Composite wood products
masoudreza habibi; Hossein Hosseinkhani; Saeed Mahdavi
Abstract
In this study, particleboard was produced using Mesquite (Prosopis juliflora) called Somr wood. Oven dry density of stem and branch wood was measured as 0.92, 0.72 g/cm3 whereas the bark weight percentage of stem and branch wood determined as 13.6 % and14 % respectively. The influence of raw material ...
Read More
In this study, particleboard was produced using Mesquite (Prosopis juliflora) called Somr wood. Oven dry density of stem and branch wood was measured as 0.92, 0.72 g/cm3 whereas the bark weight percentage of stem and branch wood determined as 13.6 % and14 % respectively. The influence of raw material mixture (stem wood, branch wood, the blend of stem and branch wood, 50/50 w/w) and resin content 10% and 12 % (based on dry weight of the particle) on particleboard properties were investigated. Properties such as MOR, MOE, IB, thickness swelling after 2 and 24 hours immersion in water were determined according to EN standard. Except for MOE, the effect of raw material type on board properties was significant. Particleboards made from branch wood, had the highest MOR. Maximum IB was observed in boards made from the blend of stem and branch wood. With the exception of bending properties, the effect of resin content on all board properties was significant. Increasing the resin content improved board properties. The lowest value of thickness swelling after 2 and 24 hours immersion in water was obtained in particleboard made from stem wood
Kamyar Salehi; Fardad Golbabaei; Saeed Mahdavi; Abas Fakhryan
Abstract
The characteristics of five common varieties of sugarcane cultivated in the southern Iran, including cp57-614, sp70-1143, cp69-106, cp48-103, and nco310 were evaluated. The characteristics measured were fiber dimension, papermaking coefficients, fiber yield, density and chemical component. cp69-106 revealed ...
Read More
The characteristics of five common varieties of sugarcane cultivated in the southern Iran, including cp57-614, sp70-1143, cp69-106, cp48-103, and nco310 were evaluated. The characteristics measured were fiber dimension, papermaking coefficients, fiber yield, density and chemical component. cp69-106 revealed the longest fiber with the average length of 1.55 mm whereas cp57-614 had the shortest fiber with average length of 1.39 mm. The cp48-103 and cp69-106 were ranked as having the widest and narrowest fiber diameter as 25.38 and 20.42 micron respectively. The measurement of the density at 12% moisture content showed that sp70-1143 with 0.35g/cm-3 provide the highest value and the cp57-614 possessed the lowest density measured at 0.17g.cm-3. There existed statistically significant differences among other fiber characteristics and papermaking coefficients. In general, the result indicated that cp69-106 provides the optimal characteristics in comparison with the other varieties based on papermaking specifications.
Pulp and paper
Amir mohsen Nazry; Mohammad Talaeipoor; Saeed Mahdavi
Abstract
The effects of different fines with different shape and size of mechanical Pulp on Paper Properties in two fractions was investigated. Fines was classified in two categories including fibrils and flakes , and then effect of these particles on pulp properties was studied.The fibril fraction was consist ...
Read More
The effects of different fines with different shape and size of mechanical Pulp on Paper Properties in two fractions was investigated. Fines was classified in two categories including fibrils and flakes , and then effect of these particles on pulp properties was studied.The fibril fraction was consist of fibrillar material, i.e., ribbons, fibrils, and thin lamella particles. The flake fraction consist of flake like material i.e., fiber wall fragments and thick lamella. An advanced image analysis method was used to characterize the properties of fibrils and flakes. The results indicate that the fibrils and flake fractions have distinct characteristics and effect on sheet properties. The fibrils strongly affected the strength properties, while the flakes improved light scattering. Generally, the smaller size Particles afforded higher sheet density and strength. Fines content and fibrillar material are very important parameters in mechanical pulping and can also affect quality controlling of mechanical pulp and papermaking.
Pulp and paper
Maryam Rostaei; Rabi Behroz; Saeid Mahdavi
Abstract
This research was performed to improve the properties of the pulp made of Aspen Deltoides, using antraquinone(AQ) catalizer. Neutral sulfite semichemical (NSSC) method in three efficiency levels of 55, 60, and 65% was applied. Cooking situations was selected as: Specific Temperature (175˚ C) , Time ...
