موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091326420111222Effect of shape and particle size of mechanical pulp fines on paper propertiesبررسی تأثیر شکل و اندازه نرمه خمیر کاغذ مکانیکی بر ویژگیهای کاغذ60562111724010.22092/ijwpr.2018.117240FAامیر محسن ناظریکارشناسی ارشد، علوم و صنایع چوب و کاغذ، دانشگاه آزاد اسلامی، واحد علوم و تحقیقات تهرانمحمد طلایی پوراستادیار، علوم و صنایع چوب و کاغذ، دانشکده منابع طبیعی، دانشگاه آزاد اسلامی، واحد علوم و تحقیقات تهران.0000-0003-1143-3701سعید مهدویعضو هیأت علمی - موسسه تحقیقات جنگلها و مراتع کشور0000-0003-4077-8063Journal Article20180925<span style="font-family: 'Times New Roman','serif'; mso-bidi-font-family: 'B Lotus';">The effects of different fines with different shape and size of mechanical Pulp on Paper Properties in two fractions was investigated. Fines was classified in two categories including fibrils and flakes , and then effect of these particles on pulp properties was studied</span><span style="font-family: 'Times New Roman','serif'; mso-bidi-font-family: 'B Lotus';">.The fibril fraction was consist of fibrillar material, i.e., ribbons, fibrils, and thin lamella particles. The flake fraction consist of flake like material i.e., fiber wall fragments and thick lamella. An advanced image analysis method was used to characterize the properties of fibrils and flakes. The results indicate that the fibrils and flake fractions have distinct characteristics and effect on sheet properties. The fibrils strongly affected the strength properties, while the flakes improved light scattering. Generally, the smaller size Particles afforded higher sheet density and strength. Fines content and fibrillar material are very important parameters in mechanical pulping and can also affect quality controlling of mechanical pulp and papermaking.</span><span style="font-size: 12.0pt; mso-ansi-font-size: 11.0pt; font-family: 'B Lotus'; mso-ascii-font-family: 'Times New Roman'; mso-hansi-font-family: 'Times New Roman';" lang="FA">در این تحقیق تأثیر شکل و اندازه نرمهها<span class="MsoFootnoteReference"><span dir="LTR"><span class="MsoFootnoteReference"><span style="font-size: 11.0pt; mso-bidi-font-size: 12.0pt; line-height: 115%; font-family: 'Times New Roman','serif'; mso-fareast-font-family: 'Times New Roman'; mso-bidi-font-family: 'B Lotus'; mso-ansi-language: EN-US; mso-fareast-language: EN-US; mso-bidi-language: FA;">[1]</span></span></span></span> بر ویژگیهای کاغذ ساخته شده از خمیر مکانیکی در دو بخش مورد مطالعه قرار گرفت. در بخش اول گروهبندی نرمهها به دو گروه نرمههای رشتهای<span class="MsoFootnoteReference"><span dir="LTR"><span class="MsoFootnoteReference"><span style="font-size: 11.0pt; mso-bidi-font-size: 12.0pt; line-height: 115%; font-family: 'Times New Roman','serif'; mso-fareast-font-family: 'Times New Roman'; mso-bidi-font-family: 'B Lotus'; mso-ansi-language: EN-US; mso-fareast-language: EN-US; mso-bidi-language: FA;">[2]</span></span></span></span> و نرمههای نواری</span><span class="MsoFootnoteReference"><span style="mso-bidi-font-size: 12.0pt; font-family: 'Times New Roman','serif'; mso-bidi-font-family: 'B Lotus';" dir="LTR"><span class="MsoFootnoteReference"><span style="font-size: 11pt; line-height: 115%;">[3]</span></span></span></span><span style="font-size: 12.0pt; mso-ansi-font-size: 11.0pt; font-family: 'B Lotus'; mso-ascii-font-family: 'Times New Roman'; mso-hansi-font-family: 'Times New Roman';" lang="FA">انجام شد و در بخش دوم نیز تأثیر آنها بر ویژگیهای کاغذ ساخته شده مورد بررسی قرارگرفت. نرمههای رشتهای از مواد رشتهای، مانند دیواره نازک سلول و رشتهها تشکیل شده و نرمههای نواری متشکل از تکههای ضخیم دیواره سلول و اشعههای سلولی میباشند. برای شناسایی ویژگیهای نرمههای رشتهای و نواری از یک روش آنالیز تصویری پیشرفته استفاده شد. نتایج نشان داد که نرمههای رشتهای و نواری دارای خواص متفاوت بوده و اثرات مختلفی را بر خواص ورقه کاغذ حاصل دارند. نرمههای رشتهای به شدت خواص مقاومتی را تحت تأثیر قرار میدهند ولی نرمههای نواری خواص پخش نور را بهبود میبخشند. در مجموع ذرات با اندازه ریزتر سبب افزایش دانسیته و مقاومتهای کاغذ میشود. در نتیجه مقادیر نرمهها و مواد رشتهای عامل بسیار مهمی در نرمههای خمیرکاغذهای مکانیکی میباشد که در کنترل کیفیت نرمههای مکانیکی و خمیرکاغذ و کاغذ تولید شده بسیار با اهمیت هستند. </span>
<br clear="all" />
<span style="font-family: 'Times New Roman','serif';">1-F</span><span style="mso-bidi-font-size: 11.0pt; font-family: 'Times New Roman','serif';">iber Fines</span>
<span class="MsoFootnoteReference"><span class="MsoFootnoteReference"><span style="font-size: 10.0pt; line-height: 115%; font-family: 'Calibri','sans-serif'; mso-fareast-font-family: 'Times New Roman'; mso-bidi-font-family: Arial; mso-ansi-language: EN-US; mso-fareast-language: EN-US; mso-bidi-language: FA;">[2]</span></span></span><span style="mso-bidi-font-size: 11.0pt; font-family: 'Times New Roman','serif';">-Fibrils</span>
