Abstract
In this study, pulp and handsheets characteristics of radiata pine wood kraft pulp was evaluated. The ratiata pine wood was collected from Chamestan Noor Research Station. Average dry and basic specific gravity of wood were determined as 0.342 and 0.308 g/cm3 and average fiber (tracheid) dimension ...
Read More
In this study, pulp and handsheets characteristics of radiata pine wood kraft pulp was evaluated. The ratiata pine wood was collected from Chamestan Noor Research Station. Average dry and basic specific gravity of wood were determined as 0.342 and 0.308 g/cm3 and average fiber (tracheid) dimension including fiber length, fiber diameter, lumen diameter and cell wall thickness were measured as 2460, 40.35, 33.17 and 3.59 µm, respectively. The chemical composition was determined as holocellulose 72.07%, alfa cellulose 43.41%, lignin 29.95%, ash 0.50 % and extractive as 1.75%. Kraft (Sulfate) process was applied for cooking and pulping the wood. A factorial randomized complete block design test was conducted to compare the fiber dimensions, physical properties, chemical composition and the yield of the pulp. To examine strength properties of handsheets, ANOVA statistical analysis was used and for grouping the means Duncan test were applied. The minimum and maximum yield and kappa number of these pulps were measured at 40.33%, 50.43% and 33.89, 60.22, respectively. The results of handsheet strength measurement indicated that radiata pine wood kraft pulp provides suitable substitute for imported long fiber pulp to be mixed with short fiber hardwood pulp.
Hossein Shob chary; Ahmad reza Saraeyan; Ali Ghasemian
Abstract
This study was conducted to investigate the properties of cotton stalks APMP pulp. APMP prepared from chipped cotton stalks. the pulps were prepared separately from debarked and bark containing stalks using three two-stage treatments.Sodium hydroxide charge as a constant level of 4% and hydrogen ...
Read More
This study was conducted to investigate the properties of cotton stalks APMP pulp. APMP prepared from chipped cotton stalks. the pulps were prepared separately from debarked and bark containing stalks using three two-stage treatments.Sodium hydroxide charge as a constant level of 4% and hydrogen peroxide at three levels of 0, 1 and 2% were used in to two-stages, sodium hydroxide as a constant level of 2% and hydrogen peroxide at three levels of 2, 3, 4% were applied. Other conditions of pulping was time's of 20 min for first stage and 100 min for second stage, temperature 70°C and l/w:6:1 as fixed factors considered. Pulp yield determined after neutralization and defiberation. All the pulps were refined up to 300 (ml, CSF) freeness and handsheets were made, then and properties of papers measured using TAPPI standards. Results showed that the pulp yield and brightness was higher in free-bark compared to bark-containing conditions. Also paper produced in free-bark condition with cotton stalks core, resulted the higher tensile and burst indexes and higher breaking length compared to whole cotton stalk.While tear index didn’t show significant difference.Generally, caliper and bulk rates were high in total treatments (free-bark and bark-containing conditions) from cotton stalk APMP process.
Pulp and paper
Somayeh Ghasemi; Ahmad reza Saraeyan
Abstract
Comparative study of pulp yield of sap wood and heart wood of Populus deltoides under both Kraft and soda cooking process have been showed that the heart wood pulp has a lower yield than that of sap wood pulp. Yield of heart wood and sap wood soda pulps was 4 percentages higher than Kraft pulp. Contrary ...
Read More
Comparative study of pulp yield of sap wood and heart wood of Populus deltoides under both Kraft and soda cooking process have been showed that the heart wood pulp has a lower yield than that of sap wood pulp. Yield of heart wood and sap wood soda pulps was 4 percentages higher than Kraft pulp. Contrary to yield, residual lignin content (Kappa number) is more in heart wood pulp than sap wood pulp in both processes. Kappa numbers of heart wood and sap wood Kraft pulps were about 34% lower than soda pulps. The results showed that in spite of lower yield of heart wood than sap wood, the residual lignin of heart wood pulp was more than sap wood pulp. The higher delignification efficiency of Kraft cooking is related to cooking liquor compositions, especially Na2S
Pulp and paper
Said mohammad Mazhari mosavi; Saeed Mahdavi; Syed zyaldin Hosseini; Hossein Resalti; Hossein Usefi
Abstract
This research is aimed to study the possibility of rapeseed straw (Hayolla401) pulping and its paper characteristics, using Soda-AQ process. The average fiber length was found 1.04 millimeter and the average fiber diameter, lumen and thickness were found 28.00, 19.09, and 4.91 micrometer, respectively. ...
Read More
This research is aimed to study the possibility of rapeseed straw (Hayolla401) pulping and its paper characteristics, using Soda-AQ process. The average fiber length was found 1.04 millimeter and the average fiber diameter, lumen and thickness were found 28.00, 19.09, and 4.91 micrometer, respectively. Cellulose, lignin, extractive material (acetone solved) and ash were measured 41.66, 16.00, 1.63, and3.46 percent, respectively. Cooking condition was determined as follow: Soda as 16, 18, and 20 percent on the basis of rapeseed dry straw, temperature was set at 175 and 185 Cº, cooking time was set at 40 and 70 minutes, and straw to liquid ratio was set at 1/8. The amount of anthraquinone added to cooking liquor was 0.2%, based on rapeseed dry straw. Using severe cooking factors caused reduction of yield and Kappa number in both methods. Refining was performed on selected pulps in order to reach 35025 (ml,CSF) freeness. The 60 gr/m² hand sheets were made in order to determine mechanical strength and physical properties. Average thickness, density and bulk is measured at 86.4µ, 0.69gr/cm³ and 1.44cm³/gr respectively. Average tear index, burst index, breaking length and tensile indexare measured at 4.6 mN.m²/gr, 3.5 kpa.m²/gr, 7.4km and 72.6Nm/g respectively.
The results showed that however screen yield of rapeseed straw pulp is low but kappa number and mechanical properties of pulp is suitable,compared with the other agriculture residues, so Rapeseed pulp can be used in paper making industries.