موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091332420171222The Potential of Utilization of Cotton Stalk Residues In Particleboard Productionپتانسیل استفاده از پسماندهای ساقه پنبه در تولید تخته خرده چوب46247210706510.22092/ijwpr.2016.107065FAابوالفضل کارگرفرددانشیار، بخش تحقیقات علوم چوب و فراوردههای آن، مؤسسه تحقیقات جنگلها و مراتع کشور، سازمان تحقیقات، آموزش و ترویج کشاورزی، تهران، ایرانJournal Article20160702The potential of cotton stalks residues for the production of particleboard was investigated. Three resin dosage gradients (10% core:10% surface; 9%core:11% surface and 8% core:12% surface) and three press times (3, 4 and 5 minutes) were selected as the variables were produced. Then the mechanical and physical properties of the boards were measured and statistically analyzed. The results of modulus of rupture (MOR), modulus of elasticity (MOE) and internal bonding (IB) measurements showed that as the resin dosage gradient increases, these properties increased and the effect of this variable on these properties was statistically significant. The highest values were reached when either 2 or 4% resin dosage gradients were applied. The effect of resin dosage gradient on thickness swelling after 2 and 24 hours immersion in water was also statistically significant and these properties were improved. The effect of press time on thickness swelling was also statistically significant and the lowest thickness swelling was observed at 5 minutes press time. The results indicated that if 2 or 4% resin dosage gradients and either 4 or 5 minutes press time is applied for the manufacturing of particleboards using cotton stalks residues, the specification of the boards meet the EN specification.هدف از این تحقیق، بررسی پتانسیل استفاده از پسماندهای ساقه پنبه در تولید تخته خرده چوب بوده است. لذا با استفاده از 3 گرادیان مصرف چسب صفر، 2 و 4 درصد بین لایه سطحی و میانی کیک خرده چوب و 3 زمان پرس 3؛ 4 و 5 دقیقه اقدام به ساخت تخته خرده چوب گردید و خواص فیزیکی و مکانیکی آنها اندازه گیری و مورد تجزیه و تحلیل قرار گرفت. نتایج نشان داد که افزایش گرادیان مصرف چسب در سطح معنی داری باعث بهبود مقاومت خمشی، مدول الاستیسیته و چسبندگی داخلی شده است و تخته های ساخته شده با گرادیان مصرف چسب 2 و 4 درصد دارای مقاومت خمشی، مدول الاستیسیته و چسبندگی داخلی بالاتری هستند. همچنین افزایش گرادیان مصرف چسب باعث بهبود واکشیدگی ضخامت 2 و 24 ساعت تخته ها شد و علاوه بر این، زمان پرس نیز اثر معنی داری بر این ویژگی تخته ها داشت و حداقل واکشیدگی ضخامت 2 و 24 ساعت در شرایط استفاده از زمان پرس 5 دقیقه مشاهده گردید. نتایج این تحقیق نشان داد که در صورت استفاده از گرادیان مصرف چسب در حد 2 الی 4 درصد بین لایه سطحی و میانی کیک خرده چوب و زمان پرس 4 و 5 دقیقه، می توان از ساقه پنبه به عنوان یک ماده لیگنوسلولزی مناسب برای تولید تخته خرده چوب با ویژگیهای مکانیکی بالاتر از استاندارد EN اروپا استفاده نمود.https://ijwpr.areeo.ac.ir/article_107065_de161b5ce37f8223c924dc1fe558002e.pdfموسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091332420171222Investigation and Comparison of Bagasse Soda Pulps Properties Bleached with Total Chlorine Free (TCF) and Elemental Chlorine Free (ECF) Stagesبررسی و مقایسه ویژگیهای خمیرکاغذ سودای باگاس رنگبری شده با توالی های کاملا بدون کلر(TCF) و بدون کلر(ECF47348511238010.22092/ijwpr.2017.108836.1377FAرامین ویسیدانشیار، دانشگاه آزاد اسلامی واحد چالوس، ایرانعلیرضا باقریفارغ التحصیل دانشگاه آزاد اسلامی چالوس، ایرانJournal Article20161223The objective of this research was accomplished on the effects of total chlorine free (TCF) and elemental chlorine free (ECF) bleaching on optical and mechanical properties of bagasse soda pulps. For this purpose, some unbleached bagasse soda pulps were randomly selected from Ahvaz Pars industry. Then these pulps were bleached with one, two and three P, OP, OPY, O(Ep)P, EHP and O(Ep)H bleaching stages by using oxygen(O) hydrogen peroxide(P), alkali extraction with hydrogen peroxide(Ep), sodium hypochlorite(H) and sodium dithionite(Y). The hand sheets with 70 gr/m2 were prepared from above-mentioned of pulps, and then the optical and mechanical properties were measured and compared according by using TAPPI standard test methods. The results showed that brightness, greenness, tear (except EHP stages), tensile, burst, breaking length strengths and folds were increased and opacity and a* factor were decreased by ECF and TCF bleaching stages. The effects of TCF bleaching stages were more sensible than ECF bleaching stages in improve of bagasse soda properties, too. In general, role of three OPY and O(Ep)H stages and two OP bleaching stages were better than EH(control) stage and unbleached bagasse soda pulps mill in improve of brightness and its paper strengths, too.