Read More
This research was performed to improve the properties of the pulp made of Aspen Deltoides, using antraquinone(AQ) catalizer. Neutral sulfite semichemical (NSSC) method in three efficiency levels of 55, 60, and 65% was applied. Cooking situations was selected as: Specific Temperature (175˚ C) , Time (Variable) , Specific Percentage of Chemicals 14% and Anthraquinone 0.1% . In all stages of cooking, weight ratio of sodium sulfide to sodium bicarbonate was set as 4.5/1. The ratio of cooking liquid to chips was 5/1. The results indicated that AQ causes an increase in efficiency and a significant decrease in Kappa. Researches also indicated that by the use of AQ, strength indexes of the paper such as strength of burst, tearing, tensile, Ring Crush Test and Corrugating Medium Test increases. Optical experiments on hand sheets following addition of AQ, indicated increase in brightness and decrease in opacity.
Composite wood products
masoudreza habibi; Hossein Hosseinkhani; Saeed Mahdavi; Sayed javad Sepidehdam
Abstract
In this study, particleboard was produced by Eucalyptus and Poplar wood mixture. Variations of this study were as follow: - Combinations of Eucalyptus and Poplar wood were (%100 , %0) , (%66.5 ,% 33.5) , (%33.5 ,% 66.5) and (%0 ,% 100) respectively. ...
Read More
In this study, particleboard was produced by Eucalyptus and Poplar wood mixture. Variations of this study were as follow: - Combinations of Eucalyptus and Poplar wood were (%100 , %0) , (%66.5 ,% 33.5) , (%33.5 ,% 66.5) and (%0 ,% 100) respectively. - Resin content ( %8 and %10) Physical and mechanical properties of boards such as MOR, MOE, IB TS2 and TS24 were tested according to EN standard. The effects of raw materials combinations on bending properties were significant. Maximum of MOE and MOR were observed in %66.5 of Poplar wood and % 33.5 of Eucalyptus wood. As expected, Physical and mechanical properties of boards were improved by increasing of resin content. Results indicated that TS2 and TS24 were increased with increasing of Poplar wood in combinations. Also the minimum of these properties were obtained in combinations of Eucalyptus and Poplar wood, %100, %0 respectively.
Composite wood products
masoudreza habibi; Hossein Hosseinkhani; Saeid Mahdavi; Fardad Golbabaei
Abstract
In this study Medium Density Fiberboard was produced from 4 year old Poplar clones (P.e. costanzo, P.e. 564.41, P.e. vernirubensis). Fibers length of P.e. costanzo, P.e. 564.41, P.e. vernirubensis were measured 805, 751 and 764 micron respectively. Also fibers diameter of these clones were determined ...
Read More
In this study Medium Density Fiberboard was produced from 4 year old Poplar clones (P.e. costanzo, P.e. 564.41, P.e. vernirubensis). Fibers length of P.e. costanzo, P.e. 564.41, P.e. vernirubensis were measured 805, 751 and 764 micron respectively. Also fibers diameter of these clones were determined 25.76, 25.44, 25.23 micron respectively. Three steaming times (5, 10, 15 minutes) were used for fibers preparation. Also three press times (3, 4, 5 minutes) and two resin contents (9%, 11%) were applied for MDF production. Thus physical and mechanical properties of boards such as MOE, MOR, IB and Thickness Swelling after 2 and 24 hours were investigated. The physical and mechanical properties of boards were tested in based on EN standard. The measurements of bending properties and IB of MDF revealed that increasing steaming time caused to decrease MOE, MOR and IB. The highest of MOE, MOR and IB were obtained in 5 minutes steaming time. Also the lowest values of Thickness Swelling after 2 and 24 hours were obtained in 15 minutes steaming time. The influence of press time on bending properties was not significant. The highest of IB was obtained in 5 minutes press time. As expected, boards demonstrated better properties at higher resin content.
