@article { author = {Kazemi, Sayed mahmood and Enayati, Aliakbar and Rahymian, Heshmatalah}, title = {RELATIONSHIP BETWEEN WOOD EXTRACTIVES AND WOOD DECAY}, journal = {Iranian Journal of Wood and Paper Science Research}, volume = {18}, number = {شماره 2}, pages = {139-154}, year = {2003}, publisher = {Research Institute of Forests and Rangelands}, issn = {1735-0913}, eissn = {2383-112X}, doi = {10.22092/ijwpr.2003.117542}, abstract = {The durability of following five wood species: Zelkova carpinifolia, Ulmus glabra, Pterocarya fraxinifolia, Carpinus betulus and Acer laetum were studied. Wood blocks exposed to Trametes versicolor(a white rot fungus) under laboratory conditions according to DIN52176 standard. After 16 weeks incubation the heart wood of Z. carpinifolia showed 2.19% reduction in weight loss, while U glabra with 41.69%, C. betulus with 45.64%, A. laetum with 53.03% and P. Fraxinifolia with 43.08% weight losses were very decayed. For finding relationship between amount of wood decay and wood extractives a regression was carried out. The percentages of extractive materials by using T20403 standard were 13.84% in Z. carpinifolia, 4.51% in U. glabra, 2.74% in C. betulus, 3.88% in A. laetum, and 4.11% in P. fraxinifolia. Finally there was a negative correlation between rate of decay and amount of wood there was expect P. fraxinifolia. for all wood species extractives.}, keywords = {WEIGHT LOSS,EXTRACTIVES,WOOD DURABILITY,DECAY,TRAMETES VERSICOLOR,AZAD,MALAG,AFRA,VAN AND MAMRAZ}, title_fa = {ارتباط بین مواد استخراجی چوب و پوسیدگی قارچی}, abstract_fa = {میزان مقاومت بیولوژیکی چوبدرون گونه های آزاد (Zelkova carpinifolia)، ملج (Ulmus glabra)، ممرز (Carpinusbetulus)، افرا (Acer laetum)، و زبان گنجشک (Pterocaria fraxinifolia) در مقابل حمله قارج رنگین کمان (Trametesversicolor) مورد مطالعه قرار گرفت. پس از 16 هفته، میانگین کاهش جرم نمونه ها به ترتیب 2.19% در آزاد، 41.69% در ملج، 45.64% در ممرز، 53.03% در افرا، و 43.08% در زبان گنجشک تعیین گردید. میزان مواد استخراجی این گونه ها نیز از طریق روش T20403-76، تعیین، به طوری که چوبدرون آزاد دارای بیشترین مقدار مواد استخراجی (13.84%)، و سایر گونه ها به ترتیب: ملج 4.51%، ممرز 2.74%، افرا 3.88%، و زبان گنجشک 4.11% مواد قابل استخراج داشتند. نتایج آماری نشان داد که بین مقدار مواد استخراجی و میزان کاهش جرم چوبدرون همه گونه ها به استثنای گونه زبان گنجشک یک رابطه مستقیم خطی و منفی وجود دارد.}, keywords_fa = {کاهش جرم,مواد استخراجی,دوام طبیعی,پوسیدگی,قارچ رنگین کمان,آزاد,ممرز,ملج,افرا و زبان گنجشک}, url = {https://ijwpr.areeo.ac.ir/article_117542.html}, eprint = {https://ijwpr.areeo.ac.ir/article_117542_fcf9e79d755608b8a59f215b7d3bc9a8.pdf} } @article { author = {Familian, Hossein and Hosseinzadeh, Abdolrahman and Asareh, Mohammad hassan and Sadeghi, Sayed mosa and Salehi, Kamyar}, title = {COMPARATIVE INVESTIGATION ON THE ANATOMICAL, PHYSICAL AND CHEMICAL CHARACTERISTICS OF ZIZIPHUS SPINA - CHRISTI (L.) WILD FROM TWO REGION IN IRAN}, journal = {Iranian Journal of Wood and Paper Science Research}, volume = {18}, number = {شماره 2}, pages = {155-184}, year = {2003}, publisher = {Research Institute of Forests and Rangelands}, issn = {1735-0913}, eissn = {2383-112X}, doi = {10.22092/ijwpr.2003.117543}, abstract = {Ziziphus spina- christi of the family Rhamnaceae is widely distributed especially