این تحقیق با هدف بررسی و مقایسه اثرات رنگبری کاملا بدون کلر(TCF) و بدون کلر(ECF) بر ویژگیهای نوری و مقاومتی کاغذ حاصل از خمیرکاغذ سودای باگاس انجام شد. به همین منظور مقداری خمیرکاغذ رنگبری نشده سودای باگاس به صورت تصادفی از کارخانه پارس اهواز انتخاب شد. سپس این خمیرکاغذ ها با توالی های یک، دو و سه مرحله ای P، OP ، OPY ، P(PE)O، EHP و H(PE)O با استفاده از اکسیژن(O)، پروکسید هیدروژن(P)، استخراج قلیایی با پروکسید هیدروژن(PE)، هیپوکلریت سدیم(H) و دی تیونیت سدیم (Y) رنگبری گردید. از خمیرکاغذ های مذکور کاغذهای دست ساز با وزن پایه gr/m2 70 تهیه و خواص نوری و مقاومتی آن ها طبق آزمون های استاندارد TAPPI اندازه گیری و مقایسه گردید. نتایج نشان داد که در اثر رنگبری کاملا بدون کلر(TCF) و بدون کلر(ECF) روشنی، سبز رنگی، مقاومت های به پارگی(بجز توالیEHP )، کششی، ترکیدن، طول پارگی و تاه شدن افزایش و ماتی و فاکتورa* کاغذ های حاصل کاهش را نشان می دهد. همچنین تاثیرتوالی های TCF در بهبود ویژگیهای خمیرکاغذ های رنگبری شده باگاس محسوس تر از توالی های ECFمی باشد. به طور کلی، نقش توالیهای رنگبری سه مرحله ایOPY و O(Ep)H و همچنین توالی رنگبری دو مرحله ای OP در سفید سازی و بهبود روشنی و مقاومت های کاغذ حاصل موثر تر از توالی دو مرحله ای EH (شاهد) و خمیرکاغذ رنگبری نشده سودای باگاس کارخانه بوده است.https://ijwpr.areeo.ac.ir/article_112380_d2073ae23941474b125798d8d01a0b81.pdfموسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091332420171222Numerical and experimental establishment of kiln drying schedule for Iranain beech based on diffusion theoryتدوین عددی و تجربی برنامه خشککردن چوب راش در کوره بر پایهی تئوری انتشار48649711309310.22092/ijwpr.2017.110385.1403FAمحراب مدهوشیدانشیار، گروه تکنولوژی و مهندسی چوب، دانشگاه علوم کشاورزی و منابع طبیعی گرگان، ایران0000-0001-6845-2749ملیحه علیزادهدانشجوی سابق کارشناسی ارشد، گروه تکنولوژی و مهندسی چوب، دانشگاه علوم کشاورزی و منابع طبیعی گرگانJournal Article20170425In order to establish a kiln drying schedule for Iranian Beech (Fagus orientalis) lumbers of 5.5 cm thickness, commercially cut from Shast Kola region , 5 km distance from Gorgan. They were then dried under the program based on diffusion theory (from Malmquist's relations) were adopted to dry the lumbers to the final moisture content of 12±2 %. This program for three separate kiln charges and initial moisture content 66.6, 58 and 45 percent was developed. Initial drying bulb temperature (first step) 46 °C and wet-bulb temperature 45 °C was calculated and in three schedules were same. The severity of surface, end checks and warp (bowing, crooking, twisting) in the lumbers were measured before and after the drying process and quality control methods were used to analyze the wood defects. Results indicated that drying of beech lumber using this new schedule was satisfactory. Also intensity changes of defect in all three repeats were about acceptable quality and quantity. Superior characteristics of this program was no surface checks in samples because the moisture content was reduced slowly.برنامههایی که تاکنون برای خشککردن انواع گونههای چوبی بومی ایران در داخل کشور تدوین شدهاند برگرفته از کد برنامههای آزمایشگاه فراورده های جنگلی آمریکا (FPL) بوده است که در نوع خود مشکلاتی را به همراه دارند. از اینرو، هدف از انجام این تحقیق تدوین برنامهای مناسب برای خشککردن چوب راش برای اولین بار و متفاوت با برنامههای قبل است که در نوع خود مزیتهایی را نیز میتواند داشته باشد. چوب راش ایران (Fagus orientalis) با برش تجاری و با ضخامت 5/5 سانتیمتر با برنامهای بر پایهی تئوری انتشار تا رسیدن به رطوبت نهایی 2±12 درصد خشک گردید. این برنامه در 3 مرحله جداگانه و با رطوبتهای اولیه 6/66، 58 و 45 درصد بر روی سه بار متفاوت کوره اجرا گردید. دمای خشک اولیه (اولین گام) محاسبه شده در هر سه مرحله یکسان و برابر 46 درجه سلسیوس و دمای تر در طول اجرای برنامه یکسان و برابر 45 درجه سلسیوس منظور گردید. شدت معایب کمانی، انحنا، تاب، ترک سطحی و ترک انتهایی در طول اجرای برنامه، قبل و بعد از خشک شدن در هر مرحله اندازهگیری و تجزیه و تحلیل آماری با استفاده از نمودارهای کنترل کیفیت انجام گردید. برنامهی جدید که با استفاده از روابط ریاضی و بر پایه تئوری انتشار تدوین شد در هر سه بار کوره، نتایج قابل قبولی به همراه داشت، به طوری که شدت تغییرات معایب در هر سه بار کوره در نمودارهای تحلیل آماری در حدود قابل قبول کمی و کیفی قرار گرفتند. در نهایت، عدم ایجاد ترک سطحی در نمونهها به دلیل اعمال شرایط ملایم کاهش رطوبت، به عنوان ویژگی برتر این برنامه جدید تدوین شده مطرح گردید.https://ijwpr.areeo.ac.ir/article_113093_5b4e7e9e9aec3e48a1511ce843e218f1.pdfموسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091332420171222Biorefinery of Black Liquor from Bagasse Soda Pulping as Surface Coating on Recycled Based Paperپالایش زیستی مایع سیاه خمیرکاغذسازی سودای باگاس به عنوان اندود سطحی کاغذ با پایه بازیافتی49850811341810.22092/ijwpr.2017.114917.1434FAحسین جلالی ترشیزیاستادیار، مهندسی پالایش زیستی، دانشگاه شهید بهشتی، ایران،0000-0003-1035-9474راحیل چالاکهدانشجوی کارشناسی ارشد، مهندسی پالایش زیستی، دانشگاه شهید بهشتی، ایرانJournal Article20170731Recently, Biorefinery is highly focused as a predominant developer in Forest product industry. Pulping black liquor as a rich residual in biopolymers from plant biomasses, has a great potential in bioenergy and biomaterials. In this study, the effects of surface coating of black liquor from bagasse soda pulping (BLBSP) in raw and filtrated form (as 2.5 g. O.D) with different concentration (30, 37, 44 & repeated 44%) on recycled based paper and its properties were investigated. Totally, the BLBSP filtration improved the paper properties more than the raw type, due to its impurity and coarse materials extraction. Higher concentration and content of the applied coatings enhanced grammage (up to 44%) and reduced water absorption (to <30%), constantly, because of mostly hydrophobic material (lignin and