Pulp and paper
Abbas Fakhryan roghani; Fardad Golbabaei; Hossein Hosseinkhani; Kamyar Salehi; Saeed Mahdavi; Sabrineh Mohsseni tavakoli
Abstract
In this reseach, chemical, anatomical and pulping properties of 12 years old Populus.triplo of adapting plan and quantity properties of this tree from karaj research station were investigated.The average of fiber length ,diameter ,lumen and thickness of cell wall 1.27 mm ,31.88 um, 23.54 um and 4.22 ...
Read More
In this reseach, chemical, anatomical and pulping properties of 12 years old Populus.triplo of adapting plan and quantity properties of this tree from karaj research station were investigated.The average of fiber length ,diameter ,lumen and thickness of cell wall 1.27 mm ,31.88 um, 23.54 um and 4.22 um and cellulose ,lignin , Ext. and ash %53.74 , %22.87 , %1.8 and %1.5 were measured respectively.The yield and kappa number of pulps between 41.152% - 48% and 18.06 – 25.28 were measured.In 14% and 18% effective alcoholli, tearh index 9.307 mNm²/gr and 10.147 mNm²/gr were obtained.
Pulp and paper
Said mohammad Mazhari mosavi; Saeed Mahdavi; Syed zyaldin Hosseini; Hossein Resalti; Hossein Usefi
Abstract
This research is aimed to study the possibility of rapeseed straw (Hayolla401) pulping and its paper characteristics, using Soda-AQ process. The average fiber length was found 1.04 millimeter and the average fiber diameter, lumen and thickness were found 28.00, 19.09, and 4.91 micrometer, respectively. ...
Read More
This research is aimed to study the possibility of rapeseed straw (Hayolla401) pulping and its paper characteristics, using Soda-AQ process. The average fiber length was found 1.04 millimeter and the average fiber diameter, lumen and thickness were found 28.00, 19.09, and 4.91 micrometer, respectively. Cellulose, lignin, extractive material (acetone solved) and ash were measured 41.66, 16.00, 1.63, and3.46 percent, respectively. Cooking condition was determined as follow: Soda as 16, 18, and 20 percent on the basis of rapeseed dry straw, temperature was set at 175 and 185 Cº, cooking time was set at 40 and 70 minutes, and straw to liquid ratio was set at 1/8. The amount of anthraquinone added to cooking liquor was 0.2%, based on rapeseed dry straw. Using severe cooking factors caused reduction of yield and Kappa number in both methods. Refining was performed on selected pulps in order to reach 35025 (ml,CSF) freeness. The 60 gr/m² hand sheets were made in order to determine mechanical strength and physical properties. Average thickness, density and bulk is measured at 86.4µ, 0.69gr/cm³ and 1.44cm³/gr respectively. Average tear index, burst index, breaking length and tensile indexare measured at 4.6 mN.m²/gr, 3.5 kpa.m²/gr, 7.4km and 72.6Nm/g respectively.
The results showed that however screen yield of rapeseed straw pulp is low but kappa number and mechanical properties of pulp is suitable,compared with the other agriculture residues, so Rapeseed pulp can be used in paper making industries.
Pulp and paper
Mohammadreza Dehghani Firouzabadi; Afshin Tvasoli; Saeed Mahdavi
Abstract
We studied the possibility of replacing imported long fiber pulp (ILFP) with kenaf bast fiber soda pulp (KBFSP) to improve the quality of paper made with bagasse soda pulp (BSP). To do so, we produced BSP with kappa number 13.5 similar to that prepared by Pars Paper Mill. We also produced KBFSP with ...
