Composite wood products
Saeid Ismaeilimoghadam; Mohammad Shamsian; Ali Bayat Kashkoli; Behzad Kord
Abstract
This research with aim of evaluation the effect of chemical treatment of wood flour on physical, mechanical and morphological properties of polypropylene-nano SiO2 hybrid nanocomposite were done. For this purpose, wood flour with sodium hydroxide and benzyl chloride to chemically treatment. For ensure ...
Read More
This research with aim of evaluation the effect of chemical treatment of wood flour on physical, mechanical and morphological properties of polypropylene-nano SiO2 hybrid nanocomposite were done. For this purpose, wood flour with sodium hydroxide and benzyl chloride to chemically treatment. For ensure the chemical treatment, Fourier transform infrared (FTIR) spectroscopy tests was done on the treated and untreated wood flour. Wood flour at 60% weight ratio with polypropylene with 4% maleic anhydrate grafted polypropylene coupling agent in extrusion were mixed. Also Nano SiO2 with 0, 1, 3 and 5% as filler was used. The sample specimen were manufactured by using injection molding techniques. Then mechanical tests such as bending resistance and modulus and physical tests such as water absorption and thickness swelling according to the ASTM standard was done on the samples. Also for morphological investigation on the Nano composites from Scanning Electron Microscopy (SEM) was used. Results showed that the bending resistance and modulus increased with effect of chemical treatment but water absorption and thickness swelling decreased. With increase of Nano SiO2 to 3% the mechanical properties increased but adding further amount Nano particles reduced the mechanical properties. With increase of SiO2 Nano particles to 5% the water absorption in Nano composites were increased, but thickness swelling was decrease. The results of SEM showed an improvement in interface between filler and matrix with effect of chemical treatment Also transmittance of Nano SiO2 to 3% levels was good.
Composite wood products
masih masoudifar; Babak Nosrati; Hamid reza Mansori; Rahim Mohebi gargari
Abstract
This study aimed to investigate the effect of chemical treatment of wood material on functional properties of wood flour / polypropylene hybrid composite. For this reason, first of all, mixed hardwood were separately treated by acetic acid, sodium hydroxide and hot water and were compared with control ...
Read More
This study aimed to investigate the effect of chemical treatment of wood material on functional properties of wood flour / polypropylene hybrid composite. For this reason, first of all, mixed hardwood were separately treated by acetic acid, sodium hydroxide and hot water and were compared with control (untreated) samples. After chemical treatment, wood flour and polypropylene with weight ratio of 50 to 50 and 3 phc of compatibilizer combines in the internal mixer and at last the WPC composite were made using injection molding. Then mechanical tests included bending resistance, tension and impact and physical examination, including water absorption and thickness swelling after 2 and 24 hours was performed on specimens according to (ASTM) standard. Also to study the morphology of the composites, scanning electron microscopy (SEM) was used. The results of this study showed that by chemical treatment the mechanical strength increased and physical properties such as water absorption and thickness swelling decreased. So that the highest flexural strength, tensile and flexural modulus is related to alkali treatment and the highest tensile modulus and impact resistance is related to the acid treatment. Also the lowest water absorption and thickness swelling was related to the alkali treatment. In order to ensure chemical treatments, Fourier transform infrared (FTIR) and weight percent gain (WPG) was used on wood flour.