in the southern region of Iran and considered as one of the most drought - resistant sub species of the country. This investigation is the first attempt to study wood properties of this species, in order to contribute to a better understanding of it. It seems necessary to recognize the best utilization of this wood that are potentially available and easy to caltivate in Iran.The results of this study revealed that Ziziphus spina - christi is a diffuse - porous with pores round to oval, dense, hard and fine - textured wood. The length of vessel elements is medium, and the diameter relative high, few vessels per unit area and the type of perforation plates is simple. Parenchyma scanty paratracheal, vasicentric and rarely aliform. Libriform fibers length medium, thin to thick - walled. Rays 1-2 cells wide with medium length and not visible with nakedeye, crystals are common in most rays. In this species also percentages of cellulose and lignin are high but ash and extractive soluble in acetone content was found to be low.}, keywords = {ZIZIPHUS SPINA- CHRISTI (L.) WILD WOOD,Anatomy,PHYSICAL,CHEMICAL,PARENCHYMA,VESSEL}, title_fa = {بررسی مقایسه ای ویژگیهای آناتومی، فیزیکی و شیمیایی چوب کنار در دو منطقه استان بوشهر}, abstract_fa = {درخت کنار Ziziphus spina- christi (L.) Willd یکی از گونه های پرطاقت در مقابل گرما و خشکی می باشد و در مناطق جنوبی کشور سازگار بوده و به راحتی رشد می کند، بنابراین شناخت ویژگیهای بنیادی آن جهت شناخت بهتر قابلیتهای کاربردی آن ضروری است. در این بررسی مطالعه خصوصیات آناتومی چوب براساس دستورالعمل IAWA، خصوصیات فیزیکی بر مبنای استاندارد ASTM و مطالعه خصوصیات شیمیایی آن برمبنای استاندارد TAPPI انجام شد. براساس بررسی انجام شده، کنار دارای چوبی با بافت متوسط تا ریز بافت بوده و اندازه منافذ (پونکتواسیون) آوندی در آن متوسط (8.5 میکرومتر) است. تیغه آوندی کامل، پراکنده آوند، طول آوند با میانگین 460 میکرومتر در دسته آوندهای با طول متوسط و قطر آوند با میانگین 110 میکرومتر در دسته آوندهای قطور قرار میگیرد. تعداد آوند با میانگین 14 عدد در میلیمتر مربع کم، پارانشیم محوری به صورت دور آوندی و حاشیهای، اشعه های چوبی کوچک، تعداد اشعه چوبی متوسط و حاوی بلور و ذرات نشاسته میباشد و طول الیاف با میانگین طول 971 میکرومتر متوسط است. منافذ ساده برروی پارانشیم عرض برخی اوقات به صورت محوری در یک ردیف قرار میگیرند. چوب کنار با میانگین جرم مخصوص خشک 0.703گرم بر سانتیمتر مکعب نیمه سنگین و درصد هم کشیدگی حجمی آن متوسط است. میانگین میزان سلولز 49.28 و لیگنین 26.98 درصد, خاکستر 1.75 درصد و مواد استخراجی محلول در استن 1.68 درصد است. هیچ یک از صفات اندازه گیری شده در طول درخت تغییر معنی داری نداشتند. }, keywords_fa = {کنار,آناتومی چوب,فیزیک و شیمی چوب,دوائر رویشی,پارانشیم,آوند}, url = {https://ijwpr.areeo.ac.ir/article_117543.html}, eprint = {https://ijwpr.areeo.ac.ir/article_117543_1b65e15f549d9a751da92ae106c8e004.pdf} } @article { author = {Roohnia, Mehran and Jahan latibari, Ahmad and Hosseini, Sayed Zyae Aldin}, title = {PULPING PROPERTIES OF RINDS FROM SUNFLOWER SEEDS}, journal = {Iranian Journal of Wood and Paper Science Research}, volume = {18}, number = {شماره 2}, pages = {185-204}, year = {2003}, publisher = {Research Institute of Forests and Rangelands}, issn = {1735-0913}, eissn = {2383-112X}, doi = {10.22092/ijwpr.2003.117544}, abstract = {In this research, pulping of rinds from sunflower seeds by soda process is