Read More
We studied the possibility of replacing imported long fiber pulp (ILFP) with kenaf bast fiber soda pulp (KBFSP) to improve the quality of paper made with bagasse soda pulp (BSP). To do so, we produced BSP with kappa number 13.5 similar to that prepared by Pars Paper Mill. We also produced KBFSP with kappa number 21.6 similar to the unbleached imported ILFP. The yield percent for BSP and KBFSP were respectively 48.9 and 55.6 %. The maximum pulping temperature was 165 °C; alkaline was 20% based on sodium hydroxide and ratio of liquor to dry weight of the raw material was 8:1. All the three pulps were beaten up to a freeness degree of 400 ml, CSF. Amounts of 0, 10, 20 and 30 percent ILFP and KBFSP were mixed with 100, 90, 80 and 70 percent BSP to produce hand sheets. In all cases of KBFSP mixing with BSP, the thickness of the generated hand sheets were higher than those produced through mixing ILFP with BSP while the density was lower. The difference in burst strength and breaking length of a mixture of 30% KBFSP with 70% BSP in the hand sheets were non-significant as compared with those of ILFP and BSP. Tear strength and opacity of mixing 30% KBFSP with 70% BSP were significantly higher than those of the ILFP and BSP with the same mixing ratio. We suggest that KBFSP provides a suitable replacement for ILFP to improve physical and strength properties of paper made with BSP.
Delaram Drakhshandeh; Behbood Mohebi; Saeed Mahdavi
Abstract
This research was carried out to study the influence of acetylation on paper dimensional stability. Specimens from printing paper and Texon paperboard were oven dried and then treated with acetic anhydride at 120°c for 30 and 60 min without catalyst. Acetylated papers were soaked in water for 2 and ...
Read More
This research was carried out to study the influence of acetylation on paper dimensional stability. Specimens from printing paper and Texon paperboard were oven dried and then treated with acetic anhydride at 120°c for 30 and 60 min without catalyst. Acetylated papers were soaked in water for 2 and 24 h. Afterwards, bulking effect of the acetylation and thickness swelling of the specimens as well as anti-swelling-effect (ASE) were determined in the treated specimens.
Results revealed that the bulking of the specimens were increased by reaction time. However, in case of Texon, it was slowed down after 30 min of the reaction time. The thickness swelling of the treated specimens was significantly reduced after soaking in water for 2 and 24 h compared with untreated samples. As it was expected the acetylation increased ASE in Texon and the printing papers.
Composite wood products
masoudreza habibi; Hossein Hosseinkhani; Saeed Mahdavi
Abstract
In this study , MDF was produced from three clones of poplar (P.e. vernirubensis, P.e. costanzo, P.e.561.41). Age clones of poplar were 4 and 12 years. In addition to age variation , the influence of three production variables (steaming time , press time and resin content on MDF properties were investigated. ...
Read More
In this study , MDF was produced from three clones of poplar (P.e. vernirubensis, P.e. costanzo, P.e.561.41). Age clones of poplar were 4 and 12 years. In addition to age variation , the influence of three production variables (steaming time , press time and resin content on MDF properties were investigated. Variations of each variable were as follow:
- Steaming time (5, 10, 15 minutes)
- Press time (3, 4, 5 minutes)
- Resin content (9%, 11%)
Fiber length and fiber diameter of 4 and 12 years old poplar clones (P.e. vernirubensis, P.e. costanzo, P.e.564.41) were measured 746, 25.23, 805, 25.76,751, 25.44 and 902, 31.62, 995, 29.23, 899, 26.83 micron respectively.
MOR, MOE, IB, TS2, TS24 were determined according to DIN standard.
Increasing steaming time decreased board's internal bond and bending properties. As expected, boards demonstrated better properties at higher resin consumption. Minimum of boards thickness swelling were obtained at 15 minutes steaming time because of fiber hydrophilic properties were decreased. There are no significant differences between 4 and 12 years old of clones for bending properties and IB of boards. The effect of age variation is only significant difference on thickness swelling of boards which it is lower for 4 years old clones.
Composite wood products
masoudreza habibi; Hossein Hosseinkhani; Saeed Mahdavi
Abstract
In this study, MDF was produced from Rice straw. Variables for Medium Density fiberboard making were as following:
- Resin content 8, 9.5, 11 (percent baced on oven dry weight of fiber)
- Press time (4, 5, 6 minutes).
There were 9 treatment conditions by combinations of the above factors and three ...
