Research Paper
Composite wood products
masoudreza habibi; Saeed Mahdavi; Hossein Hosseinkhani
Abstract
In this study, MDF was produced from Reed ( Phragmites australis ). Reeds are collected from Talabe - Anzalye areas. The treatments conditions for fiber preparing were as follows:-Steaming temperature 170°c, 180°c-Steaming time 5, 10, 15 minutesThe other production variables were constant. The ...
Read More
In this study, MDF was produced from Reed ( Phragmites australis ). Reeds are collected from Talabe - Anzalye areas. The treatments conditions for fiber preparing were as follows:-Steaming temperature 170°c, 180°c-Steaming time 5, 10, 15 minutesThe other production variables were constant. The anatomical properties of Reed such as fiber length, fiber diameter, lumen cell diameter, and cell wall thickness were measured respectively 1.38mm, 17.07, 6.15, 5.46 micron. LID ratio of Reed fiber was measured 80.84. The physical and mechanical properties of MDF were determined according to DIN standard. The measurements of bending properties and IB of MDF revealed that increasing steaming time and steaming temperature caused to decrease MOR, MOE and IB.Also the results of MDF dimentional stabilities indicated that Thickness Swelling after 2 and 24 hours decreased upon increasing steaming time and steaming temperature. Degradation of hemicellulose chains may be the reason of decreasing Thickness Swelling.
Research Paper
Mechanical conversion of wood and wooden fittings
Hossein Hosseinkhani; Abdolrahman Hosseinzadeh; Fardad Golbabaei; Abbas Fakhryan roghani; masoudreza habibi
Abstract
In order to establish a sawing pattern for small log of Iranian Poplar wood (Populus nigra), experimental specimens were prepared from fresh felled trees. All logs were cut in 230 cm, the length and two sawing patterns were used in order to saw and produce boards with 60 mm, nominal size in thickness. ...
Read More
In order to establish a sawing pattern for small log of Iranian Poplar wood (Populus nigra), experimental specimens were prepared from fresh felled trees. All logs were cut in 230 cm, the length and two sawing patterns were used in order to saw and produce boards with 60 mm, nominal size in thickness. In this study the band saw both vertical and horizontal were used. The study provides considerable evidence that there is significant difference between two sawing patterns (live & traditional method) and live sawing gave significantly more yield and slabs than the other method Sawing pattern for each top diameter of logs have been also given. Since the cost of coating is not much in relation to the benefits, end coating of logs and storage is recommended.
Research Paper
Composite wood products
Amir Nourbakhsh; Abolfazl Kargarfard
Abstract
In this study the effect of resin content and press time of particleboard from Date palm residues, Eucalyptus camaldulensis, Tamarix residues and prosopis (Mesquite) producted were investigated in southern of Iran.Variable factors as resin content (9, 10 and 11 percent) and press time (5, 6 and 7 minutes) ...
Read More
In this study the effect of resin content and press time of particleboard from Date palm residues, Eucalyptus camaldulensis, Tamarix residues and prosopis (Mesquite) producted were investigated in southern of Iran.Variable factors as resin content (9, 10 and 11 percent) and press time (5, 6 and 7 minutes) and total of 27 boards were fabricated. Other factors such as type of resin (UF), hardener content (2 percent) type of hardener (NH4Cl) press closing time (4.5 mm/sec.), board density (0.7 gr/cm3) press pressure (30 kg/cm2) and press temperature (160 °C)were held constant.All boards were tested according to DIN-68763 standard. The factorial experimental design at completely random test was used. The results of this study could be summarized as follows:Increasing the resin content from 9 to 11 percent, MOE and IE and decreased thickness swelling after two and 24 hours immersion in water. The results revealed that the polymerization of resin and wood is better at 11 percentresincontentand6 minutes of press time.
Research Paper
Pulp and paper
Abbas Fakhryan roghani; Abdolrahman Hosseinzadeh; Fardad Golbabaei
Abstract
In this investigation, physical, chemical, fiber dimensions, pulp and papermaking characteristics of 4 years old Alnus glutinosa was researched. The average of oven dry and critical density, fiber length, fiber diameter, lumen diameter and cell wall thickness were measured at 0.396, 0.368, 0.875mm, 32.66um, ...