<span class="MsoFootnoteReference"><span class="MsoFootnoteReference"><span style="font-size: 10.0pt; line-height: 115%; font-family: 'Calibri','sans-serif'; mso-fareast-font-family: 'Times New Roman'; mso-bidi-font-family: Arial; mso-ansi-language: EN-US; mso-fareast-language: EN-US; mso-bidi-language: FA;">[3]</span></span></span><span style="mso-bidi-font-size: 11.0pt; font-family: 'Times New Roman','serif';">-Flakes </span>موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091326420111222Effect of anthraquinone on NSSC pupling of P.deltoidesتأثیر افزودن آنتراکینون در تولید خمیرکاغذ نیمهشیمیایی سولفیتخنثی از گونه صنوبر دلتوئیدس62263311724110.22092/ijwpr.2011.117241FAمریم روستاییکارشناس ارشد، علوم و صنایع چوب و کاغذ، دانشگاه تربیت مدرسربیع بهروزاستادیار، علوم و صنایع چوب و کاغذ، دانشگاه تربیت مدرسسعید مهدویاستادیار، بخش تحقیقات علوم چوب و فرآوردههای آن، مؤسسه تحقیقات جنگلها و مراتع کشور0000-0003-4077-8063Journal Article20180926This research was performed to improve the properties of the pulp made of Aspen Deltoides, using antraquinone(AQ) catalizer. Neutral sulfite semichemical (NSSC) method in three efficiency levels of 55, 60, and 65% was applied. Cooking situations was selected as: Specific Temperature (175˚ C) , Time (Variable) , Specific Percentage of Chemicals 14% and Anthraquinone 0.1% . In all stages of cooking, weight ratio of sodium sulfide to sodium bicarbonate was set as 4.5/1. The ratio of cooking liquid to chips was 5/1. The results indicated that AQ causes an increase in efficiency and a significant decrease in Kappa. Researches also indicated that by the use of AQ, strength indexes of the paper such as strength of burst, tearing, tensile, Ring Crush Test and Corrugating Medium Test increases. Optical experiments on hand sheets following addition of AQ, indicated increase in brightness and decrease in opacity.این بررسی با هدف استفاده از کاتالیزور آنتراکینون جهت بهبود خواص خمیر کاغذ حاصل از گونه صنوبر دلتوئیدس به روش نیمهشیمیایی سولفیتخنثی (NSSC) در سه سطح بازده 55، 60 و 65 درصد انجام شد. شرایط پخت شامل: درجه حرارت 175 درجه سانتیگراد، زمان (متغیر)، درصد مواد شیمیایی 14 درصد و آنتراکینون 1/0 درصد بود. در تمام پختها نسبت وزنی سولفیت سدیم به بیکربنات سدیم (5/4 به 1) انتخاب شد. نسبت مایع پخت به خردهچوب 1/5 بود. نتایج حاصل نشان داد که آنتراکینون سبب افزایش بازده و نیز کاهش عدد کاپا به طور معنیداری شد. بررسیها نشان داد که با افزودن آنتراکینون شاخصهای مقاومتی کاغذ بدستآمده نظیر مقاومت به ترکیدن، پارهشدن، کشش، لهشدگی حلقوی و لهشدگی کنگرهای افزایش مییابد. به طوری که بررسی خواص نوری کاغذهای دستساز نشان داد که با افزودن آنتراکینون، روشنی افزایش یافته و ماتی کاهش مییابد.
<span style="mso-ansi-font-size: 10.0pt; mso-bidi-font-size: 12.0pt; font-family: 'B Lotus'; mso-bidi-language: FA;" lang="FA"> </span>موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091326420111222Investigation on production of bleachable chemi-mechanical pulp from
wheat strawبررسی ساخت خمیرکاغذ شیمیایی – مکانیکی رنگبری شده از کاهگندم63464611724210.22092/ijwpr.2011.117242FAاحمد جهان لتیباریعضو هیات علمی دانشگاه آزاد اسلامیnullJournal Article20180926In an attempt to develop pulping process suitable for small scale implementation, production of bleachable chemi-mechanical pulp from wheat starw is investigated. Four levels (10, 12, 14 and 16% based on oven dry weight of straw) NaOH and three pulping times (20, 30 and 40 minutes) at 95<sup>°</sup>C pulping temperature were used. After digester yield varied between 64.65 and 71.7% and the total yield after defibration was measured as 54.45% and 62%. Unrefined pulp freeness varied between 708 and 765 ml CSF. Pulps produced applying 10-16% NaOH, 40 minutes pulping time and 95<sup>°</sup>C pulping temperature was selected from further evaluation. These pulps were refined to about 365 ml CSF in a PFI mill and then handsheets were made for strength evaluation. The apparent density of the handsheets varied between 437-488 kg/m<sup>3</sup>, tear index between 6.51-7.11 mN.m<sup>2</sup>/g, and tensile index between 29.2 -30.8 N.m/g. Significant difference at 99% was not observed between the strength of the pulps. Then pulp produced applying 10% NaOH, 40 minutes pulping time and 95<sup>°</sup>C pulping temperature was selected for bleaching trials. Totally Chlorine Free (TCF) bleaching sequence was used for bleaching the selected pulp. Pulps bleached applying 4% H<sub>2</sub>O<sub>2</sub> and 3.5% NaOH, 3% sodium Silicate, 0.5% MgSO4 and 0.3% DTPA for 2 hours showed the highest brightness of 50.69% compared to 29.2% for unbleached pulp.این بررسی با هدف تولید خمیرکاغذ قابل رنگبری از کاهگندم انجام گرفته است. بدین منظور با تغییر مقدار قلیاییت فعال (NaOH) در چهار سطح 10، 12، 14 و16 درصد (برمبنای وزن خشک کاهگندم) و دو زمان پخت 20 و40 دقیقه خمیرکاغذ تهیه شده است. دمای پخت در 95 درجه سانتیگراد ثابت در نظر گرفته شده است. بازده بعد از پخت خمیرکاغذها بین 6/64 درصد تا 7/71 درصد و بازده کل بعد از جداسازی الیاف بین 45/54 درصد تا 62 درصد متغیر بوده است. درجهروانی اولیه خمیرکاغذها نیز بین 708 تا 765 میلیلیتر استاندارد کانادایی تغییر کرده است. خمیرکاغذهایی که با قلیاییت فعال 10 تا 16 درصد و زمان پخت40 دقیقهای تهیه شدهاند تا درجهروانی حدود 350 میلیلیتر استاندارد کانادایی پالایش شدند و پس از آن ویژگیهای کاغذ دستساز از آنها اندازهگیری شد. دانسیته کاغذ بین 437 تا 489 کیلوگرم بر مترمکعب، شاخص مقاومت به پاره شدن بین 51/6 تا 91/7 mN.m<sup>2</sup>/g و شاخص مقاومت به کشش بین 2/29 تا 8/30 N.m/g اندازهگیری شد. با توجه به این که اختلاف معنیداری در سطح اعتماد 99 درصد بین ویژگیهای مقاومتی کاغذهای حاصل مشاهده نشد، لذا خمیرکاغذ ساخته شده با 10 درصد قلیاییت فعال (NaOH)، 40 دقیقه زمان پخت و 95 درجه دمای پخت جهت رنگبری انتخاب شد. رنگبری خمیرکاغذ با روش کاملاً بدون کلر (TCF) انجام گرفت. در روش رنگبری یک مرحلهای TCF، استفاده از 4 درصد پروکسید هیدروژن و 5/3 درصد هیدروکسید سدیم، زمان 2 ساعت، سیلیکات سدیم 3 درصد و سولفات منیزیم معادل 5/0 درصد و 3/0 درصد DTPA وزن خشک خمیرکاغذ قبل از رنگبری، روشنی خمیرکاغذ را به 69/50 درصد (روشنی خمیرکاغذ قبل از رنگبری2/29 درصد بوده است) افزایش داد.موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091326420111222Effects of plant dyes ( walnut shell , tea plant , henna ) on paper's stability in manuscript restorationبررسی تأثیر رنگهای گیاهی (حنا، گردو و چای) بر پایداری کاغذ در مرمت نسخخطی64766611724310.22092/ijwpr.2011.117243FAسمیه سلیمانیکارشناس ارشد، مرمت اشیا فرهنگی و تاریخی، دانشگاه هنر تهرانسید جواد سپیده دماستادیار، کاغذ و صنایع چوب، دانشکده کشاورزی و منابع طبیعی، دانشگاه آزاد اسلامی واحد کرجحمیده ملکیانکارشناس ارشد مرمت اشیا فرهنگی و تاریخی، کتابخانه مجلس شورای اسلامیJournal Article20180926The stability of colored paper through dyes is very important in manuscript restoration. In this project Japanese papers (model papers) were colored with different dyes such as henna, walnut and tea. Artificial aging test was performed on these papers as well. Dye effect on stability of colored papers was measured through mechanical (folding endurance, tensile breaking and tear resistance) tests before/after aging test statistically; folding endurance test results in color level is significant. Tea colored paper sample was not as stable as model paper in folding resistance and the average of tea sample compare to model sample was 39.9 to 69.5. Folding endurance reduction was seen in tea and henna samples following aging test. The effects on tensile and tear resistance were not statistically different or dyes were not affected to cause any increase or decrease in stabilities. Scanning electron microscopy (SEM) images of model and dyed papers have demonstrated color and aging effects. The pH test upon henna sample, have shown acidic condition. Model paper was not the same as dyed papers in terms of weight and thickness. All samples include model and dyed papers, demonstrated decrease in brightness and yellowness and increase in redness following aging test.استفاده از رنگهای گیاهی بر پایداری کاغذمرمتی در زمینه همرنگ سازی، در مرمت نسخخطی حائز اهمیت میباشد. در این پروژه پس از تهیه کاغذهای تیشوی ژاپنی و رنگرزی آنها با رنگهای گیاهی برگ حنا، پوست گردو و برگ چای سیاه، آزمون کهنهسازی مصنوعی برروی نمونهها انجام گردید. به منظور بررسی تأثیر هر یک از عوامل رنگزا بر خواص مقاومتی کاغذهای رنگرزی شده، آزمونهای مکانیکی مقاومت به تاخوردگی، کشش و پاره شدن بر روی نمونهها قبل و بعد از کهنهسازی انجام شد. در بررسی نتایج آزمون مقاومت به تاخوردگی، شاهد تأثیر معنادار رنگ از نظر آماری هستیم که نمونه چای در مقایسه با کاغذ شاهد با میانگین 9/39 به 5/69 کاهش چشمگیر مقاومت به تاشدن را نشان میدهد. این مسئله یعنی کاهش مقاومت به تاشدن در مورد رنگ چای و همچنین رنگ حنا بعد از کهنهسازی نیز مشاهده میگردد. در آزمونهای مکانیکی، مقاومتکششی و پارهشدن از نظر آماری اثرهای معنادار ندارد؛ بعبارت دیگر رنگرزی تأثیری بر افزایش یا کاهش میزان این مقاومتها نداشته است. تصاویر میکروسکوپ الکترونی نمونههای شاهد و رنگرزی شده، تأثیر عوامل رنگ و کهنهسازی را بخوبی نشان میدهد. در آزمون pH سنجی نمونه رنگرزی شده با حنا دارای pH کاملاً اسیدی میباشد که آن به دلیل ساختار شیمیایی گیاه حنا میباشد. در آزمونهای تعیین جرمپایه و ضخامت کاغذ، کاغذهای رنگرزی شده دارای جرم پایه و ضخامتهای بالاتری نسبت به نمونه شاهد میباشند. بنابراین در بررسی نتایج آزمون روشنی در همه نمونهها بعد از کهنهسازی میزان روشنی و زردی کاهش و میزان قرمزی افزایش داشته است.موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091326420111222Effect of steaming time on medium density fiberboard properties produced from beech wood fibersاثر زمان بخارزنی بر ویژگیهای تختهفیبر دانسیته متوسط (MDF) ساخته شده از الیاف چوب راش66768111724410.22092/ijwpr.2011.117244FAابوالفضل کارگرفردعضو هیئت علمی بخش تحقیقات علوم چوب و فرآوردههای آن، مؤسسه تحقیقات جنگلها و مراتع کشور، تهرانرضا حاجی حسنیکارشناس بخش تحقیقات علوم چوب و فرآوردههای آن0000-0003-0104-5764فاطمه رضاییکارشناس، مهندسی علوم چوب و کاغذ، دانشکده منابع طبیعی، دانشگاه مازندرانJournal Article20180926In this investigation, 36 laboratory Medium Density Fiberboard (MDF) panels were produced using beech wood fibers. Variables were three steaming time (5, 10 and 15 minutes), two press time (4 and 6 minutes) and two resin consumption levels (9 and 11%). The physical and mechanical properties of panels were measured and analyzed. The results indicated that the favorite MOR was observed in panels produced through 4 minutes press time, 11% resin consumption and 10 minutes steaming time. Also increase in steaming time to 15 minutes and press time to 6 minutes, caused the MOR and MOE of boards reduced to minimum level. The internal bonding (IB) of boards decreased with steaming and press time increase. However, the panels produced at 25 minutes of steaming time showed minimum of thickness swelling. The results of this investigation indicated that the thickness swelling of boards improved with increase in steaming time. However mechanical properties of boards were higher where the shorter steaming time applied.در این بررسی از الیاف چوب گونه راش، با استفاده از سه زمان بخارزنی 5، 10 و 15 دقیقه، دو زمانپرس 4 و6 دقیقه و دو میزان مصرف چسب 9 و 11 درصد، تختهفیبر دانسیته متوسط (MDF) به روش خشک تهیه گردید. سپس خواص فیزیکی و مکانیکی تختههای ساخته شده از آنها اندازهگیری و با استفاده از طرح آماری فاکتوریل مورد تجزیه و تحلیل قرار گرفت. نتایج نشان داد که در شرایط زمان بخارزنی10 دقیقه، زمانپرس4 دقیقه و مصرف چسب 11 درصد، مقاومتخمشی در حد مطلوبی قرار دارد. همچنین با افزایش زمان بخارزنی به 15 دقیقه و زمانپرس به 6 دقیقه، مقادیرMOR و MOE به حداقل کاهش یافت. همچنین چسبندگیداخلی تختههای ساخته شده با افزایش زمان بخارزنی و زمانپرس کاهش یافته است، در حالی که حداقل واکشیدگیضخامت تختهها در شرایط استفاده از زمان بخارزنی 15 دقیقه مشاهده گردید. بنابراین نتایج حاصل از اندازهگیری ویژگیهای فیزیکی و مکانیکی تختهفیبرهای ساخته شده نشان داد که با افزایش زمان بخارزنی، واکشیدگیضخامت تختهها بهبود مییابد. در حالی که ویژگیهای مکانیکی تختههای ساخته شده با زمانهای کوتاهتر بخارزنی در سطح بالاتری قرار داشته است.موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091326420111222Effect of steam treatment on chemical changes of wood componentsتأثیر تیمار با بخار آب روی ویژگیهای شیمیایی خردههای چوب صنوبر68269811724510.22092/ijwpr.2011.117245FAحمید هاتف نیادانشآموخته کارشناسی ارشد صنایع چوب، دانشکده منابع طبیعی، دانشگاه تهرانعلی اکبر عنایتیاستاد گروه علوم و صنایع چوب و کاغذ دانشکده منابع طبیعی. دانشگاه تهرانکاظم دوست حسینیاستاد گروه علوم و صنایع چوب و کاغذ دانشکده منابع طبیعی. دانشگاه تهرانمحمد آزادفلاحاستادیار گروه علوم و صنایع چوب و کاغذ دانشکده منابع طبیعی. دانشگاه تهرانJournal Article20180926Poplar wood chips were treated by steaming in different conditions. The chemical composition changes of milled wood were studied. The obtained results indicate hemicelluloses degradation, reduction of acetyl groups and formation of organic acid during the treatment. It was also found that steam treatment has led to degradation of low-molecular lignin units, decrease in cellulose amorphous regions, increase of acetone extractives and hot water solubility as well as one percent sodium hydroxide solubility. The FT-IR spectra indicated a structural change of aromatic polymers in the wood, cleavage of the acetyl group of hemicelluloses and formation of organic acid.<span lang="FA" dir="RTL">در این مطالعه چوب صنوبر تحت تأثیر بخار داغ آب، تیمار و تغییرات شیمیایی ایجاد شده در ترکیبات اصلی آن بررسی شد. نتایج نشان داد که کاهش مقدار همیسلولزها در اثر بخارآب داغ، سریع و به مقدار زیاد اتفاق میافتد. تخریب همیسلولزها، حذف گروههای استیل و تولید اسیدهای آلی با افزایش شدت تیمار زیاد میشود. افزایش این اسیدها همزمان با افزایش شدت تیمار، تخریب همیسلولزها و نیز بخشی از مناطق آمورف سلولز را تسریع کرده و میتواند باعث کاهش مقاومتهای چوب تیمار شده شود. همچنین تعدادی از واحدهایی از لیگنین که وزن مولکولی پایین دارند تخریب میشوند. مقادیر مواد استخراجی، مواد قابل حل در آب داغ و مواد قابل حل در محلول گرم هیدروکسید سدیم یک درصد، با افزایش شدت تیمار زیاد میشود. همچنین نتایج طیفسنجی </span><span>FT-IR</span><span dir="RTL"> <span lang="FA">تغییرات ساختاری در پلیمرهای آروماتیک و گسست گروههای استیل همیسلولزها و تولید اسیدهای آلی را نشان داد.</span></span>موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091326420111222Effect of nanoclay on the properties of medium density
fiberboard (MDF)اثر نانو ذراترس بر خواص تختهفیبر با دانسیته متوسط (MDF)69970711724610.22092/ijwpr.2011.117246FAسید محمد جواد موسوی حسینیکارشناس ارشد، علوم و صنایع چوب و کاغذ، دانشکده منابع طبیعی- دانشگاه تهرانمحمد مهدی فائزی پوراستاد، گروه علوم و صنایع چوب و کاغذ دانشگاه تهرانحسین یوسفیدانشآموخته دکترای تخصصی علوم و صنایع چوب و کاغذ دانشگاه تهرانJournal Article20180926The effect of using nanoclay on MDF properties was investigated. Sodium montmorolonit (NA<sup>+</sup>MMT) was used in three levels of 0, 3 and 6 percent based on dry weight of two resins of urea formaldehyde (UF) and Methylene diphenyl diisocyanate (MDI). Modulus of rupture (MOR), modulus of elasticity (MOE), internal bonding (IB), thickness swelling (TS) and water absorption (WA) of MDF were measured based on EN standard. Results demonstrated that with the increase of nanoclay in both UF and MDI resins MOR and MOE of MDF increased significantly in such a way that with the use of UF containing 6% nanoclay MOR increased by 33%. Although, IB was significantly affected by UF containing nanoclay, MDI containig nanoclay caused reduction in IB. WA and TS of MDF made from MDI did not show significant variation by increase of nanoclay but those made from UF resin positively affected by adding nanoclay in such a way that MDF made from 3% nanoclay showed 41% loss in TS compared to those made from pure UF.در این مطالعه اثر نانو ذراترس بر خواص کاربردی تختهفیبر با دانسیته متوسط (MDF) مورد بررسی قرار گرفت. از نانو ذراترس سدیم مونت موریلونیت (NA<sup>+</sup>MMT) در سه سطح صفر، 3 و 6 درصد بر مبنای وزن خشک دو نوع رزین اوره فرمالدهید (UF) و متیلندیفنیلدیایزوسیانات (MDI) استفاده شد. مقاومتخمشی، مدولالاستیسیته، چسبندگیداخلی، جذب آب و واکشیدگیضخامت در 24 ساعت مورد ارزیابی قرار گرفتند. نتایج نشان داد که با افزایش درصد نانورس در تختههای ساخته شده با چسب UF و MDI، مقاومتخمشی و مدولالاستیسیته نمونهها افزایش یافتهاست. به طوری که در نمونههای ساخته شده با چسب UF با افزودن 6 درصد نانورس حدود 33 درصد افزایش مقاومتخمشی مشاهده شد. وجود اختلاف معنیدار در بین تیمارها برای آزمون چسبندگیداخلی دیده شد، به طوری که با افزایش نانورس چسبندگیداخلی تختههای ساخته شده با چسب UF افزایش یافت ولی در مورد چسب MDI، مقاومت چسبندگیداخلی کاهش نشان داد. اختلاف بین تیمارها برای جذب آب تختههای ساخته شده با چسب ایزوسیانات قابل توجه نیست و برای تختههای ساخته شده با چسب اورهفرمآلدهید با افزایش نانورس اندکی کاهش جذب آب مشاهده شد. بنابراین با افزایش نانورس در تختههای ساخته شده با چسب UF مقدار واکشیدگیضخامت کاهش قابل توجهی یافتهاست، به طوری که در اثر استفاده از 3 درصد نانورس، 41 درصد کاهش واکشیدگیضخامت مشاهده شد و در مورد تختههای ساخته شده با چسب MDI با افزایش نانورس مقدار واکشیدگیضخامت نمونهها افزایش غیر معنیداری یافت.موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091326420111222Stress analysis and failure prediction in dowel joint by FEMتحلیل توزیع تنش و پیشبینی شکست در اتصال دوبل به روش عناصر محدود70871811724710.22092/ijwpr.2011.117247FAامیر لشگریاستادیار، گروه علوم و صنایع چوب و کاغذ، دانشگاه آزاد اسلامی واحد کرجJournal Article20180926In this study, distribution pattern and tension concentration as well as failure prediction in dowel joint were analyzed. The effect of dowel diameter (6, 8, 10 mm) and wood type (Beech, Alder and white spruce) on tension resistance and bending moment were examined. The dimensions for making T-form joints were 5×5×2/5 cm. Wooden dowel used in this research was carpinus betulus which accounts as the common dowel in market. Also, PVA was used in Joints. A total of 36Tshape samples comprising 9 combinations of the above factors in 4 replications were made. Tension resistance and bending moment were measured by mechanical test machine. For exertion strength due to analyzing the resistance loading speed equal to 1.25 mm/min were applied. Also, to analyze distribution pattern and tension concentration in affected joints, finite element method and ANSYS Software were used. According to the results of the simulation modeling, joint which endured the maximum tension complied with the real joints. Distribution of tension in the middle of the bending moment depth was greatest and tension in dowel joints was concentrated in impaired points.در این بررسی نحوه توزیع تنش، تمرکز تنش و پیشبینی محلهای شکست در اتصال دوبل، مقاومتکششی و گشتاورخمشی مورد مطالعه قرار گرفت. اثر قطر دوبل در سه مقدار 6 ، 8 و10 میلیمتر، نوع گونه چوبی راش، توسکا و نوئل بر مقاومتکششی و گشتاورخمشی بررسی شده است. برای ساخت اتصالات T شکل ابعاد عضوها در اتصال مورد بررسی 5/2×5×5 سانتیمتر بوده است. فاصله بین دوبلها 2 سانتیمتر بوده است. نوع گونه چوبی دوبل مورد استفاده در این تحقیق از جنس ممرز بوده که دوبل متداول در بازار است. چسب مورد استفاده بهعنوان ماده کمکی نیز در اتصال دوبل چسب پلی وینیل استات میباشد. از ترکیب عوامل متغیر فوق 9 ترکیب عوامل بوجود آمده که با توجه به 4 تکرار جمعاً 36 نمونه T شکل ساخته و مقاومتکششی و گشتاورخمشی بوسیله ماشین آزمون مکانیکی اندازهگیری شد. برای اعمال نیروهای مورد نظر برای بررسی مقاومتهای مزبور از سرعت بارگذاری معادل با 25/1 میلیمتر بر دقیقه استفاده شد. برای بررسی توزیع تنش و تمرکز تنش در اتصالها از روش عناصر محدود و نرمافزار ANSYS استفاده شده است. با توجه به نتایج حاصل از شبیهسازی اِلمانی از اتصال که تنش حداکثر را تحمل میکند با اِلمانی که در اتصال واقعی دچار شکست میشوند مطابق است. بنابراین توزیع تنش در قسمت میانی دوبل در اعمال گشتاورخمشی حداکثر است و تنش در اتصالات دوبل در نقاطی که شکست ایجاد شده متمرکز است. توزیع تنش در اتصالات دوبل در زمان اعمال بار کششی در قسمتهای فوقانی دوبل حداکثر بوده و میزان تنش در حوالی حفره دوبل حداکثر است؛ به طور کلی شکست در حالت تجربی در اتصال دوبل بیشتر در عضوهای اتصال رخ میدهد تا دوبلموسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091326420111222Effect of great size wood particles on density profile and physical -mechanical properties of particleboards made from poplarاثر اختلاط خردههای چوب درشت بر پروفیل دانسیته و خواص فیزیکی- مکانیکی تخته خردهچوب ساخته شده از چوب صنوبر71973111724810.22092/ijwpr.2011.117248FAعلی اکبر عنایتیاستاد، گروه علوم و صنایع چوب و کاغذ، دانشکده منابع طبیعی دانشگاه تهرانفرناز اصلاحکارشناسارشد، گروه علوم و صنایع چوب و کاغذ، دانشکده منابع طبیعی دانشگاه تهرانJournal Article20180926This study was conducted to investigate the effect of mixing great size wood particles of poplar with appropriate size particles of the same species, on density profile and physical -mechanical properties of the made particleboard, this study was carried out. One layer boards were made by use of appropriate and great size residue particles on a 7mm pores screen with the ratio of 0/100, 15/85, 30/70, and 45/55 respectively. The results obtained from measured physical and mechanical properties showed that increasing great particles ratio had no negative effect on properties of boards. Increasing the amount of this particles in boards composition, caused increasing internal bonding and decreasing water absorption and thickness swelling levels. In addition, there were no significant differences within boards made from different treatments MOR and MOE properties. Regarding results of this study, when %15 great particles was used with appropriate particle ones, boards had minimum reduction of mechanical strength. Investigation of density profile showed the same result. But all properties of the boards were over the determined limit in terms of relevant standard values even in the case of using 45% great particles.<span style="font-size: 12.0pt; font-family: 'B Lotus'; mso-ascii-font-family: 'Times New Roman'; mso-hansi-font-family: 'Times New Roman'; mso-bidi-language: FA;" lang="FA">هدف از انجام این تحقیق بررسی اثر اختلاط خردههای چوب درشت صنوبر با خردههای چوب با اندازة مناسب همین گونه برپروفیل دانسیته و خواص فیزیکی- مکانیکی تخته خردهچوبهای ساخته شده از آن بوده است. به این منظور با استفاده از خردههای چوب درشت باقی مانده روی الک با درشتی 7</span><span style="font-size: 12.0pt; font-family: 'B Lotus'; mso-ascii-font-family: 'Times New Roman'; mso-hansi-font-family: 'Times New Roman'; mso-bidi-language: FA;" lang="FA">میلیمتر و خردههای چوب با ابعاد معمول و با نسبت اختلاط: 0به100، 15 به</span><span style="font-size: 12.0pt; font-family: 'B Lotus'; mso-ascii-font-family: 'Times New Roman'; mso-hansi-font-family: 'Times New Roman'; mso-bidi-language: FA;" lang="FA">85،30 به70 و</span><span style="font-size: 12.0pt; font-family: 'B Lotus'; mso-ascii-font-family: 'Times New Roman'; mso-hansi-font-family: 'Times New Roman'; mso-bidi-language: FA;" lang="FA">45</span><span style="font-size: 12.0pt; font-family: 'B Lotus'; mso-ascii-font-family: 'Times New Roman'; mso-hansi-font-family: 'Times New Roman'; mso-bidi-language: FA;" lang="FA">به 55</span><span style="font-size: 12.0pt; font-family: 'B Lotus'; mso-ascii-font-family: 'Times New