Read More
In this study, MDF was produced from Rice straw. Variables for Medium Density fiberboard making were as following:
- Resin content 8, 9.5, 11 (percent baced on oven dry weight of fiber)
- Press time (4, 5, 6 minutes).
There were 9 treatment conditions by combinations of the above factors and three replications for each combinations which resulted in producing 27 boards.The other production variables were constant.
The anatomical properties of Rice straw such as fiber length, fiber diameter were measured respectively 810, 10.1 micron. L/D ratio of Rice straw fiber was measured 80.2. The physical and mechanical properties of MDF were determined according to DIN standard. The measurements of bending properties and IB of MDF revealed that the highest MOR, MOE, IB were obtained in variables combination of 11% resin content and press time of 6 minute and at this conditions thickness swelling of boards were the lowest.
According to Duncans, test method the effects of press times (4 & 5 minutes) and resin content (8% & 9.5%) on bending properties were not significant statistically.
Pulp and paper
Saeed Mahdavi; masoudreza habibi; kermanian hossein
Abstract
Global concerns for preservation of forests and elimination of pollution from pulping and papermaking processes has led us to explore alternate fibrous resources other than wood and new environmentally begin pulping and bleaching processes for papermaking without sacrificing quality. Various alternate ...
Read More
Global concerns for preservation of forests and elimination of pollution from pulping and papermaking processes has led us to explore alternate fibrous resources other than wood and new environmentally begin pulping and bleaching processes for papermaking without sacrificing quality. Various alternate fibrous resources such as agricultural residues are already in use in many countries and considerable research have been undertaken to produce pulps by conventional and non-conventional processes. Wheat straw has high quantity among agricultural residues in Iran. Kraft, Soda and Ethanol-alkali pulping were carried out after sampling and preparing of wheat straw. Retention of carbohydrates is improved compared to the alkaline pulping processes, resulting in about 8 to 15 % higher yield at the same level of residual lignin. There was lower energy consumption for refining Ethanol-alkali pulps. There were no statistical differences among the physical properties. The strengths of Ethanol-alkali pulps consist of tear index, burst index and breaking length were lower than alkaline pulps, but all of the strength properties were higher than kraft and liner paper except tear index that addition of some long fiber can solve the problem.
Saeed Mahdavi; masoudreza habibi; Kamyar Salehi; Hossein Familian; kermanian hossein
Abstract
The common reed, P.australis, covers vast region in south of Iran. Specially, there is possibility of executing harvest in Hoor-Alazim canebrake as a reed natural provenance. It has good properties for papermaking in comparison of typical nonwood materials. Chips were pulped using typical kraft, soda ...
Read More
The common reed, P.australis, covers vast region in south of Iran. Specially, there is possibility of executing harvest in Hoor-Alazim canebrake as a reed natural provenance. It has good properties for papermaking in comparison of typical nonwood materials. Chips were pulped using typical kraft, soda and NSSC processes. Standard testing of pulp properties was made using TAPPI procedures. Pulps were beaten in a PFI mill to 400m.l.csf freeness level. Handsheets were made from the refined reed pulps for measuring strengths. Screen yield and kappa number of soda pulp were about similar to kraft pulp. NSSC pulp has lower kappa number than the soda at the equivalent screen yield. Energy consumption for beating from kraft, soda and NSSC pulps reduced respectively. Initial freeness of reed pulp was near to hardwood typical, thus good drainage and runnability on reed papermaking is expectable. The physical properties of reed handsheets were higher than newsprint and fluting pulps of Mazandaran Company. Overall, soda and NSSC reed pulps can be used in producing of newsprint and fluting papers based on the properties.
Composite wood products
masoudreza habibi; Saeed Mahdavi; Hossein Hosseinkhani
Abstract
In this study, MDF was produced from Reed ( Phragmites australis ). Reeds are collected from Talabe - Anzalye areas. The treatments conditions for fiber preparing were as follows:-Steaming temperature 170°c, 180°c-Steaming time 5, 10, 15 minutesThe other production variables were constant. The ...