Read More
In this investigation, physical, chemical, fiber dimensions, pulp and papermaking characteristics of 4 years old Alnus glutinosa was researched. The average of oven dry and critical density, fiber length, fiber diameter, lumen diameter and cell wall thickness were measured at 0.396, 0.368, 0.875mm, 32.66um, 27.28 urn and 2.70 urn respectively. Chemical compositions were obtained 48.5% cellulose, 25.35% lignin, 0.31% ash and 2.36% extractives. CMP, one stage APMP and two stage APMP processes were used for cooking. After preliminary cooking, cooking temperature, cooking time, NaOH and H202 charges were applied at 95 degree of centigrade, 10, 20, 30 and 40 minutes 10%,3% and so on. In CMP process, the average of yield, burst index, breaking length, tear index opacity and brightness were obtained at %73.72-%82.57, Kpa m2/gr. 1.53, Km 3.81, mNm2/gr 3.34, %99.59 and %29.35 correspondingly.In one stage APMP process, the average of yield, burst index, breaking length, tear index opacity and brightness were obtained at %74.09-%81.57, Kpa m2/gr. 1.52, Km 3.5, mNm2/gr3.2, %99.80 and%28.21 respectively.In two stage APMP process, the average of yield, burst index, breaking length, tear index opacity and brightness were obtained at %73.99-%80.89, Kpa m2/gr. 1.92, Km 3.95, mNm2/gr 3.45, %99.85 and %32.41 in that order.Among yields of pulp in the three methods, there weren't significant difference at level 5%. In two stages APMP paper, the burst index, breaking length and brightness were more than other and changes of cooking methods hadn't significant differences at level 5% on tear index.
Research Paper
Composite wood products
Abolfazl Kargarfard; Abdolrahman Hosseinzadeh; Kazem Doosthosseini; Ahmad Jahan latibari; Amir Nourbakhsh
Abstract
In this investigation, experimental boards were produced using beech wood particle, mat moisture content gradient at 0,3 and 6%, two press temperature sat 165and 1850 C and two press times at 3 and 5 minutes. 36 sample boards produced and the physical and mechanical properties of those tested.The results ...
Read More
In this investigation, experimental boards were produced using beech wood particle, mat moisture content gradient at 0,3 and 6%, two press temperature sat 165and 1850 C and two press times at 3 and 5 minutes. 36 sample boards produced and the physical and mechanical properties of those tested.The results indicated that mat moisture content gradient had significantly effected on modified of modulus of elasticity of boards, and with increasing mat moisture content gradient, the MOE of boards increased. Also in 0% mat moisture content gradient, increasing of press time, modulus of rupture and modulus of elasticity decreased. However with increasing mat moisture content gradient, increasing of press time caused of these properties modified.On the other hand an inverse relationship observed between mat moisture content gradient and internal bond of boards that due to of negative effect of increasing of vapor pressure were on resin bond quality in middle layer. But with increasing press time from 3 to 5 minutes, the internal bond of boards increased. The results of thickness swelling measurement indicated that with increasing mat moisture content gradient, the thickness swelling of boards increased. However, when press time increased, the thickness swelling of boards decreased.
Research Paper
Composite wood products
Amir Nourbakhsh; Abdolrahman Hosseinzadeh; Kazem Doosthosseini; Abolfazl Kargarfard; Mazyar Radkyan
Abstract
In this investigation feasibility of Beech slabs in particleboards production were prepared at three different contents resin of 9, 10, and 11 percent, press temperatures of 165°C and 175°C and hardener contents of 1.5 and 2.5 percent.Based on the DIN-68763 standard physical and mechanical properties ...
Read More
In this investigation feasibility of Beech slabs in particleboards production were prepared at three different contents resin of 9, 10, and 11 percent, press temperatures of 165°C and 175°C and hardener contents of 1.5 and 2.5 percent.Based on the DIN-68763 standard physical and mechanical properties including MOR, MOE, IB, and thickness swelling (after 2 and 24 immersion in water) were tested.According to the factorial experimental design at completely random test was analysis. The potential utilization of Beech slabs residues in particleboard production including: resin content (11%), press time (6 min.), press temp. (175°C), and hardener contents (2.5%) were found.
Research Paper
Management and Economics wood
Habib alah Arab tabar firoz jaei; Ali Reza nezhad; Abdolrahman Hosseinzadeh
Abstract
In this study, durability of Eucalyptus wood(Eucalyptus intertexta R.T.Baker) in both treated with creosote and celcore and untreated to attack by Trametes versicolor (L.ex)L loyd. were evaluated heart wood by the Kolleshal methodes described in DIN 52176, and B.S. 838. The comparison of weight ...
Read More
In this study, durability of Eucalyptus wood(Eucalyptus intertexta R.T.Baker) in both treated with creosote and celcore and untreated to attack by Trametes versicolor (L.ex)L loyd. were evaluated heart wood by the Kolleshal methodes described in DIN 52176, and B.S. 838. The comparison of weight losses of samples were also evaluated and it showed that fungus had no effect on the treated samples but it caused 4% weight loss of natural durability samples. Based on this study, it can be concluded that E. intertexta wood can be classified as a durable wood.