aspen, 2- %50 OCC + %50 aspen, ...
Read More
In this study, aspen chips with OCC (Old Corrugated Container) were used in particleboard production and samples were prepared at two different levels of resin contents (%9 and %10) and three levels of combination:
1- %25 OCC +%75 aspen, 2- %50 OCC + %50 aspen, 3- %75 OCC +%25 aspen. Indeed in this study these two mentioned factors are variable and other factors such as press temperature: 165 ºC, press time: 5 minute, mat moisture %12, board density 0.75 g/cm3 and press pressure 30 kg/cm2 were constant. After the boards were manufactured according to DIN-68763 standard, were undergone different tests such as: bending strength, modulus of elasticity, internal bonding strength and thickness swelling after 2 & 24 hours immersion in water. The results indicate that second ratio(%50 OCC and %50 aspen chips) is proper for bending applications and the first ratio(%25 OCC and %75 aspen chips) is proper for tensile and thickness swelling applications. Therefore, applying the OCC more than %50 in manufacturing combination; result in decreasing the physical and mechanical properties. Moreover the results show that when the resin content increases, the board features improve.
Physics and anatomy
Kazem Dost hosseini; Hamideh Abdolzadeh
Abstract
The feasibility of using of wood and old corrugated container (OCC) fibers on the surface layers of particleboards was investigated. The kind of applied furnish at surface layers, the moisture and adhesive content were considered as variables and their effects on hardness and roughness of manufactured ...
Read More
The feasibility of using of wood and old corrugated container (OCC) fibers on the surface layers of particleboards was investigated. The kind of applied furnish at surface layers, the moisture and adhesive content were considered as variables and their effects on hardness and roughness of manufactured particleboards were examined. The results indicated that the application of both wood fibers and OCC on the surface layers of particleboard resulted in improving surface quality. The moisture and adhesive contents at high levels led to improved surface quality. The control samples with 10% adhesive and 14% moisture content yielded more hardness than the other. The smoothest surfaces appeared on the particleboards manufactured with wood and OCC fibers as well as 14% moisture content and 12% adhesive.