Roman'; mso-hansi-font-family: 'Times New Roman'; mso-bidi-language: FA;" lang="FA">تختههای یک لایه به ضخامت 15 میلیمتر با جرم مخصوص 65/0 گرم</span><span style="font-size: 12.0pt; font-family: 'B Lotus'; mso-ascii-font-family: 'Times New Roman'; mso-hansi-font-family: 'Times New Roman'; mso-bidi-language: FA;" lang="FA">بر سانتیمترمکعب ساخته شد. نتایج حاصل از اندازهگیری ویژگیهای فیزیکی و مکانیکی تختهها نشان داد که افزودن خردههای چوب درشت اثر منفی بر خواص فیزیکی و مکانیکی تختهها نداشته است، به طوری که با افزایش مقدار این خردههای چوب در ساختار تختهها چسبندگی داخلی افزایش، مقاومتخمشی و مدولگسیختگی بدون تغییر و جذب آب و واکشیدگی ضخامت آنها کاهش یافت. با توجه به نتایج این تحقیق مشخص گردید که استفاده از 15 درصد خردههای چوب درشت به همراه خردههای چوب با اندازة مناسب، در تختههای ساخته شده کمترین افت را در مقاومتهای مکانیکی آنها خواهیم داشت، به نحوی که رد بررسی پروفیل دانسیته نیز همین نتیجه را نشان میدهد. امّا اگر از خردهچوبهای درشت به میزان 45 درصد استفاده شود، تمامی ویژگیهای فیزیکی و مکانیکی تختهها بیشتر از حد تعیین شده در استاندارد مربوط به این گونه تختهها میباشد.</span>موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091326420111222Designing and manufacturing of polyester composites reinforced with natural and synthetic fibers as an alternative for the wood in music instrumentsطراحی و ساخت کامپوزیتهای پلیمری از الیاف طبیعی و مصنوعی با رزین پلیاستر برای جایگزینی چوب در ساخت آلات موسیقی73275611725110.22092/ijwpr.2011.117251FAجعفر اسکندریدانشیار، مهندسی مکانیک، مرکز کامپوزیت تهرانامیر سهیل پیرایش فرکارشناس نخبه مهندسی پلیمر، دانشگاه آزاد اسلامی واحد علوم و تحقیقات تهران، ساختمان فنی و مهندسی، گروه مهندسی پلیمرمحمد مهدی جلیلیاستادیار، مهندسی پلیمر، دانشگاه آزاد اسلامی واحد علوم و تحقیقات، گروه مهندسی پلیمرسید یحیی موسویکارشناس نخبه مهندسی پلیمر، دانشگاه آزاد اسلامی واحد علوم و تحقیقات تهران، ساختمان فنی و مهندسی، گروه مهندسی پلیمرمهران روح نیادانشیار، علوم صنایع چوب و کاغذ، دانشگاه آزاد اسلامی واحد کرج، گروه چوب و کاغذ0000-0002-7466-995XJournal Article20180926In this study, three composites (Carbon fiber- Polyester resin, Glass fiber-Polyester resin and Hemp fiber-Polyester resin) are designed as a substitute for the wood in music instruments and their acoustic properties such as elastic modulus, acoustic coefficient, and acoustic coefficient efficiency are investigated. For better evaluation of the results, two wood specimens from <em>Cupressus arizonica</em> and <em>Morus Alba</em> trees (which are using in many acoustic applications) were chosen and analyzed as control samples. The results show that the resultant composites possess essential acoustic and vibrational properties so that the result for Carbon fiber-Polyester composite exhibits tremendous acoustic properties than wood samples did. In this paper, the water absorption of resultant composites and wood samples were also measured. The results demonstrate that composites specimens could resist against humidity much better than wood samples.
در این پژوهش باتوجه به معایب چوب برای کاربرد در ساخت آلات موسیقی، کامپوزیتهایی بهعنوان جایگزین چوب در آلات موسیقی طراحی گردید و خواص آکوستیک این سه نوع کامپوزیت مختلف (الیاف کربن- رزین پلیاستر، الیاف شیشه- رزین پلیاستر، الیاف کنف- رزین پلیاستر) مانند مدول الاستیک، ضریب آکوستیک، فاکتور کارایی تبدیل آکوستیک و دیگر فاکتورهای مرتبط مورد بررسی قرار گرفت. بمنظور درک بهتر نتایج بدستآمده از نمونههای کامپوزیتی ساخته شده، دو نمونه چوب درختان سرو و توت سفید (که کاربرد بسیار زیادی در ساخت آلات موسیقی دارند) بهعنوان نمونههای شاهد انتخاب شده و مورد بررسی قرار گرفتند. مقایسه نتایج نشان داد که کامپوزیتهای ساخته شده دارای خواص ارتعاشی و آکوستیکی بسیار ویژهای هستند، به طوری که نتایج بدستآمده در نمونه الیاف کربن-رزین پلیاستر بسیار فراتر از خواص آکوستیک چوب درختان سرو و توت بود. همچنین در این پژوهش میزان جذب آب کامپوزیتهای تهیه شده در کنار دو نمونه چوب اندازهگیری شد، که نتایج مقاومت بسیار خوب این نمونههای کامپوزیتی در برابر رطوبت در مقایسه با نمونههای چوبی را نشان داد.موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091326420111222Effect of different polypropylene grades and coupling agent on the properties of Wood Plastic Compositesاثر درجات مختلف پلیپروپیلن و ماده سازگارکننده بر روی ویژگیهای چندسازه چوب- پلاستیک75778411725210.22092/ijwpr.2011.117252FAفاطمه طاهریکارشناسارشد صنایع چوب، دانشکده منابع طبیعی دانشگاه تهرانعلی اکبر عنایتیاستاد، گروه صنایع چوب و کاغذ، دانشکده منابع طبیعی دانشگاه تهرانعبدالرسول ارومیه ایدانشیار، پژوهشکده پلیمر و پتروشیمی ایرانمهدی تجویدیدانشیار، گروه صنایع چوب و کاغذ، دانشکده منابع طبیعی دانشگاه تهرانJournal Article20180926By utilizing three different grades of Polypropylene (PP) as matrix, two different kind of MAPP as coupling agent and without MAPP and <em>Pistachio's</em> flour, composite samples were produced. Physical and mechanical properties of wood plastic composites including: MOR, MOE, tensile strength, bending strength, impact strength, hardness, water absorption and thickness swelling (816 hours) were determined. Results indicated that the effect of different grade of polypropylene and coupling agent on water absorption, thickness swelling, hardness and impact strength variables were insignificant. Use of Polypropylene having higher Melt Flow Index (MFI) leads to increase in mechanical properties of wood plastic composite samples such as Bending and Tensile strength even if coupling agent wasn't used. Use of different kind of MAPP as coupling age in making wood plastic composites can result in better mechanical properties which based on their type have different effect.