studied. Fiber length was 0.89 millimeters and its chemical content, contained 40.5% Cellulose, 30.5% Lignin, 3.33% Ash and 1.93% Extractives. Conditions of Soda process were three different soda consummations of (Chemical charge) 14%, 16% and 18%. Liquor on rinds ratio, was equal to 6, and period of digestion was 30 minutes. Yield and Kappa number on the best choice of conditions of pulping (165 degree of centigrade temperature and 16% soda consumption) were measured respectively 55.7% and 74.96.Using PFImill, four kinds of pulps with four different free nesses were produced from the proper Pulp and were changed to hand sheets. Study on mechanical strength of hand sheets showed that beating has no effect on tear strength from 30 to 40 SR and it reduces this strength after more beating. Practically, no effect was observed on burst strength and breaking length during beating from 30SR to 60SR. This lignocellulose, agricultural residue is a cheap by-product in Sunflower-oil producer factories. Some of them is as a food for live-stocks and some is burned as a source of energy. Because of this, using rind from sunflower seeds in Paper and other cellulosic industries can be useful.}, keywords = {pulp,PAPER,SODA PROCESS,RINDS,SEEDS-SUNFLOWER}, title_fa = {بررسی ویژگیهای کاغذ تهیه شده از پوست دانه آفتابگردان}, abstract_fa = {در این تحقیق، تهیه کاغذ از پوست دانه آفتابگردان مورد مطالعه قرار گرفته است. طول الیاف پوست دانه آفتابگردان 0.89میلیمتر و ترکیبهای شیمیایی پوست دانه آفتابگردان شامل سلولز 40.5%، لیگنین 30.5%، خاکستر 3.33% و مواد استخراجی محلول در استن و الکل 1.93% تعیین گردید. شرایط پخت سودا شامل سه درجه حرارت 165،170 و 175 درجه سانتیگراد، قلیاییت فعال در سه میزان 14%، 16% و 18% بر مبنای سود سوزآور و نسبت مایع پخت به پوست 6 به 1 انتخاب شد. بازده و عدد کاپا در مناسبترین شرایط پخت (درجه حرارت 165 درجه سانتیگراد و قلیاییت فعال 16%) بر مبنای سود به ترتیب، 55.7% و 74.96% بدست آمدند.از این خمیر توسط پالایشگرPFI ، 4 نوع خمیر کاغذ با 4 درجه روانی 30، 40، 50 و 60 درجه SR تهیه و از هر نوع 5 برگ کاغذ دست ساز تهیه گردید. بررسی در مورد مقاومتهای کاغذ بدست آمده نشان داد که افزایش پالایش در محدوده تغییر درجه روانی از 30 تا 40 SR بر روی مقاومت در برابر پاره شدن بی تاثیر و با افزایش پالایش از این مقاومت کاسته می شود. همچنین در محدوده مورد بررسی (30 تا 60 SR) مشاهده شد که افزایش پالایش تاثیری در مقاومت در برابر ترکیدن و طول شکست کاغذ بدست آمده ندارد.این ماده لیگنوسلولزی در کارخانه های روغن کشی از آفتابگردان، به مقدار زیادی به صورت دورریز، تولید می شود. بخشی از آن به مصرف خوراک دام می رسد و بخشی دیگر به عنوان منبع حرارت سوزانده می شود. بدین جهت استفاده از آن می تواند در صنایع کاغذسازی و دیگر صنایع سلولزی مفید باشد.}, keywords_fa = {خمیرکاغذ,کاغذ,فرایند سودا,پوست دانه آفتابگردان}, url = {https://ijwpr.areeo.ac.ir/article_117544.html}, eprint = {https://ijwpr.areeo.ac.ir/article_117544_ea9e890066078741515223d61da2733b.pdf} } @article { author = {Arab tabar firoz jaei, Habib alah and Reza nezhad, Ali and Hosseinzadeh, Abdolrahman}, title = {DURABILITY OF 6 WOOD SPECIES AGAINST MARINE BORERS IN CHABAHAR PORT COASTS (OMAN SEA)}, journal = {Iranian Journal of Wood and Paper Science Research}, volume = {18}, number = {شماره 2}, pages = {205-218}, year = {2003}, publisher = {Research Institute of Forests and Rangelands}, issn = {1735-0913}, eissn = {2383-112X}, doi = {10.22092/ijwpr.2003.117545}, abstract = {Samples of 6 wood species including: Oak (Quercus castaneafolia) Horn beam (Carpinus betulus), Beech (Fagus orientalis), Alder (alnus subcordata), Oriental plane (platanus orientalis) and Babul (Acasia arabica) were treated with Creosote. The dimension of samples was 200 x 75 x 20 mm. Both treated and untreated samples were installed in sea water (Chabahar port coasts) according to IRG/WP-4432 (1985). After 8, 12, 24, 33 months, the samples were inspected according to recommendation of ASTM D 2481. During this installation period, the control samples of Alder after 8 months, the samples of Oak and Hornbeam, Beech and Oriental plane after 12 months, seriously attacked. The grade of samples Babul after 12 months installation in sea water was 3.8. Treated samples with Creosote, samples of Oak 24 months and Hornbeam, after 33 months, were seriously attacked.So, treating with creosote using full cell process causes an increase in wood, durability against marine boreres approximately more than two times of untreated samples.}, keywords = {CREOSOTE,durability,MARINE BORERS,Oak,HORB BEAM,BEECH AND ALDER}, title_fa = {بررسی دوام 6 گونه چوبی ایران درمقابل عوامل مخرب دریایی در بندر چابهار}, abstract_fa = {نمونه های آزمودنی از گونه های بلند مازو (Quercus castaneafolia)، ممرز (Carpinus betulus)، راش (Fagusorientalis)، توسـکا (Alnus subcordata)، چنار (Platanus orientalis) و کرت (Acasia arabica) به ابعاد 200×75×20میلیمتر تهیه شدند. نمونه های آزمودنی گونه های بلند مازو و ممرز به روش بتل با ماده حفاظتی کرئوزوت اشباع شدند. نمونه های اشباع شده همراه نمونه های شاهد این گونه ها در ساحل بندر چابهار در داخل دریا نصب شدند. دوام نمونه های آزمودنی در مقابل عوامل مخرب دریایی (marine borers) پس از مدت 8، 12، 24 و 33 ماه استقرار در آب دریا، براساس آیین نامه شماره D-2481 استاندارد ASTM مورد ارزیابی قرار گرفتند. براساس نتایج ارزیابی نمونه های آزمودنی، نمونه های شاهد توسکا پس از 8 ماه به درجه تخریب 0، بلند مازو، ممرز و راش پس از مدت 12 ماه به درجه تخریب 0 و کرت پس از مدت 12 ماه به درجه تخریب 3.8 رسیدند. نمونه های آزمونی اشباع شده با کرئوزوت گونه های بلند مازو پس از مدت 24 ماه استقرار در دریا و ممرز پس از مدت 33 ماه استقرار در دریا، به درجه تخریب 0 رسیدند. بدین ترتیب، اشباع با کرئوزوت، باعث افزایش دوام چوبها در مقابل حفاران دریایی تقریبا به میزان دو برابر نمونه های شاهد شد.  }, keywords_fa = {کرئوزوت,دوام,حفاران دریایی,بلند مازو,ممرز,راش,توسکا}, url = {https://ijwpr.areeo.ac.ir/article_117545.html}, eprint = {} } @article { author = {Fakhryan roghani, Abbas and Hosseinzadeh, Abdolrahman and Golbabaei, Fardad and Hosseinkhani, Hossein}, title = {INVESTIGATION ON DELIGNIFICATION AND PULPING OF SPRUCE (PICEA ABIES)}, journal = {Iranian Journal of Wood and Paper Science Research}, volume = {18}, number = {شماره 2}, pages = {219-238}, year = {2003}, publisher = {Research Institute of Forests and Rangelands}, issn = {1735-0913}, eissn = {2383-112X}, doi = {10.22092/ijwpr.2003.117546}, abstract = {Two 22 years old spruce trees (Picea abies) from Picesoon region of Gilan province are investigated. These samples were transferred to the Alborz research center. The physical, anatomical and chemical properties of samples were determined. Dry and critical specific gravity, fiber length, amount of cellulose and lignin were measured at 0.334, 0.306, 3.07 mm, % 59.74 and % 28.94 respectively. Average yield and kappa number of kraft pulp at %16, %18 and % 20 effective alkalis were determined at 48/67%, 44.67%, 45.63% and 46.85, 33.98 and 26.89 respectively. The result of this research indicates that production of suitable pulp from picea abies wood is possible.