minerals) accumulation which would increase the paper mass and would fill the porous structure, resulted in reduction in water adsorption capacity of the lignocellulosic network. But the optimum treatment respect to the tensile, burst and tear strengths was the lowest applied concentration, which are attributed to the easier BLBSP penetration into the paper structure and its contribution in bonding. Recycled paper usage in packaging purposes require compression and bending strengths that increased by the liquor concentrating as bending stiffness (up to >200%) and compressive crush resistance (up to >150%). In this regard, film formation, thickening the paper and also the effective role of lignin could be noted beside the bonding enhancement. Repeatedly application of the BLBSP no significantly improved the almost properties, but also decreased them.اخیراً پالایش زیستی بهعنوان توسعهدهنده برجسته صنایع فراوردههای جنگلی، مورد پیگیری جدی قراردارد. مایع سیاه فرایندهای خمیرکاغذسازی بهعنوان پسماندی سرشار از بیوپلیمرهای تولیدی در زیستتودههای گیاهی، از پتانسیل بالائی برای تولید بیومواد و بیوانرژی برخوردارست. در این پژوهش، تاثیر اندودسازی سطحی مایع سیاه خمیرکاغذسازی سودای باگاس (5/2 گرم خشک) در دو حالت خام و تصفیهشده با غلظتهای مختلف (30، 37، 44 و دوباره %44) بر کاغذ پایه بازیافتی و ویژگیهای آن بررسی گردید. بطورکلی، فیلترکردن مایع مزبور بواسطه حذف مواد ناخالص و درشت موجب برتری ویژگیها نسبت به حالت فیلرنشده گردید. افزایش غلظت و میزان اندود اعمالی، افزایش گرماژ (تا 44%) و کاهش جذب آب (به کمتر از %30) را پیوسته بههمراه داشت، چراکه انباشت مواد عمدتاً غیرآبدوست (لیگنین و مواد معدنی) علاوه بر افزایش جرم و پرکردن منافذ ساختار کاغذ؛ کاهش قابلیت جذب آب بستر لیگنوسلولزی را بههمراه دارد. لیکن تیمار بهینه از منظر مقاومتهای کشش، ترکیدن و پارگی در پاینترین غلظت اندود بدستآمد که نفوذ سهلتر لیکور رقیق بهدرون ساختار کاغذ و نیز مشارکت در پیوندیابی را میتوان استدلال نمود. کاربرد کاغذهای بازیافتی در بستهبندی، مقاومتهای فشاری و خمشی کاغذ را طلب نموده که افزایش غلظت لیکور اندودساز، مقاومتهای سفتی خمشی (تا بیش از 200 درصد) و فشاری لهیدگی (تا بیش از 150 درصد) را افزایش داد. علاوه بر تقویت پیوندیابی، تشکیل فیلم، افزایش ضخامت کاغذ و نیز سهم بهسزای لیگنین در این راستا قابل ذکرست. اعمال دوبار لیکورهای پخت نهتنها بهبود چشمگیری را در غالب ویژگیها بوجود نیاورد، بلکه منجر به کاهش نیز گردید.https://ijwpr.areeo.ac.ir/article_113418_940de583cd11024de3176ea4a0d28053.pdfموسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091332420171222The effects of natural weathering on different properties of paper made in Pars factoryبررسی اثر هوازدگی طبیعی باگاس بر ویژگی های مختلف محصول نهایی در کارخانه کاغذ پارس50951711341910.22092/ijwpr.2017.109270.1386FAمیثم خلیلیان شلمزاریدانشجوی کارشناسی ارشد، گروه صنایع چوب و فراوردههای سلولزی، دانشگاه صنعتی خاتمالانبیا، بهبهانمحمد علی سعادت نیااستادیار، گروه صنایع چوب و فراوردههای سلولزی، دانشگاه صنعتی خاتمالانبیا، بهبهان، ایرانحمید رضا پیرایشاستادیار، گروه صنایع چوب و فراوردههای سلولزی، دانشگاه صنعتی خاتمالانبیا، بهبهان، ایرانJournal Article20170122The aim of this study was to investigate the effects of natural weathering induced by critical climate conditions on quality of sugarcane bagasse lignocellulosic material in Pars factory. The experimental samples selected from fresh and also stored bagasse for durations of 6 months, 1, 2 and 5 years, were used. The mechanical and the chemical properties as well the color variations were measured on taken samples. The results showed that the long storage durations of bagasse significantly decreased the quality of row materials observed in hand sheet tensile and fold strengths. The results illustrated that the amount of Lignin and extractives increased (44 % in lignin and 32% in extractives amount respectively) and also decrease in amount of cellulose and hemicellulose was found (10% for cellulose and 43% for hemicellulose) during 5 years storage in yard. According to the results, there was an obvious difference in L and a color index of 5 years old bagasse in comparing with those of fresh bagasse. Finally it can be drawn that the use of discorded and weathered bagasse could cause the loss in the final products quality which means more chemical treatment for bleaching and more using long fiber in paper making process.این تحقیق به بررسی تاثیر کهنگی طبیعی حاصل از شرایط بد آب و هوایی جنوب ایران بر کیفیت ماده لیگنوسلولزی باگاس در کارخانه کاغذسازی پارس پرداخته است. لذا نمونه هایی از سطح توده باگاس انبار شده در یارد کارخانه کاغذ پارس طی دوره های زمانی تازه، 6 ماهه، 1 ساله، 2 ساله و 5 ساله تهیه و برای ارزیابی تغییرات مربوط به رنگ، ترکیبات شیمیایی و مقاومت مکانیکی مورد استفاده قرار گرفت. نتایج نشان داد که رهاسازی باگاس در محوطه باز کارخانه برای یک دوره طولانی به طور معنی داری باعث افت کیفیت ماده اولیه شده به طوریکه طی 5 سال باعث کاهش شدید مقاومت کششی و تاخوردگی محصول نهایی شده است. این افت کیفیت در بازه زمانی مورد مطالعه همراه با افزایش 44 درصدی لیگنین و 32 درصدی ماده استخراجی بود. همچنین تاثیر نور خورشید و تر و خشک شدن ماده مذکور طی دوره مذکور به ترتیب باعث افت 10 و 43 درصدی میزان سلولز و همی سلولز شده است. بعلاوه نتایج رنگ سنجی نشان داد که در مقایسه با باگاس تازه، باگاس 5 ساله بشدت تیره تر شده به طوریکه شاخص روشنایی و میزان قرمزی آن افزایش