Read More
In this study, MDF was produced from Reed ( Phragmites australis ). Reeds are collected from Talabe - Anzalye areas. The treatments conditions for fiber preparing were as follows:-Steaming temperature 170°c, 180°c-Steaming time 5, 10, 15 minutesThe other production variables were constant. The anatomical properties of Reed such as fiber length, fiber diameter, lumen cell diameter, and cell wall thickness were measured respectively 1.38mm, 17.07, 6.15, 5.46 micron. LID ratio of Reed fiber was measured 80.84. The physical and mechanical properties of MDF were determined according to DIN standard. The measurements of bending properties and IB of MDF revealed that increasing steaming time and steaming temperature caused to decrease MOR, MOE and IB.Also the results of MDF dimentional stabilities indicated that Thickness Swelling after 2 and 24 hours decreased upon increasing steaming time and steaming temperature. Degradation of hemicellulose chains may be the reason of decreasing Thickness Swelling.
Composite wood products
masoudreza habibi; Saeed Mahdavi; Hossein Hosseinkhani; Sayed javad Sepideh dam
Abstract
In this study, MDF was produced from Reed (Phragmites australis). Reeds are collected from Hor-Alazym area. The treatments conditions for fiber preparing were as following:- Steaming temperature 170, 180oC(Steaming pressure 7,9 bar).- Steaming time 5, 10, 15 minutes.The other production variables were ...
Read More
In this study, MDF was produced from Reed (Phragmites australis). Reeds are collected from Hor-Alazym area. The treatments conditions for fiber preparing were as following:- Steaming temperature 170, 180oC(Steaming pressure 7,9 bar).- Steaming time 5, 10, 15 minutes.The other production variables were constant.The anatomical properties of Reed such as Fiber length, fiber diameter, lumen cell diameter, and cell wall thickness were measured. LID ratio of Reed fiber was measured 73.69. The physical and mechanical properties of MDF were determined according to DIN standard. The measurements of bending properties and IB of MDF revealed that increasing steaming time and steaming temperature caused to decrease MOR, MOE, and IB.Also the results of MDF dimentional stabilities indicated that Thickness Swelling after 2 and 24 hours decreased upon increasing steaming time and steaming temperature. Degradation of hemicellulose chains may be the reason of decreasing Thickness Swelling.
Physics and anatomy
Saeed Mahdavi; masoudreza habibi
Abstract
Growing interest in wood and paper consumption in Iranian industries and forest utilization constraints call for alternative approaches on the exploitation trend. Lately, industrial countries consider utilization of small diameter trees and branches residual wood. European hornbeam with vast coverage ...
Read More
Growing interest in wood and paper consumption in Iranian industries and forest utilization constraints call for alternative approaches on the exploitation trend. Lately, industrial countries consider utilization of small diameter trees and branches residual wood. European hornbeam with vast coverage among the other species in Iran can be an alternative to tree shortage of raw material for the sector. This study showed that the branch fiber dimensions have significantly differed compare to trunk.Average fiber length was measured as 1.76mm for breast height of three trunks and 1.43 mm for two branches samples. Fiber length increased from crown downward to the stump and also from pith to bark, but there was a significant negative correlation between the variations and tree height. Fiber length increased in trees of up to 30 years of age and decreased afterwards. There is no orderly pattern from tree base to the upper branches.Runkel and flexibility coefficients of branch were better than trunk despite of higher fiber dimensions in trunk.
Physics and anatomy
Saeed Mahdavi; Abdolrahman Hosseinzadeh; Hossein Familian; masoudreza habibi
Abstract
Cross sectional disks were cut at breast height from three 17-year-old trees of E.camaldulensis grown in Pasand research station in Mazandaran province. Ring width, wood density, and fiber dimension were measured for each two rings from pith to the bark. Overall average disks, fiber length, fiber width, ...