با استفاده از سه درجه مختلف پلیپروپیلن و دو نوع سازگارکننده متفاوت و بدون سازگارکننده و آرد چوب پسته، نمونههای آزمونی چندسازههای چوبپلاستیک ساخته شده و خواص آنها با یکدیگر مقایسه گردید. به این منظور خواص فیزیکی و مکانیکی نمونههای آزمونی چوبپلاستیک ازجمله جذب آب و واکشیدگی ضخامت درازمدت (816 ساعت)، مقاومتخمشی، مقاومتکششی، مدولالاستیسیته کششی و خمشی، مقاومت به ضربه و سختی اندازهگیری شد. نتایج حاصل از اندازهگیریهای ویژگیهای فیزیکی و مکانیکی نشان داد که اثر درجه پلیپروپیلن و نوع ماده سازگارکننده بر میزان جذب آب و واکشیدگی ضخامت نمونهها پس از 816 ساعت غوطهوری در آب و همچنین مقاومت به ضربه و سختی، معنیدار نبوده است. البته استفاده از پلیپروپیلن با شاخص جریان مذاب بالاتر حتی در صورت عدم استفاده از مادهسازگازکننده، منجر به افزایش ویژگیهای مکانیکی چندسازهی چوبپلاستیک ازجمله مقاومتخمشی و کششی شد. به هرحال، به کار بردن انواع متفاوت MAPP بهعنوان سازگارکننده، ویژگیهای مکانیکی چوبپلاستیک را افزایش میدهد که با توجه به نوع آن میتواند اثر متفاوتی داشته باشد.
موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091326420111222Determination of proper college student chair dimension and comparison with the prevalent modelتعیین ابعاد مناسب صندلی دانشجویی و مقایسه آن با صندلیهای مورد استفاده77278411725310.22092/ijwpr.2011.117253FAعلی بیات کشکولیاستادیار، گروه علوم و صنایع چوب و کاغذ، دانشگاه زابلمرتضی ناظریاناستادیار، گروه علوم و صنایع چوب و کاغذ، دانشگاه زابلJournal Article20180926Definition of furniture design and its products according to the principles of anthropometry is essential and meaningful. Dimensions of chair should optimize fitting based on anthropometric measurements of population. The research explores the appropriate chair dimension which best fit the anthropometric characteristics of Zabol students. The applied methodologies were descriptive and approximate. Anthropometric measurements of Zabol students, include back height, arm-shoulder to elbow, popliteal height, buttock popliteal height and hip circumference, and statistical analyzes, include Duncan analysis and descriptive statistics used and proper dimension of chair were determinate by the guideline. A total of 140 students (15 female and 20 male representing each of the four bachelor duration) were sampled. Dimension of all chairs variety were recorded. Differences of anthropometric measurements of 60 people were measured to available education chair. The obtained results showed that the chair dimensions were greater than the acceptable limits for most students. If chair dimensions, include armrest height, seat height, seat depth, seat width and backrest height are equal to 20, 42, 38, upwards of 59 and 35 cm, match percent could be improved to 32%, also, 49%, 49%, upwards of 59% and 44%, respectively.<strong> </strong>شناسایی روش دخالت اصول ارگونومی در طراحی مبلمان ضروری و مزایای زیادی دارد. ابعاد صندلیها باید حداکثر تناسب را با ابعاد آنتروپومتری جامعه آماری داشته باشد. حال سئوال، اساسی این است که مناسبترین ابعاد صندلی برای جامعه آماری مورد مطالعه چه اندازههایی باید باشد. با عنایت به این سئوال، روششناسی تحقیق توصیفی و تخمینی بوده و از ابعاد آنتروپومتری دانشجویان دانشگاه زابل شامل ارتفاع شانه، ارتفاع آرنج، ارتفاع رکبی، طول رکبی کپل و عرض کپل و همچنین تجزیه و تحلیل آماری همانند آزمون مقایسه میانگین دانکن و معیارهای آمار توصیفی برای تعیین ابعاد صندلی مناسب استفاده شد. تعداد 15 نفر آقا و20 نفر خانم از هر سال تحصیلی دوره لیسانس که برابر140 نفر میباشد، انتخاب شدند. ابعاد هرکدام از تمام انواع صندلیهای آموزشی دانشگاه اندازهگیری شد و اختلاف ابعاد آنتروپومتریک تعداد60 نفر از دانشجوبان یک نوع صندلی آموزشی که دارای حداکثر فراوانی بود، محاسبه شد. نتایج نشان میدهد که دانشجویان بر روی صندلیهای بلندتر از حالت استاندارد مینشینند. اگر ارتفاع سطح دسته صندلی از سطح نشستگاه برابر20، ارتفاع سطح نشستگاه 42، عمق سطح نشستگاه 38، عرض سطح نشستگاه بیش از 59 و ارتفاع پشتی صندلی 35 سانتیمتر باشد، تناسب این ابعاد با ابعاد آنتروپومتری بهترتیب تا 32، 49، 49، بیش از 59 و 44 درصد بهبود مییابد.موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091326420111222Evaluation of steam pretreatment of poplar wood particles on the mechanical and physical properties of particleboardارزیابی ویژگیهای فیزیکی، مکانیکی تخته خرده چوب ساخته شده از خردههای چوب صنوبر تیمار شده با بخار آب78579711725510.22092/ijwpr.2011.117255FAحمید هاتف نیادانشآموخته کارشناسی ارشد صنایع چوب، دانشکده منابع طبیعی، دانشگاه تهرانعلی اکبر عنایتیاستاد گروه علوم و صنایع چوب و کاغذ دانشکده منابع طبیعی. دانشگاه تهرانکاظم دوست حسینیاستاد گروه علوم و صنایع چوب و کاغذ دانشکده منابع طبیعی. دانشگاه تهرانمحمد آزاد فلاحاستادیار گروه علوم و صنایع چوب و کاغذ دانشکده منابع طبیعی. دانشگاه تهرانJournal Article20180926 In this research the effect of steam pretreatment on the physical and mechanical properties of particleboard were evaluated. Steam pre-treatment was applied on the particles of poplar wood in a stainless steel reactor at four different temperature (155, 165, 175 and 185 <sup>◦</sup>C) and three different retention time (15, 30 and 45 min). The obtained results indicated that mechanical properties include MOR and IB content of the particleboard decreased, whereas MOE increased initially then decreased with severity of treatment conditions. The physical properties of the board i.e. thickness swelling, water absorption and consequently dimensional stability were improved by steam pretreatment. The observed changes can be attributed to reduction in hemicelluloses content and hydroxyl groups within wood component.