داشته است. بنابراین استفاده از یک ماده کهنه و هوازده منجر به افزایش استفاده از مواد شیمیایی در مرحله رنگبری و خمیر الیاف بلند جهت جبران افت کیفیت محصول نهایی خواهد شد.https://ijwpr.areeo.ac.ir/article_113419_336ad29c94b049d5b6864c7acd1562c2.pdfموسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091332420171222The Effect of Chemical Pre-treatment of Industrial Waste of Licorice Root on its Pulp Structural Properties in Bio- Refinery Conceptاثر پیش تیمارشیمیایی پسماند صنعتی ریشه شیرین بیان بر ویژگی های ساختاری خمیر آن از منظر پالایش زیستی51852911357110.22092/ijwpr.2017.110712.1419FAزهرا تک زارعدانش آموخته کارشناسی ارشد صنایع خمیر و کاغذ، گروه مهندسی پالایش زیستی، دانشگاه شهید بهشتیحسین کرمانیاندانشیار گروه مهندسی پالایش زیستی، دانشگاه شهید بهشتیامید رمضانیاستادیار گروه مهندسی پالایش زیستی، دانشگاه شهید بهشتی0000-0003-0909-0578اسماعیل رسولی گرمارودیاستادیار گروه مهندسی پالایش زیستی، دانشگاه شهید بهشتی0000-0002-9503-0848علی عبدالخانیدانشیار گروه علوم و صنایع چوب و کاغذ، دانشگاه تهرانJournal Article20170522In this study, the liquorice root (Glycyrrhiza glabra) has been extracted in the Liquorice factory of Kerman, supplied as raw material. The above mentioned waste, after pre-hydrolyzed with sulfuric acid 2% at 130 °C in 60 minutes, is cooked at temperatures of 170 ̊C, the chemicals charge of 20%, and in four times 15, 30, 60 and 90 minutes and rate of liquor to waste 7:1 in Soda process. Obtained Soda pulps were evaluated in yield, lignin percentage, water retention value (WRV), viscosity and crystallinity. Results showed that by prolonging of cooking time, pulp yield and lignin percentage were decreased and WRV increased. Also, pulp viscosity in 30, 45 min was increased by increasing in cooking time that according to other results, it seems that it is false viscosity. In addition, accordance with characterizing of samples by XRD, by progressive cooking time from 15 to 45 min, sample crystallinity decreased and in 60 min its value is increased. According to the pulps viscosity and downward trend of lignin removal with progressive cooking time, this addition can be due to crystallization of hemicellulose like xylan on the crystalline zone of cellulose chain. Therefore, according to the results and based on Bio-refinery concept, cooking time 30 min suggested as the best option for production of high value-added products in saccharification process.در این تحقیق، ابتدا ریشه شیرینبیان (Glycyrrhiza glabra) که در کارخانه لیکوریس کرمان عصارهگیری شده بود، بهصورت تفاله صنعتی به عنوان ماد اولیه تهیه گردید. پس از پیشهیدرولیز، تفاله مذکور با اسید سولفوریک 2% بر اساس وزن خشک نمونه در دمای C̊ 130 و در زمان 60 دقیقه، عملیات پخت سودا در دمای C̊ 170، غلظت مواد شیمیایی 20%، و در چهار زمان 15، 30، 45 و 60 دقیقه و نسبت مایع پخت به تفاله 7 به 1 صورت پذیرفت. خمیرهای سودای تولیدشده از نظر میزان بازده، وازد الک، درصد لیگنین، ماندگاری آب، ویسکوزیته و درجه کریستالیته مورد ارزیابی قرار گرفتند. نتایج نشان داد که با افزایش زمان پخت بازده خمیر و درصد لیگنین کاهش و ماندگاری آب افزایش مییابد. همچنین، ویسکوزیته با افزایش زمان پخت در 30 و 45 دقیقه افزایش مییابد که بر اساس بررسیها و تطبیق با سایر دادهها به نظر میرسد افزایش ویسکوزیته کاذب باشد. به علاوه، نتایج بررسی نمونههای پیشتیمار شده با پراش پرتو ایکس نشان میدهد که با افزایش زمان پخت از 15 دقیقه تا 45 دقیقه پخت سودا، درجه کریستالیته نمونهها کاهش و در 60 دقیقه افزایش مییابد که تطبیق دادههای ویسکوزیته و روند نزولی حذف لیگنین با افزایش زمان پخت نشان میدهد که افزایش کریستالیته ناشی از جذب مجدد همیسلولزهایی نظیر زایلان در بخش کریستالی سلولز باشد. بنابراین، با توجه به نتایج بدست آمده و بر اساس دیدگاه پالایش زیستی میتوان زمان پخت 30 دقیقه را به عنوان بهترین گزینه برای تولید محصولات با ارزش افزوده بالاتر در فرایند قندسازی پیشنهاد نمود.https://ijwpr.areeo.ac.ir/article_113571_f89629e4f8f019e3cafa9743629a7b8e.pdfموسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091332420171222Hydrophobization of Paper Using Organosilane and Titanium Dioxide Nanoparticles with Layer by Layer Methodآب گریز کردن کاغذ با استفاده از ترکیبات ارگانوسیلان و نانوذرات دی اکسید تیتانیوم با روش لایه به لایه53054011342110.22092/ijwpr.2017.114822.1433FAباقر اشرفی رادکارشناس ارشد، گروه علوم و صنایع چوب و کاغذ، دانشکده منابع طبیعی، دانشگاه تهران، کرج، ایرانمحمد آزادفلاحاستادیار، گروه علوم و صنایع چوب و کاغذ، دانشکده منابع طبیعی، دانشگاه تهران، کرج، ایرانفاطمه کلائی موخرکارشناس ارشد، گروه علوم و صنایع چوب و کاغذ، دانشکده منابع طبیعی، دانشگاه تهران، کرج، ایرانسهیلا ایزدیاراستادیار، گروه علوم و صنایع چوب و کاغذ، دانشکده منابع طبیعی، دانشگاه تهران، کرج، ایرانمهدی رحمانی نیااستادیار، گروه علوم و صنایع چوب و کاغذ، دانشکده منابع طبیعی و علوم دریایی، دانشگاه تربیت مدرس، نور، ایران0000-0001-6943-0146Journal Article20170723Utilization of paper as packaging material and developing applied technological program on paper-based substrate are drastically dependent to control of cellulosic fiber hydrophilicity and to enhancement of its hydrophobic properties. Then this work carried out with the aim of developing hydrophobic surface on cellulosic fiber with layer by layer (LBL) method while keeping and enhancing the properties of paper network. The deposition was implemented by titanium dioxide