Read More
Cross sectional disks were cut at breast height from three 17-year-old trees of E.camaldulensis grown in Pasand research station in Mazandaran province. Ring width, wood density, and fiber dimension were measured for each two rings from pith to the bark. Overall average disks, fiber length, fiber width, lumen diameter, and cell wall thickness were measured at 758, 15.93, 8.63, and 3.65 micrometer respectively. Mean values for the oven dry and basic. Density was 0.708 g/cm3 and 0.552 g/cm3. Cross sectional \ growth rate and wood production for the trees were measured at 11.1 mm and 12.3 m3/ha./year respectively. Chemical compositions of the wood consist or cellulose, lignin, extractives (in acetone soluble) and ash were measured at 47.44%, 30.87%, 6.96%, and 0.27% respectively. The result showed that E.camaldulensis is classified as short fiber hardwood with low frequency. Fiber dimensions and density slightly increased from pith to the bark. There was high significant correlation between cell wall thickness and density, while; there was no significant correlation between ring width and the others. Among the properties studied, cell wall thickness and fiber length showed the most variations.
Composite wood products
masoudreza habibi; Abdolrahman Hosseinzadeh; Fardad Golbabaei; Hossein Hosseinkhani; Javad Sepidedam; Saeed Mahdavi
Abstract
In this study, MDF was produced from wet depicting Bagasse in three steaming time of 5, 10 and 15 minutes and in two steaming temperatures of 170°C and 180°C. There were 6 treatment conditions by combination of the above factors and three replications for each combination which resulted in producing ...
Read More
In this study, MDF was produced from wet depicting Bagasse in three steaming time of 5, 10 and 15 minutes and in two steaming temperatures of 170°C and 180°C. There were 6 treatment conditions by combination of the above factors and three replications for each combination which resulted in producing 18 boards.The anatomical and chemical properties of Bagasse and also the physical and mechanical properties of MDF such as MOR, MOE, IB and swelling thickness after 2 and 24 hours were studied.Fiber length, fiber diameter, lumen cell diameter, and cell wall thickness were respectively measured 1.24 mm 22.90m., 12.48 m and 5.28m cellulose, lignin, extractives, and ash contents were 53.68%, 20.44%, 0.96% and 1.14% respectively.The measurement of MOR, MOE, IB and SW (after 2 and 24 hours) of the MDF revealed that the proper condition is obtained at the steaming temperature of 170°C and the steaming time of 5 minutes. The properties in the above-mentioned conditions were measured 12.22Mpa, 1370 Mpa, 0.13 Mpa, 47.11% and 52.22% respectively.
Composite wood products
masoudreza habibi; Abdolrahman Hosseinzadeh; Hossein Hosseinkhani; Saeed Mahdavi
Abstract
In this study the effect of two variables, (resin content and press time) on properties of MDF was investigated. Levels of each variable was as follow: Resin content (8, 9.5, 11 percent) Press time (4, 5, 6 minutes). The statistical analysis proved that the effect of press time on MOE and MOR was significant. ...
Read More
In this study the effect of two variables, (resin content and press time) on properties of MDF was investigated. Levels of each variable was as follow: Resin content (8, 9.5, 11 percent) Press time (4, 5, 6 minutes). The statistical analysis proved that the effect of press time on MOE and MOR was significant. MOE and MOR were the highest at press time of 6 minutes. According to Duncan's test, there aren’t any significant differences between MOE at press time of 5 and 6 minutes. Also the effect of resin content on MOE had significant differences. MOE was the highest at resin content of 11%. There aren’t any significant differences between MOE on resin content at 9.5% and 11% levels. The results showed that effects of press time and resin content had significant differences on IB. IB was the highest at press time of 6 minutes and resin content of 11%. There aren’t any significant differences between IB on resin content at 9.5% and 11%. The effects of press time and resin content had significant differences on thickness swelling after 2 hours. Thickness swelling was the lowest at press time of 6 minutes and resin content of 11%. According to the results of this study optimum combination for MDF production from baggasse includes resin content and press time of 9.5% and 5 minutes respectively.
Physics and anatomy
Hossein Familian; Abdolrahman Hosseinzadeh; Mohammad hassan Asareh; Saeed Mahdavi; Sayed mosa Sadeghi; Kamyar Salehi
Abstract
Ziziphus lotus of the family Rhamnaceae is distributed in the southern region of Iran and considered as one of drought - resistant tree species of the country. This investigation is the first attempt to study wood properties of this species, in order to contribute to a better understanding of it. The ...