در این تحقیق، تأثیر دما و زمان پیشتیمار گرمایی (بخاردهی) خردههای چوب صنوبر روی ویژگیهای فیزیکی و مکانیکی تختهخردهچوب بررسی شد. تیمار خردههای چوب در چهار سطح دما (155، 165، 175 و 185 درجه سیلسیوس) و در سه سطح زمان (15، 30 و 45 دقیقه) انجام شد. نتایج نشان دادند که تیمار گرمایی باعث کاهش مقاومت خمشی و چسبندگی داخلی، افزایش مدول الاستیسیته، کاهش جذب آب و بهبود واکشیدگی ضخامت تخته میشود. دلایل اصلی این تغییرات را میتوان به کاهش مقدار همیسلولزهای چوب نسبت داد. به طوری که بیشترین بهبود در خواص فیزیکی تختهها در تختههای ساخته شده با خردههای چوب تیمار شده در دمای 185 درجه سیلسیوس و به مدت 45 دقیقه مشاهده شد ضمن اینکه مقاومتهای مکانیکی این تختهها هم از مقادیر ذکر شده در استاندارد مربوطه بالاتر بود.موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091326420111222Creep behavior of the composites made from creep behavior of the composites made from waste materials of OCC recycling millsرفتار خزشی مواد مرکب حاصل از ضایعات کارخانههای بازیافت کارتنهای کهنه (OCC)79881011725410.22092/ijwpr.2011.117254FAحامد یونسی کرد خلیلیدانشجوی دکترای رشته فرآوردههای چندسازه چوب، دانشکده منابع طبیعی و علوم دریایی، دانشگاه تربیت مدرسمهران جلیلونددانشجوی کارشناسی ارشد گروه علوم و صنایع چوب و کاغذ، دانشکده منابع طبیعی و علوم دریایی، دانشگاه تربیت مدرسربیع بهروزاستادیار گروه علوم و صنایع چوب و کاغذ، دانشکده منابع طبیعی و علوم دریایی، دانشگاه تربیت مدرسJournal Article20180926
The purpose of this study was to investigate effects of different loading levels and addition of urea formaldehyde and polyethylene on the creep behavior of composites made from wastes of OCC recycling mills. The composites manufactured by hot press method and three-point bending test performed before creep test. In general, the results showed positive effects of additive materials such as urea formaldehyde and polyethylene on the creep behavior of the composites. While adding UF and PE decreased primary and final creep as well as return deformation percentage of the composites. Also the obtained results indicated that remaining creep had higher sensitivity to loading levels compared to primary and final creep. Also the increase of the load levels from 20% to 30% led to an increase in creep content of the composites.هدف از این پژوهش، بررسی تأثیر سطوح بارگذاری مختلف )20 و30 درصد) و افزودن چسب اوره فرمالدئید و پلیاتیلن (5 و10درصد) بر رفتار خزشی فرآوردههای مرکب حاصل از ضایعات کارخانههای بازیافت کارتنهای کهنه (OCC) میباشد. نمونههای مورد نظر با روش پرس گرم ساخته شده و قبل از انجام آزمون خزش نیز آزمون خمش سه نقطهای روی فرآوردههای مرکب مورد مطالعه انجام شد. نتایج نشان داد که به طور کلی، استفاده از مواد افزودنی (رزین یا پلیاتیلن) در ساخت فرآوردههای مرکب، تأثیر مثبتی در رفتار خزشی این فرآوردهها داشته است، بهطوری که افزودن چسب اوره فرمالدئید و پلیاتیلن موجب کاهش میزان خیز آنی، خیز نهایی، خیز آنی واحد بار، خیز نهایی واحد بار و درصد بازگشت تغییر شکل مواد مرکب مورد مطالعه میشود. همچنین نتایج این تحقیق نشان داد که خیز باقیمانده در مقایسه با خیز آنی و نهایی نسبت به سطح بارگذاری حساسیت بیشتری نشان میدهد و با افزودن سطوح بارگذاری از 20 به 30 درصد، افزایش بیشتری در مقدار خیز کلیه فرآوردههای مرکب مورد مطالعه مشاهده میشود.موسسه تحقیقات جنگلها و مراتع کشورتحقیقات علوم چوب و کاغذ ایران1735-091326420111222Effect of Beech bark Content on Physical and Mechanical Properties
of Bark Flour-Polypropylene Compositesبررسی اثر درصد پوست راش بر خواص فیزیکی و مکانیکی مواد مرکب آرد پوست-پلیپروپیلن81182311725610.22092/ijwpr.2011.117256FAسعید کاظمی نجفیدانشیار گروه علوم و صنایع چوب و کاغذ، دانشکده منابع طبیعی و علوم دریایی، دانشگاه تربیت مدرسعلی عظیمی دلارستانیکارشناسیارشد گروه علوم و صنایع چوب و کاغذ، دانشکده منابنام نویسندگاآدرس:ن:ع طبیعی و علوم دریایی، دانشگاه تربیت مدرسJournal Article20180926In this study, physical and mechanical properties of composites made of bark flour and polypropylene were studied and compared with those of wood flour-polypropylene composites. Bark flour content were adjusted at three levels (40, 50 and 60%) and compounded at absence and presence of 2% compatibilizer (MAPP) in a twin screw extruder to produce the bark flour-polypropylene composites. The wood flour-polypropylene composites also were manufactured at 60 filler weight wood flour loading. The results showed that water absorption and thickness swelling of composites containing bark flour increase with increasing bark flour content. The composites containing bark flour exhibited lower water absorption and thickness swelling than those made from wood flour. In absence of MAPP, bark content had no significant effect on flexural modulus of the composites but flexural strength and un-notched Izod impact strength significantly decreased with increase in bark content. The use of MAPP had no significant effect in increasing the mechanical properties. A comparison indicates that in absence of MAPP, bark flour-PP composites exhibited higher mechanical properties than wood flour-PP composite but in presence of MAPP, results were quite inversed.در این تحقیق خواص فیزیکی و مکانیکی مواد مرکب حاصل از آرد پوست و پلیپروپیلن مورد مطالعه قرار گرفت و با خواص مواد مرکب آردچوب-پلیپروپیلن مقایسه شد. مقدار پرکننده آرد پوست در سه سطح 40، 50 و60 درصد در نظر گرفته شد و با عدم حضور و حضور2 درصد سازگارگننده MAPP با پلیپروپیلن در دستگاه اکسترودر دو مارپیچ مخلوط و مواد مرکب ساخته شد. مواد مرکب آردچوب-پلیپروپیلن نیز با نسبت 60 به 40 آرد چوب به پلیپروپیلن ساخته شد. نتایج نشان دادند با افزودن درصد آرد پوست جذب آب و واکشیدگی ضخامت کوتاهمدت مواد مرکب کاهش مییابد و مصرف سازگارکننده موجب کاهش جزیی این خواص میگردد. امّا با عدم حضور سازگارکننده افزایش درصد پوست در مواد مرکب پوست پلیپروپیلن مدولالاستیسیته تغییر معنیداری را نشان نمیدهد، ولی مقاومتخمشی و مقاومت به ضربه به طور معنیداری کاهش مییابد. استفاده از سازگارکننده باعث افزایش کمی در خواص مذکور میشود. مقایسه خواص مکانیکی مواد مرکب آرد پوست پلیپروپیلن و مواد مرکب، آرد چوب پلیپروپیلن نشان داد که با عدم حضور سازگارکننده، خواص مکانیکی مواد مرکب حاوی آرد پوست بیشتر از مواد مرکب دارای آرد چوب میباشد، در حالی که با حضور سازگارکننده نتایج بعکس میباشد.