nanoparticles and poly acrylic acid as cationic and anionic layer respectively on the fibers of unbleached hardwood Kraft pulp and using Zycosil and fluoroalkyl silane on the last layer. The hand-sheets were then made by this modified fiber. The contact angle and roughness were measured to evaluate the effect of layers on hydrophobicity. The results indicated that roughness increased with the number of layers. The instant contact angle was also increased with the number of layers and reached approximately to 110 degree at 7th layer. The dynamic contact angles dropped more lately with increasing the number of layers. The fluorosilane deposition as 8th layer in comparison with Zycosil showed more effect on surface energy reduction. The instant contact angle of Zycosil treated paper was measured 125 degree which dropped significantly to 48 degree after 30 seconds. However, fluorosilane modified paper exhibited contact angle of 140 degree at the same time. In addition, the presence of titanium dioxide nanoparticles on the surface of fiber was demonstrated by scanning electron microscopy (SEM) of paper surface.استفاده از کاغذ بهعنوان ماده بستهبندی و توسعه برنامههای کاربردی تکنولوژیکی برروی بسترهای کاغذی تا حد زیادی به کنترل خواص آبدوستی الیاف سلولزی و بهبود خواص دفع آب آن بستگی دارد. لذا تحقیق حاضر با هدف توسعه سطوح آبگریز در الیاف سلولزی با روش لایه به لایه و با حفظ و بهبود همزمان خواصفیزیکی شبکه کاغذ انجام شد. لایهنشانی توسط نانوذرات دیاکسیدتیتانیوم و پلیآکریلیکاسید به ترتیب به عنوان لایه کاتیونی و آنیونی به تعداد 3،5 و 7 لایه و با استفاده از زایکوسیل و فلوئوروآلکیلسیلان در آخرین لایه روی الیاف خمیرکاغذ رنگبرینشده کرافت پهن-برگان انجام شد. سپس با استفاده از این الیاف سلولزی اصلاحشده کاغذهای دستساز ساخته شد. ویژگیهای زبری و زاویه تماس به منظور ارزیابی اثرات آبگریزی لایهها اندازهگیری شدند. نتایج نشان داد که میزان زبری با افزایش تعداد لایهها افزایش یافته است. زاویه تماس آنی نیز با افزایش تعداد لایههای جذبشده افزایش یافته است و در لایه هفتم به مقدار تقریبی 110 درجه رسیده است. همچنین با افزایش لایهها، زاویه تماس دینامیکی نیز با تاخیر بیشتر دچار افت شد. استفاده از فلوئوروسیلان به عنوان لایه هشتم در مقایسه با نانو زایکوسیل تاثیر بیشتری در کاهش انرژی سطحی نشان داد. زاویهتماس آنی کاغذ تیمار شده با نانو زایکوسیل حدود 125 درجه اندازهگیری شد که بعد از گذشت تنها 30 ثانیه این مقدار با یک افت چشمگیر به 48 درجه رسید. با این وجود کاغذ اصلاح شده با فلوئوروسیلان در همین مدتزمان زاویه-تماس 140 درجه را نشان داد. علاوه بر این، تصاویر میکروسکوپ الکترونی (SEM)تهیهشده از سطح کاغذ وجود نانوذرات دیاکسیدتیتانیوم را در سطح الیاف ثابت کرد.https://ijwpr.areeo.ac.ir/article_113421_33e84a7c80c6c4b0655524ee5a8c147e.pdfموسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091332420171222The effect of moisture content and storage time of Bagasse on particleboard physical and mechanical propertiesتأثیر مقدار رطوبت و زمان انبارداری باگاس بر خواص فیزیکی و مکانیکی تخته خرده چوب54155211342210.22092/ijwpr.2017.110679.1416FAمسعود رضا حبیبیاستادیار پژوهشی، بخش تحقیقات علوم چوب و فراورده های آن، مؤسسه تحقیقات جنگل ها و مراتع کشور، سازمان تحقیقات، آموزش و ترویج کشاورزی، تهران، ایراناحمد جهان لتیباریاستاد علوم و صنایع چوب و کاغذ، دانشگاه آزاد اسلامی واحد کرجسعید مهدویدانشیار، بخش تحقیقات علوم چوب و فراورده های آن، مؤسسه تحقیقات جنگل ها و مراتع کشور، سازمان تحقیقات، آموزش و ترویج کشاورزی، تهران، ایران0000-0003-4077-8063Journal Article20170519This study was carried out to investigate the effect of storage time and moisture content of bagasse on the physical and mechanical properties of particleboard. For this purpose, wet depitting bagasse was used and samples were maintained in bailing storage method. In this study, was applied 4 storage times (1.5, 3, 4.5 and 6 months) and 2 moisture content of Bagasse (45% and 55%). According to these variables, particleboards were made. Also chemical properties (pH, acid and alkaline buffering capacity) of Bagasse were determined. The mechanical and physical properties of the boards were measured and statistically analyzed using factorial experiment and complete randomized design. Then Duncan multiple range test was used for grouping of the averages. The results revealed that with decreasing of Bagasse moisture content, Bagasse sample pH and acid buffering capacity were decreased and increased, respectively. Also bending properties and thickness swelling after 24 hours immersion of the boards were improved. With increasing of storage time, the chemical properties of Bagasse tend to be alkaline, and the minimum of board internal bond strength was obtained in 1.5 month storage time. The physical properties of boards were improved with increasing of storage timeدر این تحقیق، تاثیر مقدار رطوبت و زمان انبارداری باگاس بر ویژگیهای فیزیکی و مکانیکی تخته ساخته شده از آن بررسی شده است. ابتدا برای این منظور از باگاس مغز زدایی شده به روش مرطوب و روش انبارداری از نوع عدل بندی استفاده شد. از 4 زمان انبارداری 5/1، 3، 5/4 و 6 ماه و دو مقدار رطوبت باگاس 45 و 55 درصد استفاده شد. با توجه به این متغیرها، نسبت به ساخت تختهخردهچوب اقدام گردید. همچنین ویژگیهای شیمیایی باگاس (pH، ظرفیت بافرکنندگی اسیدی و قلیایی) تعیین شدند. نتایج اندازهگیری ویژگیهای فیزیکی و مکانیکی تختههای ساخته شده با استفاده