}, keywords = {PICEA ABIES,KRAFT PROCESS,EFFECTIVE ALKALI,CELLULOSE,LIGNIN,pulp}, title_fa = {بررسی لیگنین زدایی و کاغذسازی چوب درخت نوئل (پیسه آ آبیس)}, abstract_fa = {از دو اصله درخت 22 ساله پیسه آ آبیس (Picea abies) از منطقه پیسه سون اسالم استان گیلان نمونه برداری شده است. میانگین جرم ویژه نسبی خشک و بحرانی این درختان 0.334 و 0.306 اندازه گیری شده است. میانگین طول تراکئیدها، قطر تراکئیدها، قطر حفره سلولی و ضخامت دیواره تراکئیدها به ترتیب 3.07 میلیمتر، 44.67 میکرون، 36.29میکرون و 4.19 میکرون بدست آمدند. ضریب لاغری الیاف این درخت 68.72 و ضریب نرمش و ضریب رانکل آن به ترتیب81.23 و 23.02 تعیین شدند. میانگین میزان سلولز، لیگنین، خاکستر و مواد استخراجی چوب این درخت به ترتیب59.74%، 28.94%، 0.3% و 1.41 درصد اندازه گیری شدند. در اثر افزایش میزان قلیاییت موثر و در نتیجه انحلال بیشتر لیگنین، بازده و عدد کاپای خمیر کاغذها کاهش یافت، به طوری که بازده خمیر کاغذها در قلیاییت موثر 16% برابر با 48.67 درصد، قلیاییت موثر 18% برابر 44.67 درصد و در قلیاییت موثر 20% برابر با 45.63 درصد و عدد کاپای آنها نیز به ترتیب 46.85، 33.98 و 26.89 اندازه گیری شد. نتایج اندازه گیری مقاومت کاغذها نیز نشان داد که با افزایش زمان پخت تغییرات مقاومتهای بدست آمده در سطح 1% معنی دار شده است.}, keywords_fa = {پیسه آ آبیس,روش کرافت,قلیاییت موثر,سلولز,لیگنین و خمیرکاغذ}, url = {https://ijwpr.areeo.ac.ir/article_117546.html}, eprint = {https://ijwpr.areeo.ac.ir/article_117546_942e4ad0fc7958fb535f61f8c5eee27d.pdf} } @article { author = {Salehi, Kamyar and Hosseinzadeh, Abdolrahman and Familian, Hossein}, title = {STUDY ON COTTON STEM FOR CELLULOSIC INDUSTRIES}, journal = {Iranian Journal of Wood and Paper Science Research}, volume = {18}, number = {شماره 2}, pages = {239-267}, year = {2003}, publisher = {Research Institute of Forests and Rangelands}, issn = {1735-0913}, eissn = {2383-112X}, doi = {10.22092/ijwpr.2003.117547}, abstract = {In order to investigate the possibility of utilizing cotton stem in cellulosic industries chemical, physical and anatomical properties of cotton stem (var. varamin) was investigated.Cotton wood fiber length, fiber diameter, lumen diameter and cell wall thickness was measured at 840 mm, 23.9mlm, 16/11mm, and 3/9mm respectively.Cotton stem oven-dry density, basic density, and air-dry density were measured at 0/44 gr./cm3, 0.4Ogr/cm3, and .42gr/cm3.Shrinkage and swelling was measured at 7.7 %, 8.3% and porosity was measured at 70.5%.Chemical composition was as follow: cellulose 52%, lignin 29.2%, ash 104% and extractives 6.8%.Anatomical features were as follow: Growth ring boundaries distinct or absent Wood diffuse-porous. Vessels in diagonal or radial pattern grouping:partly solitary partly in radial multiples of 2-4-6 or very small cluster Simple perforation plate. Intervesse pit alternate. Intervessel pit size: minute -< 4mm. Vestured pits absent. Vessel-ray pits with much reduced borders to apparently simple Helical Thickening absent. Mean tangential diameter of vessel lumina 50-100mm. Vessels per square millimeter 20-40 vessels. Mean vessel element length - < 350mm. Tyloses Gums & deposits absent. Fiber with simple to minutely bordered pits. Helical thickening in ground tissue fibers absent.Nonseptate fiber present. Fibers very thin walled. Rays with multi seriate portion as wide as uniseriate portion. Aggregate rays absent. Ray height> 1mm. Body ray cells procumbent with over 4 rows of upright  And square marginal cells Ray per millimeter 4-12/mm.