Read More
Ziziphus lotus of the family Rhamnaceae is distributed in the southern region of Iran and considered as one of drought - resistant tree species of the country. This investigation is the first attempt to study wood properties of this species, in order to contribute to a better understanding of it. The results of this study revealed that Ziziphus lotus is a diffuse – porous with basic specific gravity medium and medium - textured wood. The length of vessel elements are medium, the diameter of vessel elements is small, porous with pores round to oval, intervessel pilting, opposite and intermediate, 20 vessels per square millimeter, simple perforation plates, vessel - ray pits similar to intervessel pits in size and shape and half bordered; Vascular tracheids present, there are rarely tyloses and Gums in vessels. Fibers with simple to minutely bordered pits, thin - to thick – walled and fiber lengths short; Parenchyma scanty paratracheal, vasicentric and rarely aliform; Ray uniseriate and sometimes biseriate, ray height is short, rays with procumbent, Square and upright cells mixed throughout the ray and one Prismatic crystals in chambered upright and square ray cells, rays 12 per mm, silica bodies in ray cells; There are 7-10 Schizogenous canals in pith.In this species also percentages of cellulose are high but ash and extractive soluble in acetone content was found to be low.
Physics and anatomy
Saeed Mahdavi; Abdolrahman Hosseinzadeh; Abbas Fakhryan roghani; masoudreza habibi
Abstract
In order to evaluate reed as a raw material for wood & paper industries, three main regions of Iran consist of south, North and East were selected for this study. Phragmites australis is dominant species in these regions and this study concentrated on it as well.Chemical components and biometry of ...
Read More
In order to evaluate reed as a raw material for wood & paper industries, three main regions of Iran consist of south, North and East were selected for this study. Phragmites australis is dominant species in these regions and this study concentrated on it as well.Chemical components and biometry of fibers were determined with four and thirty replications respectively. Statistical analysis showed that there were no significant differences among three regions in fiber length and lumen diameter but reversely fiber width and cell wall thickness showed significant differences. The highest fiber length mean was 1.39mm. For North (Anzali) Coefficients of papermaking of fibers also were calculated for each region. Biometerical fiber results, showed that P. australis has good fiber compare to the Iranians hardwoods as papermaking.The results also showed that there are significant differences between regions and subregions at %5 level. North had the highest and lowest cellulose and lignin contents respectively. These results also proved that P.australis is one of the best Iranians' raw materials as cellulose and lignin contents between the others.
Abas Fakhryan; Ahmad Jahan latibari; Abdolrahman Hosseinzadeh; Fardad Golbabaei; Saeid Mahdavi
Saeid Mahdavi; Abdolrahman Hosseinzadeh; Ahmad Jahan latibari; Hossein Resalati; Abbas Fakhryan roghani
Physics and anatomy
Abdolrahman Hosseinzadeh; Ahmad Jahan latibari; Hossein Familian; Saeed Mahdavi; Sayed javad Sepidehdam
Abstract
In this investigation, samples were collected from three tamarix species including: Tamarix meyeri from northern part and T. aphylla and T. strica from the southern parts of Iran. Nine dominat tamarix trees were felled, three for each species. From each tree 10 cm thick cross-sections at three different ...
Read More
In this investigation, samples were collected from three tamarix species including: Tamarix meyeri from northern part and T. aphylla and T. strica from the southern parts of Iran. Nine dominat tamarix trees were felled, three for each species. From each tree 10 cm thick cross-sections at three different heights (5, 25 and 50% of the tree height) were cut. These disks were used for anatomical study, and remaining logs were transferred to laboratory for physical and chemical tests. The results of this study revealed that wood from these three species of tamarix is considered unsuitable for pulping and in the case, It is used for pulping, the pulp yield will be low and the strength of the pulp will be quite low, which is the consequence of short and thick-walled fibers that will not provide adequate fiber bonding. In addition, because of the large diameter and thick-walled fibers, the strength properties of the woods are also low.