از آزمایش فاکتوریل در قالب طرح کاملا تصادفی تجزیه و تحلیل آماری شد و میانگینها با استفاده از آزمون دانکن گروهبندی شدند. نتایج نشان داد که با کاهش مقدار رطوبت باگاس، pH و ظرفیت بافرکنندگی اسیدی باگاس به ترتیب کاهش و افزایش یافته، و مقاومت خمشی، مدول الاستیسیته و مقدار واکشیدگی ضخامت پس از 24 ساعت غوطهوری در آب تختهها بهبود یافته است. با افزایش زمان انبارداری، ویژگیهای شیمیایی باگاس تمایل به قلیایی شدن داشتند و حداقل مقاومت چسبندگی داخلی تختهها در زمان انبارداری 5/1 ماه ملاحظه شد. با افزایش زمان انبارداری نیز خواص فیزیکی تختهها بهبود یافت.https://ijwpr.areeo.ac.ir/article_113422_add47c19cd6062e7867071b9a1eba0c5.pdfموسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091332420171222The effect of recycling process on the chemical properties and wettability of obtained fibers from MDF wastesتأثیر فرایند بازیافت بر ویژگی های شیمیایی و خاصیت تر شوندگی الیاف حاصل از پسماند تخته فیبر با دانسیته متوسط55356411355310.22092/ijwpr.2017.109697.1393FAمحمد احمدیاستادیار، گروه مهندسی منابع طبیعی، دانشکده کشاورزی و منابع طبیعی، دانشگاه محقق اردبیلی، اردبیل، ایرانبیتا معزی پوردانشآموخته دکتری، گروه علوم و صنایع چوب و کاغذ، دانشکده منابع طبیعی، دانشگاه تهران، ایرانمعراج شرریاستادیار- دانشکده کشاورزی و منابع طبیعی- دانشگاه محقق اردبیلیJournal Article20170220In this study properties of fibers recycled from MDF wastes as one of the potential important resources as raw materials for MDF production were investigated.<br /> For this purpose, two different methods including ohmic heating (for 2 and 4 min) and hydrothermal method (at 105˚c for 150 min) were utilized for recycling the wastes of MDF and original fibers were studied as control sample. <br /> The chemical composition of fibers (lignin, cellulose and hemicellulose content), as effective variable on quality of fibers was measured. Also for probing the chemical characteristic of fiber surface, FT-IR test was utilized. In addition, the wettability of fibers also was determined by measuring the contact angels between fibers surface and water drop. <br /> The results showed that the chemical composition of fibers is changed within recycling process. Most changes were occurred in hemicellulose and extractives content. The results of FT-IR test revealed the existence of more carbonyl groups and furfural and lower amount of hydroxyl groups in recycled fibers compared to original fibers which caused by esterification process. The wettability of fibers was decreased after recycling process especially in hydrothermal method.در این تحقیق ویژگی های الیاف بازیافت شده از پسماند ام دی اف که یکی ازمنابع بالقوه ی مهم قابل استفاده به عنوان ماده ی اولیه ی در ساخت ام دی اف می باشند، مورد بررسی قرار گرفت. به این منظور از دو روش حرارت دهی اهمیک (در دو زمان 2 و 4 دقیقه) و هیدروترمال (در دمای105 درجه سانتی گراد به مدت 150 دقیقه ) برای بازیافت پسماند ام دی اف استفاده شد واز الیاف بکر به عنوان نمونه ی شاهد استفاده شد.<br /> ترکیب شیمیایی الیاف (مقدار لیگنین، سلولز و همی سلولز) به عنوان عوامل موثر بر کیفیت الیاف اندازه گیری شد. از الیاف بکر و بازیافتی طیف FT-IR گرفته شد تا تغییرات شیمیایی سطح پس از بازیافت مشخص شود. هم چنین به منظور تعیین خاصیت تر شوندگی الیاف تصاویری از وضعیت قطره ی آب بر سطح الیاف تهیه شد و زاویه ی تماس بین قطره ی آب و سطح الیاف اندازه گیری شد. نتایج نشان داد که ترکیب شیمیایی الیاف در اثر بازیافت دستخوش تغییر می شود، بیشترین تغییر در مقدار همی سلولز و مواد استخراجی رخ داد. هم چنین در الیاف بازیافتی به روش هیدروترمال، کاهش چشم گیر در مقدار لیگنین مشاهده شد. نتایج FT-IR بیانگر وجود گروه های کربونیل بیشتر و هیدروکسی کمتر در الیاف بازیافتی نسبت به الیاف بکر بود که نشان دهنده ی فرایند استری شدن در الیاف بازیافتی می باشد. بررسی زاویه تماس قطره ی آب روی سطح الیاف نشان داد که ترشوندگی الیاف پس از بازیافت مخصوصاً در روش هیدروترمال کاهش یافته است.https://ijwpr.areeo.ac.ir/article_113553_c8df0216e887ca0636d95fd70ee15f96.pdfموسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091332420171222Simulation of condensing unit of liquor in Mazandaran wood and paper industryشبیه سازی واحد تغلیظ لیکور در کارخانه چوب و کاغذ مازندران56557511342310.22092/ijwpr.2017.109327.1387FAسهیل پورمحمودیدانشجوی کارشناسی گروه مهندسی شیمی، دانشکده فنی و مهندسی، دانشگاه مازندران، بابلسر، مازندران، ایرانایمان ترابی وسطی کلائیدانشجوی کارشناسی گروه مهندسی شیمی، دانشکده فنی و مهندسی، دانشگاه مازندران، بابلسر، مازندران، ایرانالهام امیدبخش امیریاستادیار، گروه مهندسی شیمی، دانشکده فنی و مهندسی، دانشگاه مازندران، بابلسر، مازندران، ایرانJournal Article20170127Mazandaran wood and paper industry is known as the largest manufacturer of paper in the Middle East. Black liquor is liquid product of pulp cooking chemical process, which is much polluted because of some organic and inorganic compounds. So, chemical and energy recovery of black liquor are one of the interesting studies. There are different ways for this one among them concentration method of liquor is used in Mazandaran wood and paper industry. In this work, Condensing unit of liquor was simulated by Hysys software. Then, simulation results were compared with factory data and acceptable results were obtained. In the next step, the effect of operating conditions of the two main feed streams was studied. The results showed that with increasing of dilute liquor temperature, concentration of output liquor flow increases as per 40°C increasing of temperature, almost 28 percent of the condensed value increases. Also, by 10 kPa increasing of the dilute liquor pressure, approximately 39% of condensed value decreases. By increasing the pressure and flow rate of steam, concentration of output liquor somewhat increases, while, this increasing for flow rate, is initially steep and then less steep. The effect of steam temperature on the concentration of output liquor at different pressures must be checked individually.