}, keywords = {Anatomy,FIBER,RAY,VESSEL ELEMENTS,BORDERED PIT,UNISERIATE}, title_fa = {بررسی خصوصیات بنیادی چوب ساقه پنبه رقم ورامین جهت استفاده در صنایع سلولزی}, abstract_fa = {رقم ورامین یکی از رقمهای ارزشمند گیاه پنبه است که نزدیک به 40% پنبه کاری کشور در مناطق مرکزی ایران و خراسان و بخشی از استانهای اردبیل و آذربایجان شرقی را زیر پوشش دارد. با توجه به سیاست جایگزینی ضایعات کشاورزی به جای محصولات جنگلی در کارخانه های صنایع سلولزی و حجم فراوان این ماده اولیه مناسب در مزارع کشور و توجه به اینکه شناخت خصوصیات ماده اولیه، یکی از ملزومات استفاده صحیح از آن در صنعت می باشد بررسی خصوصیات بنیادی در مورد چوب ساقه پنبه مورد توجه قرار گرفت.در این تحقیق نمونه های آزمونی از مزرعه موسسه تحقیقات پنبه ورامین به آزمایشگاه های مجتمع تحقیقاتی البرز منتقل شد و آزمایشهای متعدد بر روی آنها انجام گرفت. آزمایشهای آناتومی و تشریحی بر طبق استانداردهای IAWA و آزمایشهای فیزیکی چوب بر طبق استانداردهای ASTM و آزمایشهای شیمیایی چوب بر طبق استانداردهای TAPPI انجام گرفت. چوب ساقه پنبه ورامین پراکنده آوند و آوندها معمولا به صورت تک، دوتایی و همچنین دسته های 4-6-8 تایی هم مشاهده می شود که معمولا به صورت شعاعی قرار دارند به ندرت دسته های خوشه ای با تعداد کم آوند هم مشاهده می شود. تیغه بین آوندی از نوع کاملا ساده و گرد می باشد. آرایش منافذ دیوار آوندی از نوع منافذ پشت سر هم طولی می باشد، متوسط قطر منافذ دیوار آوندی 3.7 میکرون و تعداد منافذ در ناحیه تلاقی آوند و اشعه کاهش می یابد و پراکنده با شکلهای گرد و یا نامنظم، میانگین قطر آوندها 740 میکرون و تعداد آوندها 23.2 عدد در میلیمتر مربع اندازه گیری شد. میانگین طول عناصر آوندی 188.4 میکرون و هیچگونه تیلی مشاهده نشد. فیبرها با منافذ ساده و پراکنده با قطری کمتر از 3 میکرون دیده می شوند. فیبرها دارای دیواره نازک و فاقد ضخامت مارپیچی هستند. پارانشیم محوری در اطراف آوندها مشاهده می شود. اشعه چوبی ناهمگن و با سلولهای با اندازه های متفاوت دیده می شوند. میانگین ارتفاع اشعه های چوبی 577 میکرون و ترکیب سلولها در آنها مخلوطی از ردیفهای ایستاده و خوابیده می باشد تعداد اشعه چوبی بطور متوسط 7 عدد در میلیمتر اندازه گیری شد. میانگین طول الیاف اندازه گیری شده در سه ناحیه یقه،50% و 75% طول ساقه840 میکرون و میانگین قطر الیاف 23.9میکرون و همچنین میانگین قطر حفره سلولی 16.11 و میانگین ضخامت دیواره در الیاف چوب ساقه پنبه ورامین 3.9میکرون اندازه گیری شد. چوب پنبه ورامین دارای جرم حجمی خشک 0.44 گرم بر سانتیمتر مکعب و جرم حجمی بحرانی 0.40 گرم بر سانتیمتر مکعب می باشد و میزان هم کشیدگی حجمی آن 7.7 درصد و واکشیدگی حجمی آن 8.3 درصد اندازه گیری شد. همچنین درصد تخلخل آن نیز 70.5 درصد برآورد شد. میزان درصد مواد شیمیایی تشکیل دهنده چوب پنبه ورامین نیز آزمایش شد که سلولز 52 درصد، لیگنین 29.9 درصد، خاکستر 1.4 درصد و مواد استخراجی 6.8 درصد را نشان داد. }, keywords_fa = {پنبه رقم ورامین,آناتومی چوب,فیزیک چوب,شیمی چوب,الیاف,سلولز,لیگنین}, url = {https://ijwpr.areeo.ac.ir/article_117547.html}, eprint = {https://ijwpr.areeo.ac.ir/article_117547_c77c6013f599080e54938692df6e74b0.pdf} }