کارخانه چوب و کاغذ مازندران به عنوان بزرگترین کارخانه تولید کاغذ در خاورمیانه شناخته می شود. لیکور سیاه، محصول مایع حاصل از فرآیند شیمیایی پخت خمیر کاغذ میباشد که به علت وجود برخی ترکیبات آلی و معدنی به شدت آلودهکننده است و بازیابی مواد شیمیایی و انرژی موجود در لیکور سیاه یکی از بحث های مورد تحقیق پژوهشگران است. روش های متفاوتی موجود است که روش تغلیظ لیکور، روش مورد استفاده در کارخانه چوب و کاغذ مازندران است. در این کار، واحد تغلیظ لیکور توسط نرم افزار هایسیس شبیه سازی شده است و نتایج حاصل از شبیه سازی جریان لیکورنهائی با داده های کارخانه مقایسه شده است و نتایج قابل قبولی به دست آمده است. در مرحله بعد اثر شرایط عملیاتی دو جریان خوراک اصلی این واحد مورد بررسی قرار گرفته است. نتایج نشان داده است که با افزایش دمای جریان لیکور رقیق ورودی، درصد غلظت جریان لیکور خروجی افزایش می یابد. به طوریکه با افزایش دمای جریان لیکور رقیق ورودی به میزان 40 درجه سانتیگراد، تقریباً 28 درصد میزان تغلیظ افزایش می یابد. همچنین، با افزایش فشار جریان لیکور رقیق ورودی به میزان 10 کیلوپاسکال، تقریباً 39 درصد میزان تغلیظ کاهش می یابد. با افزایش میزان فشار و دبی جریان بخار، غلظت لیکور خروجی تا حدودی افزایش می یابد البته این افزایش در دبی، ابتدا با شیب تندی و سپس با شیب کمتری است. اثر دمای جریان بخار ورودی بر میزان تغلیظ جریان لیکور نهایی لیکور در فشارهای مختلف باید جداگانه بررسی شود.https://ijwpr.areeo.ac.ir/article_113423_a8e1d84a66ce749062c26eed306fd1dd.pdfموسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091332420171222Evaluation the physical and mechanical properties of the boards manufactured by mixture of wheat straw and tobacco stalkارزیابی ویژگی های فیزیکی و مکانیکی تخته ساخته شده از مخلوط کاه گندم و ساقه توتون57658411342010.22092/ijwpr.2017.110657.1413FAلعیا جمالی راداستادیار، گروه علوم و صنایع چوب و کاغذ، دانشکده کشاورزی و منابع طبیعی، دانشگاه گنبدکاووس، گنبد، ایرانفرشته کرکارشناس ارشد گروه علوم و صنایع چوب و کاغذ، دانشکده کشاورزی و منابع طبیعی، دانشگاه گنبدکاووس، گنبد، ایرانفرشید فرجیاستادیار، گروه علوم و صنایع چوب و کاغذ، دانشکده کشاورزی و منابع طبیعی، دانشگاه گنبدکاووس، گنبد، ایرانسحاب حجازیدانشیار، گروه علوم و صنایع چوب و کاغذ، دانشکده منابع طبیعی، دانشگاه تهران، کرج، ایرانJournal Article20170516In this research, the manufacture of particleboard using lignocellulosic residues including wheat straw and tobacco stalks mixed with industrial wood chips were studied. The variable factors included the mixture of wheat straw and tobacco stalks with industrial wood chips in four levels 0/100, 20/80, 40/60 and 60/40 (In any combination, according to the desired levels, tobacco stalks and wheat straw were used equally) and the amount of urea formaldehyde resin was at two levels 12 and 14% of the dry weight of the wood chips. The results showed that by increasing the mixture of wheat straw and tobacco stalk up to 60 percent, the physical and mechanical properties of the boards decreased significantly. But increasing the amount of adhesive consumption up to 14 percent had a positive impact on the physical and mechanical properties of the boards and improved internal bonding, bending strength and modulus of elasticity and dimensional stability of the boards. It means that by increasing the use of this type of wastes up to 40 percent with an increase in the amount of UF adhesive up to 14% can be produced the boards with the mechanical properties at standard level.در این بررسی امکان ساخت تخته خرده چوب با استفاده از پسماندهای لیگنوسلولزی شامل کاه گندم و ساقه توتون به همراه خرده چوب صنعتی مورد مطالعه قرار گرفت. عوامل متغییر شامل مقدار اختلاط کاه گندم و ساقه توتون با خرده چوب صنعتی در چهار سطح 100:0 ، 80:20 ، 60:40 و 40:60 درصد (در هر ترکیب با توجه به سطوح مورد نظر به نسبت مساوی از ساقه توتون و کاه گندم استفاده شد) و مقدار مصرف چسب اوره فرمالدهید در دو سطح 12 و 14 درصد وزن خشک خرده چوب بودند. نتایج حاصل از تحقیق نشان داد که با افزایش مقدار مصرف مخلوط کاه گندم و ساقه توتون تا 60 درصد، ویژگی های فیزیکی و مکانیکی پانل ها کاهش معنی داری داشت. از سوی دیگر افزایش مقدار مصرف چسب تا 14 درصد تأثیر مثبتی بر خواص فیزیکی و مکانیکی تخته ها داشته است و باعث بهبود چسبندگی داخلی، مقاومت خمشی و مدول الاستیسیته و پایداری ابعادی تخته ها شده است. نتایج این تحقیق نشان داد که با افزایش مصرف این نوع ضایعات تا سطح 40 درصد به همراه افزایش مقدار مصرف چسب تا 14 درصد، می توان تخته هایی با ویژگی های مکانیکی استاندارد تولید کرد.https://ijwpr.areeo.ac.ir/article_113420_89d2734e70d898fc0dd11fdbefc59aea.pdfموسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091332420171222Potential of CMP pulp production of Salix species in comparison with Populusپتانسیل تولید خمیر کاغذ شیمیایی-مکانیکی از گونه های بید در مقایسه با گونه صنوبر58559511357310.22092/ijwpr.2017.110696.1418FAحسین رسالتیاستاد گروه صنایع خمیروکاغذ، دانشگاه علوم کشاورزی و منابع طبیعی ساری. دانشکده مهندسی چوب و کاغذمصطفی نیکخواه دافچاهیدانشجوی دکتری دانشگاه علوم کشاورزی و منابع طبیعی ساریJournal Article20170521Due to shortage of harvestable forest wood in Iran, the potential of CMP pulp production from various species of salix (alba, fragilis and aegyptica), in comparison with populus deltoides, was investigated across this research work. The cooking liqour of Mazandaran wood and paper Mill, consisting of 50:50 ratios of sodium sulfite and sodium bisulfite, and hydrogen peroxide, were used for Chemical treatment and bleaching of the pulps, respectively. The results showed that the paper pulps of fragilis salix and alba salix had higher bulk and lower opacity than other species, respectively. From the strength properties point of view, the highest and lowest tensile strength of produced papers were related to alba and fragilis species, and, the highest and lowest burst and tear strength of the prepared papers have belonged to Salix aegyptica and Populus species, respectively. The data have shown that Salix species have a good pothential to be used as raw material to produce CMP pulp at the cooking yield of 85%. According to the results of this research work, alba salix and aegyptica salix are in first and the second priority to produce CMP pulp ,at the cooking yield of 85%, respectively.به علت کمبود چوبهای جنگلی قابل برداشت در ایران، پتانسیل تولید خمیر کاغذ شیمیایی-مکانیکی از گونههای سریعالرشد بید (آلبا، فوکا و مشک) در مقایسه با گونه سریعالرشد و غیرجنگلی صنوبر در این تحقیق مورد بررسی قرار گرفته است. از مایع پخت کارخانه چوب و کاغذ مازندران با نسبت 50:50 سولفیت سدیم و بی سولفیت سدیم برای تیمار شیمیایی و از پراکسید هیدروژن برای رنگبری خمیرهای کاغذ استفاده شد. نتایج نشان داد که خمیرهای کاغذ بید فوکا و بید آلبا به ترتیب دارای بیشترین و کمترین مقدار بالک و ماتی در بین گونهها بودهاند. از لحاظ خصوصیات مقاومتی، بیشترین و کمترین مقاومت کششی به ترتیب به کاغذهای بید آلبا و بید فوکا و بیشترین و کمترین مقادیر مقاومتهای ترکیدن و پارگی به ترتیب به کاغذهای بید مشک و صنوبر تعلق داشته است. دادههای حاصل از این مطالعه نشان داده است که گونههای بید دارای پتانسیل خوبی جهت استفاده به عنوان ماده اولیه در تولید خمیر کاغذ شیمیایی-مکانیکی در بازده پخت 85% میباشند. به طوری که طبق نتایج حاصل از این کار تحقیقاتی، گونه بید آلبا در اولویت اول و گونه بید مشک در اولویت دوم برای تولید خمیر کاغذ شیمیایی-مکانیکی (در بازده پخت 85%) قرار دارد.https://ijwpr.areeo.ac.ir/article_113573_36100c1296fd8ff44a5b441f2cf53f54.pdfموسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091332420171222Investigating the effect of diameter and dowel surface in softwood joints, made by welding and glueبررسی اثر قطر و سطح دوبل در اتصالات چوب سوزنیبرگ، ساخته شده به دو روش جوشکاری و اتصال با چسب59860511357210.22092/ijwpr.2017.115561.1439FAپانته آ عمرانیاستادیار، گروه صنایع چوب، دانشکده مهندسی عمران، دانشگاه تربیت دبیر شهید رجایی، تهران، ایران0000-0003-0027-3984هادی مریمیدانشجوی کارشناسی ارشد گروه صنایع چوب، دانشکده عمران، دانشگاه تربیت دبیر شهید رجایی، تهران، ایرانرضا عیسی پوردانشجوی کارشناسی ارشد گروه صنایع چوب، دانشکده عمران، دانشگاه تربیت دبیر شهید رجایی، تهران، ایرانJournal Article20170923Joints in furniture and wooden structures due to the highly sensitive bearing load are today one of the most important scientific topics. The most recent method proposed to build wooden joints in Europe and the United States is a method eco-friendly, without using any type of adhesive substance or connector, called "wood welding". In the present study, the effect of diameter and dowel surface on the tensile strength of softwood joints (made with dowel) was investigated using two methods: wood welding and glue bonding. Polyvinyl acetate glue (PVA) for bonding, species Fir (Abies alba) for members joint and species Hornbeam (Carpinus betulus) for connector dowels were selected as fixed parameters. The structure of the welded surfaces was analyzed using scanning electron microscopy (SEM). The results of the tensile strength test showed that parameters of diameter and type of dowel surface have a significant effect on the tensile strength of softwood joints in both joint methods.اتصالات در مبلمان و سازههای چوبی بهعلت حساسیت زیاد در برابر تحمل بار یکی از مهمترین مباحث علمی امروزه میباشند. جدیدترین روش مطرح در اروپا و امریکا برای ساخت اتصالات چوبی، روشی است دوستدار محیط زیست، بدون استفاده از هر نوع ماده چسبنده یا اتصالدهنده به نام "جوشکاری چوب". در پژوهش حاضر، تأثیر اندازه قطر و سطح دوبل بر مقاومت کششی اتصالات چوب سوزنیبرگ ساخته شده با دوبل چوبی به دو روش جوشکاری چوب و اتصال با چسب، مورد بررسی قرار گرفت. چسب پلیوینیل استات (PVA) برای ایجاد اتصال، گونه نراد (Abies alba) برای اعضای اتصال و گونه ممرز (Carpinus betulus) برای دوبلهای اتصالدهنده، به عنوان عوامل ثابت انتخاب شدند. ساختار سطوح جوشکاری شده با استفاده از میکروسکوپ الکترونی روبشی (SEM)، مورد تحلیل قرار گرفت. بررسی دادههای حاصل از آزمون مقاومت کششی، نشان داد که پارامترهای اندازه قطر و نوع سطح دوبل بر مقاومت کششی اتصالات چوب سوزنیبرگ اثر معنیداری در هر دو روش اتصال دارند.https://ijwpr.areeo.ac.ir/article_113572_b02229ec33cb78a383c7384cdbfc824b.pdf